- 熔体流动速率 [g/10min]: 12.0
- 缺口冲击强度: 0.534
- 弯曲模量 [MPa]: 1.31
- 硬度: 85.0
- 热变形温度 [℃]: 95.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength at Break | 31.0 MPa | 4500 psi | at max load; ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Flexural Modulus | 1.31 GPa | 190 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Gardner Impact | 10.2 J | 7.50 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
| Haze | 11 % @Thickness 50.0 mm | 11 % @Thickness 1.97 in | ASTM D1003 |