- 熔体流动速率 [g/10min]: 2.0
- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 28.3
- 弯曲模量 [MPa]: 1.03
- 热变形温度 [℃]: 93.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Modulus | 1.03 GPa | 150 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | at 0°F; ASTM D256 |
| 0.694 J/cm | 1.30 ft-lb/in | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |