- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.9
- 缺口冲击强度: 15.0
- 拉伸强度 [MPa]: 22.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 58 | 58 | ISO 868 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 6.0 % | 6.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.10 GPa | 160 ksi | At 1 mm/min; ISO 527-2 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 108/1A |
| Peel Strength | >= 3.00 kN/m | >= 17.1 pli | 3-layer at 140°C; DIN 30678 |
| >= 4.00 kN/m | >= 22.8 pli | 3-layer at 110°C; DIN 30678 | |
| >= 10.0 kN/m | >= 57.1 pli | 3-layer at 80°C; DIN 30678 | |
| >= 20.0 kN/m | >= 114 pli | 3-layer; DIN 30678 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 145 °C | 293 °F | A50 (10 N); ISO 306 |
| Processing Properties | Metric | English | Comments |
| Front Barrel Temperature | 235 - 245 °C | 455 - 473 °F | |
| Head Temperature | 235 - 245 °C | 455 - 473 °F | |