- 熔体流动速率 [g/10min]: 20.0
- 缺口冲击强度: 0.26
- 拉伸强度 [MPa]: 36.0
- 弯曲模量 [MPa]: 1.83
- 硬度: 113.0
- 热变形温度 [℃]: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.907 g/cc | 0.907 g/cc | ASTM D792 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C | 20 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 113 | 113 | ASTM D785 |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50 mm/min; ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | ASTM D638 |
| Flexural Modulus | 1.83 GPa | 265 ksi | 5 mm/min, tangent; ASTM D790 |
| Izod Impact, Notched | 0.260 J/cm | 0.487 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |