- 熔体流动速率 [g/10min]: 90.0
- 缺口冲击强度: 0.214
- 拉伸强度 [MPa]: 29.0
- 弯曲模量 [MPa]: 1.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Flow | 90 g/10 min @Load 2.16 kg, Temperature 230 °C | 90 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | 2 in/min; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D790 |
| Izod Impact, Notched | 0.214 J/cm | 0.400 ft-lb/in | ASTM D256 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 160 °C | 320 °F | |