- 熔体流动速率 [g/10min]: 22.0
- 密度 [g/cm3]: 0.92
- 拉伸强度 [MPa]: 35.0
- 弯曲模量 [MPa]: 1.85
- 热变形温度 [℃]: 108.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ISO 1183 | ||
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 230 °C | 22 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| 96 g/10 min @Load 5.00 kg, Temperature 230 °C | 96 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 85.0 MPa | 12300 psi | H 385/30; ISO 2039 | ||
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | At 50 mm/min; ISO 527-2 | ||
| Tensile Modulus | 2.00 GPa | 290 ksi | At 1 mm/min; ISO 527-2 | ||
| Flexural Modulus | 1.85 GPa | 268 ksi | At 2 mm/min; ISO 178 | ||
| Charpy Impact Unnotched | 10.2 J/cm² | 48.5 ft-lb/in² | ISO 179/1eU | ||
| 3.50 J/cm² @Temperature -20.0 °C | 16.7 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA | ||
| 0.150 J/cm² @Temperature -20.0 °C | 0.714 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-2 | ||
| Vicat Softening Point | 95.0 °C | 203 °F | B (50N); ISO 306 | ||
| 156 °C | 313 °F | A (10N); ISO 306 | |||
| Shrinkage | 1.5 % @Thickness 2.00 mm | 1.5 % @Thickness 0.0787 in | disk; Borealis Method | ||
| Optical Properties | Metric | English | Comments | ||
| Gloss | 75 % | 75 % | 20°; DIN 67530 | ||
| 95 % | 95 % | 60°; DIN 67530 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | Polymer Mass Temp | ||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Descriptive Properties | |||||
| Emissions, ug C/g | 30 | VDA 277 | |||
| Fogging, mg | 1.1 | At 100°C/ 16 hours | |||