- 缺口冲击强度: 5.34
- 拉伸强度 [MPa]: 22.1
- 弯曲模量 [MPa]: 0.965
- 硬度: 65.0
- 热变形温度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Index of Compound | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 65 | 65 | ASTM D785 |
| Tensile Strength, Yield | 22.1 MPa | 3200 psi | 2 in/min; ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Flexural Modulus | 0.965 GPa | 140 ksi | ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Gardner Impact | 40.7 J | 30.0 ft-lb | ASTM D3029 |
| 40.7 J @Temperature -28.9 °C | 30.0 ft-lb @Temperature -20.0 °F | ASTM D3029 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 |