- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.905
- 弯曲模量 [MPa]: 1.45
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ISO 1183 |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Flexural Modulus | 1.45 GPa | 210 ksi | 50% humidity; ISO 178 |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C | 0.952 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA |
| 2.50 J/cm² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 166 °C | 331 °F | |
| Vicat Softening Point | 154 °C @Load 1.02 kg | 309 °F @Load 2.25 lb | A50; ISO 306 |