- 成型收缩率 [%]: 0.009
- 弯曲强度 [MPa]: 38.0
- 弯曲模量 [MPa]: 0.125
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 - 0.014 cm/cm @Thickness 3.20 mm | 0.0090 - 0.014 in/in @Thickness 0.126 in | 72 hr; ASTM D955 |
| 0.011 - 0.016 cm/cm @Thickness 3.20 mm | 0.011 - 0.016 in/in @Thickness 0.126 in | 48 hr, at 121°C; ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 55 | 55 | 15 sec delay; ASTM D2240 |
| Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ASTM D638 |
| Elongation at Break | 450 % | 450 % | 20 in/min; ASTM D412 |
| Flexural Modulus | 0.125 GPa | 18.1 ksi | 1.3 mm/min; ASTM D790 |
| Tear Strength | 20.2 kN/m | 115 pli | 2 in/min; ASTM D624 |
| Compression Set | 30 % | 30 % | Method B, 22 h, 23°C; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 120 µm/m-°C @Temperature -30.0 - 30.0 °C | 66.7 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM E831 |