- 缺口冲击强度: 0.908
- 拉伸强度 [MPa]: 28.3
- 弯曲模量 [MPa]: 1.24
- 热变形温度 [℃]: 87.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Index of Compound | 8.0 g/10 min @Temperature 230 °C | 8.0 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
| Elongation at Yield | 12 % | 12 % | ASTM D638 |
| Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Gardner Impact | 20.00 J @Thickness 3.20 mm, Temperature -30.0 °C | 14.75 ft-lb @Thickness 0.126 in, Temperature -22.0 °F | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |