- 熔体流动速率 [g/10min]: 1.5
- 缺口冲击强度: 2.67
- 拉伸强度 [MPa]: 25.5
- 弯曲模量 [MPa]: 1.17
- 热变形温度 [℃]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Flow | 1.5 g/10 min @Temperature 230 °C | 1.5 g/10 min @Temperature 446 °F | Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.5 MPa | 3700 psi | 2 in/min; ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Flexural Modulus | 1.17 GPa | 170 ksi | ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Gardner Impact | 2.03 J @Temperature -28.9 °C | 1.50 ft-lb @Temperature -20.0 °F | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ASTM D648 |