- 密度 [g/cm3]: 0.9
- 缺口冲击强度: 5.87
- 拉伸强度 [MPa]: 22.1
- 弯曲模量 [MPa]: 1.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D1505 |
| Melt Index of Compound | 10 g/10 min @Temperature 230 °C | 10 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.1 MPa | 3200 psi | 50 mm/min; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ASTM D638 |
| Flexural Modulus | 1.00 GPa | 145 ksi | 1.3 mm/min, 1% Secant; ASTM D790 |
| Izod Impact, Notched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D256 |