- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.9
- 弯曲模量 [MPa]: 0.700
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 - 0.910 g/cc | 0.0325 - 0.0329 lb/in³ | ISO 1183 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 400 - 500 % | 400 - 500 % | MD/TD; ISO 527-3 |
| Tensile Modulus | 0.650 - 0.850 GPa | 94.3 - 123 ksi | MD/TD; ISO 527-3 |
| Flexural Modulus | 0.700 GPa | 102 ksi | ISO 178 |
| Dart Drop, Total Energy | 28.0 J | 20.7 ft-lb | 1050N; ISO 7765-2 |
| Coefficient of Friction | >= 0.70 | >= 0.70 | film to film; ISO 8295 |
| Film Tensile Strength at Break, MD | 45.0 - 55.0 MPa | 6530 - 7980 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 35.0 - 45.0 MPa | 5080 - 6530 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 128 - 132 °C | 262 - 270 °F | ISO 3146 |
| Vicat Softening Point | 114 °C | 237 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 1.3 % | <= 1.3 % | ASTM D1003 |
| Gloss | >= 135 % | >= 135 % | 20° of arc; ASTM D2457 |