- 密度 [g/cm3]: 0.9
- 缺口冲击强度: 0.481
- 拉伸强度 [MPa]: 33.1
- 弯曲模量 [MPa]: 1.31
- 硬度: 105.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D1505 |
| Melt Index of Compound | 1.1 g/10 min @Temperature 230 °C | 1.1 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 33.1 MPa | 4800 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | >= 10 % | >= 10 % | 50 mm/min; ASTM D638 |
| Flexural Modulus | 1.31 GPa | 190 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Temperature 22.8 °C | 0.900 ft-lb/in @Temperature 73.0 °F | ASTM D256 |