- 熔体流动速率 [g/10min]: 96.0
- 密度 [g/cm3]: 0.91
- 拉伸强度 [MPa]: 26.0
- 弯曲模量 [MPa]: 1.40
- 热变形温度 [℃]: 100.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ISO 1183 | ||
| Melt Flow | 96 g/10 min @Load 5.00 kg, Temperature 230 °C | 96 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 66.0 MPa | 9570 psi | H 385/30; ISO 2039 | ||
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | At 50 mm/min; ISO 527-2 | ||
| Elongation at Yield | 6.0 % | 6.0 % | At 50 mm/min; ISO 527-2 | ||
| Tensile Modulus | 1.50 GPa | 218 ksi | At 1 mm/min; ISO 527-2 | ||
| Flexural Modulus | 1.40 GPa | 203 ksi | At 2 mm/min; ISO 178 | ||
| Charpy Impact Unnotched | 6.70 J/cm² @Temperature -20.0 °C | 31.9 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA | ||
| 0.320 J/cm² @Temperature -20.0 °C | 1.52 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | ISO 75-2 | ||
| Vicat Softening Point | 75.0 °C | 167 °F | B (50N); ISO 306 | ||
| 150 °C | 302 °F | A (10N); ISO 306 | |||
| Shrinkage | 1.6 % | 1.6 % | Borealis Method | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | Polymer Mass Temp | ||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Descriptive Properties | |||||
| Emissions, ug C/g | 37 | VDA 277 | |||
| Fogging, mg | 0.9 | At 100°C/ 16 hours | |||