- 密度 [g/cm3]: 1.71
- 缺口冲击强度: 1.12
- 弯曲强度 [MPa]: 135.0
- 弯曲模量 [MPa]: 16.5
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.71 g/cc | 1.71 g/cc | ASTM D 792 | ||
Density | 1.71 g/cc | 0.0618 lb/in³ | ISO 1183 | ||
Filler Content | 40 % | 40 % | |||
Linear Mold Shrinkage, Flow | 0.00050 cm/cm @Thickness 2.00 mm | 0.00050 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Thickness 2.00 mm | 0.0050 in/in @Thickness 0.0787 in | ISO 294-4 | ||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 | ||
Tensile Strength, Ultimate | 135 MPa @Thickness 3.17 mm, Temperature 23.0 °C | 19600 psi @Thickness 0.125 in, Temperature 73.4 °F | ASTM D638 | ||
Elongation at Break | 1.1 % | 1.1 % | ISO 527 | ||
1.3 % @Thickness 3.17 mm, Temperature 23.0 °C | 1.3 % @Thickness 0.125 in, Temperature 73.4 °F | ASTM D638 | |||
Tensile Modulus | 17.0 GPa @Temperature 23.0 °C | 2470 ksi @Temperature 73.4 °F | ISO 527 | ||
Flexural Strength | 190 MPa @Temperature 23.0 °C | 27600 psi @Temperature 73.4 °F | ISO 178 | ||
183 MPa @Thickness 3.17 mm, Temperature 23.0 °C | 26500 psi @Thickness 0.125 in, Temperature 73.4 °F | ASTM D790 | |||
Flexural Modulus | 16.5 GPa @Temperature 23.0 °C | 2390 ksi @Temperature 73.4 °F | ISO 178 | ||
15.6 GPa @Thickness 3.17 mm, Temperature 23.0 °C | 2260 ksi @Thickness 0.125 in, Temperature 73.4 °F | ASTM D790 | |||
Izod Impact, Notched | 1.12 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 2.10 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 | ||
Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | ||
Izod Impact, Unnotched (ISO) | 20.0 kJ/m² @Temperature -30.0 °C | 9.52 ft-lb/in² @Temperature -22.0 °F | ISO 180/1U | ||
20.0 kJ/m² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U | |||
Charpy Impact Unnotched | 2.00 J/cm² @Temperature -30.0 °C | 9.52 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
2.30 J/cm² @Temperature 23.0 °C | 10.9 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C | 7.14 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
1.50 J/cm² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | |||
Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 | |||
Dielectric Strength | 27.0 kV/mm @Thickness 2.00 mm | 686 kV/in @Thickness 0.0787 in | IEC 60243-1 | ||
45.0 kV/mm @Thickness 1.00 mm | 1140 kV/in @Thickness 0.0394 in | IEC 60243-1 | |||
Comparative Tracking Index | 175 V | 175 V | IEC 60112 | ||
175 - 249 V | 175 - 249 V | UL 746A | |||
Thermal Properties | Metric | English | Comments | ||
CTE, linear | 0.000 µm/m-°C @Thickness 2.00 mm, Temperature 160 - 260 °C | 0.000 µin/in-°F @Thickness 0.0787 in, Temperature 320 - 500 °F | ISO 11359-1/-2 | ||
2.00 µm/m-°C @Thickness 4.00 mm, Temperature 160 - 260 °C | 1.11 µin/in-°F @Thickness 0.157 in, Temperature 320 - 500 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 23.0 °C | 1.67 µin/in-°F @Thickness 0.157 in, Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 2.00 mm, Temperature -40.0 - 23.0 °C | 1.67 µin/in-°F @Thickness 0.0787 in, Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 2.00 mm, Temperature -40.0 - 260 °C | 1.67 µin/in-°F @Thickness 0.0787 in, Temperature -40.0 - 500 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 260 °C | 1.67 µin/in-°F @Thickness 0.157 in, Temperature -40.0 - 500 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 1.67 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 2.00 mm, Temperature 55.0 - 160 °C | 1.67 µin/in-°F @Thickness 0.0787 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
4.00 µm/m-°C @Thickness 4.00 mm, Temperature 23.0 - 55.0 °C | 2.22 µin/in-°F @Thickness 0.157 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
5.00 µm/m-°C @Thickness 4.00 mm, Temperature 55.0 - 160 °C | 2.78 µin/in-°F @Thickness 0.157 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 30.6 µin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2; 2mm | ||
56.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 31.1 µin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2; 4mm | |||
77.0 µm/m-°C @Temperature -40.0 - 260 °C | 42.8 µin/in-°F @Temperature -40.0 - 500 °F | ISO 11359-1/-2; 2mm | |||
79.0 µm/m-°C @Temperature -40.0 - 260 °C | 43.9 µin/in-°F @Temperature -40.0 - 500 °F | ISO 11359-1/-2; 4mm | |||
62.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 34.4 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
64.0 µm/m-°C @Thickness 4.00 mm, Temperature 23.0 - 55.0 °C | 35.6 µin/in-°F @Thickness 0.157 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
80.0 µm/m-°C @Thickness 2.00 mm, Temperature 55.0 - 160 °C | 44.4 µin/in-°F @Thickness 0.0787 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
82.0 µm/m-°C @Thickness 4.00 mm, Temperature 55.0 - 160 °C | 45.6 µin/in-°F @Thickness 0.157 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
90.0 µm/m-°C @Thickness 2.00 mm, Temperature 160 - 260 °C | 50.0 µin/in-°F @Thickness 0.0787 in, Temperature 320 - 500 °F | ISO 11359-1/-2 | |||
94.0 µm/m-°C @Thickness 4.00 mm, Temperature 160 - 260 °C | 52.2 µin/in-°F @Thickness 0.157 in, Temperature 320 - 500 °F | ISO 11359-1/-2 | |||
Melting Point | 335 °C | 635 °F | ASTM D 3418 | ||
335 °C | 635 °F | 10°C/min; ISO 11357-1/-3 | |||
Deflection Temperature at 1.8 MPa (264 psi) | 271 °C | 520 °F | ASTM D 648 | ||
280 °C | 536 °F | ISO 75-1/-2 | |||
Glass Transition Temp, Tg | 120 °C | 248 °F | ASTM D 3418 | ||
UL RTI, Electrical | 240 °C @Thickness 1.50 mm | 464 °F @Thickness 0.0591 in | UL 746B | ||
240 °C @Thickness 0.750 mm | 464 °F @Thickness 0.0295 in | UL 746B | |||
240 °C @Thickness 3.00 mm | 464 °F @Thickness 0.118 in | UL 746B | |||
UL RTI, Mechanical with Impact | 220 °C @Thickness 1.50 mm | 428 °F @Thickness 0.0591 in | UL 746B | ||
220 °C @Thickness 0.750 mm | 428 °F @Thickness 0.0295 in | UL 746B | |||
220 °C @Thickness 3.00 mm | 428 °F @Thickness 0.118 in | UL 746B | |||
UL RTI, Mechanical without Impact | 240 °C @Thickness 1.50 mm | 464 °F @Thickness 0.0591 in | UL 746B | ||
240 °C @Thickness 0.750 mm | 464 °F @Thickness 0.0295 in | UL 746B | |||
240 °C @Thickness 3.00 mm | 464 °F @Thickness 0.118 in | UL 746B | |||
Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | ||
V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | IEC 60695-11-10 | |||
V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | |||
V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | UL94 | |||
V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | IEC 60695-11-10 | |||
V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | UL94 | |||
V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | IEC 60695-11-10 | |||
V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL94 | |||
Glow Wire Test | 800 °C @Thickness 0.700 mm | 1470 °F @Thickness 0.0276 in | Glow Wire Ignition Temperature; IEC 60695-2-13 | ||
800 °C @Thickness 1.00 mm | 1470 °F @Thickness 0.0394 in | Glow Wire Ignition Temperature; IEC 60695-2-13 | |||
800 °C @Thickness 2.00 mm | 1470 °F @Thickness 0.0787 in | Glow Wire Ignition Temperature; IEC 60695-2-13 | |||
900 °C @Thickness 3.00 mm | 1650 °F @Thickness 0.118 in | Glow Wire Ignition Temperature; IEC 60695-2-13 | |||
960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | Glow Wire Flammability Index; IEC 60695-2-12 | |||
960 °C @Thickness 2.00 mm | 1760 °F @Thickness 0.0787 in | Glow Wire Flammability Index; IEC 60695-2-12 | |||
960 °C @Thickness 0.700 mm | 1760 °F @Thickness 0.0276 in | Glow Wire Flammability Index; IEC 60695-2-12 | |||
960 °C @Thickness 1.00 mm | 1760 °F @Thickness 0.0394 in | Glow Wire Flammability Index; IEC 60695-2-12 | |||
Processing Properties | Metric | English | Comments | ||
Melt Temperature | 355 °C | 671 °F | Optimum | ||
350 - 360 °C | 662 - 680 °F | ||||
Mold Temperature | 80.0 °C | 176 °F | Optimum | ||
40.0 - 150 °C | 104 - 302 °F | ||||
Drying Temperature | 150 °C | 302 °F | |||
Dry Time | 3 hour | 3 hour | Dehumidified Dryer | ||
Moisture Content | <= 0.010 % | <= 0.010 % | |||
Descriptive Properties | |||||
Additive | Lubricant | ||||
Color | Black | ||||
Drying Recommended | Yes | ||||
Features | Appearance, Pleasing Surface | ||||
Arc Resistant | |||||
Aromatic | |||||
Chemical Resistance, Good | |||||
Dimensional Stability, Good | |||||
Flow, Good | |||||
Heat Aging Resistance, Good | |||||
Lubricated | |||||
Moisture Absorption, Low | |||||
Platable | |||||
Filler | Glass fiber reinforcement | ||||
Flame Retardant - Halogen/Red Phosphorus Free | Yes | ||||
Forms | Pellets | ||||
Generic | LCP | ||||
Part Marking Code | >LCP-GF40< | ISO 11469 | |||
Polymer Family | LCP | ||||
Polymer Type | LCP | ||||
Processing | Injection Moldable | ||||
Processing Method | Injection Molding | ||||
Product Category | Electrical Resins | ||||
Flame Retardant Resins | |||||
Glass Reinforced Resins | |||||
Region Available | Americas | ||||
Asia/Pacific | |||||
Europe | |||||
Resin Identification | LCP-GF40 | ISO 1043 | |||
Uses | Automotive Applications | ||||
Automotive Electronics | |||||
Automotive, Under the Hood | |||||
Communication Applications | |||||
Computer Components | |||||
Connectors | |||||
Electrical/Electronic Applications | |||||
Parts, Engineering | |||||
Parts, Thin-walled | |||||
Printer Parts |