- 成型收缩率 [%]: 0.001
- 缺口冲击强度: 5.0
- 拉伸强度 [MPa]: 26.0
- 弯曲强度 [MPa]: 31.0
- 弯曲模量 [MPa]: 0.750
- 热变形温度 [℃]: 75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm | 0.0010 - 0.0030 in/in @Thickness 0.126 in | 48 hr, at 80 and 121°C; ASTM D955 |
| 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm | 0.0010 - 0.0030 in/in @Thickness 0.126 in | 72 hr; ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 56 | 56 | 15 sec delay; ASTM D2240 |
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | 2 in/min, at max load; ASTM D638 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 2 in/min; ASTM D638 |
| Elongation at Break | 400 % | 400 % | ASTM D412 |
| Flexural Modulus | 0.750 GPa | 109 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 5.00 J/cm | 9.37 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 11.1 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ASTM D648 |