- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.905
- 拉伸强度 [MPa]: 36.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ISO 1183 |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| 0.60 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.60 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 10 % | 10 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.65 GPa | 239 ksi | 1mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C | 0.952 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA |
| 0.700 J/cm² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 95.0 °C @Load 5.10 kg | 203 °F @Load 11.2 lb | B50; ISO 306 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 190 - 230 °C | 374 - 446 °F | cylinder |
| Die Temperature | 200 - 230 °C | 392 - 446 °F | |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | |
| Head Temperature | 200 - 230 °C | 392 - 446 °F | |