  4. Celanese Zenite® 6130 BK010 LCP

Celanese Zenite® 6130 BK010 LCP

Celanese Zenite® 6130 BK010 LCP 物性表: Celanese Zenite® 6130 BK010 LCP物性表及特性介绍,Celanese Zenite® 6130 BK010 LCP注塑参数详情,如需Celanese Zenite® 6130 BK010 LCP下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.62
  • 弯曲模量 [MPa]: 11.0
  • 热变形温度 [℃]: 300.0
 
Physical PropertiesMetricEnglishComments
Density 1.62 g/cc0.0585 lb/in³ISO 1183
Linear Mold Shrinkage, Flow 0.00050 cm/cm
@Thickness 2.00 mm		0.00050 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
@Thickness 2.00 mm		0.0080 in/in
@Thickness 0.0787 in		ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 130 MPa18900 psiISO 527
Elongation at Break 2.0 %2.0 %ISO 527
Tensile Modulus 13.0 GPa
@Temperature 23.0 °C		1890 ksi
@Temperature 73.4 °F		ISO 527
Flexural Strength 190 MPa
@Temperature 23.0 °C		27600 psi
@Temperature 73.4 °F		ISO 178
Flexural Modulus 11.0 GPa
@Temperature 23.0 °C		1600 ksi
@Temperature 73.4 °F		ISO 178
Charpy Impact Unnotched  3.00 J/cm²
@Temperature -30.0 °C		14.3 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 4.00 J/cm²
@Temperature 23.0 °C		19.0 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  3.00 J/cm²
@Temperature -30.0 °C		14.3 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 3.50 J/cm²
@Temperature 23.0 °C		16.7 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+15 ohm-cm>= 1.00e+15 ohm-cmIEC 60093
 1.00e+16 ohm-cm1.00e+16 ohm-cmIEC 60093
Surface Resistance >= 1.00e+15 ohm>= 1.00e+15 ohmIEC 60093
 1.00e+16 ohm1.00e+16 ohmIEC 60093
Dielectric Constant 4.5
@Frequency 100 Hz		4.5
@Frequency 100 Hz		IEC 60250
 4.0
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.0
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 4.2
@Frequency 1000 Hz,
Temperature 23.0 °C		4.2
@Frequency 1000 Hz,
Temperature 73.4 °F		IEC 60250
 4.3
@Frequency 1.00e+6 Hz,
Temperature 100 °C		4.3
@Frequency 1.00e+6 Hz,
Temperature 212 °F		IEC 60250
 4.3
@Frequency 1.00e+6 Hz,
Temperature 150 °C		4.3
@Frequency 1.00e+6 Hz,
Temperature 302 °F		IEC 60250
 4.3
@Frequency 1.00e+6 Hz,
Temperature 200 °C		4.3
@Frequency 1.00e+6 Hz,
Temperature 392 °F		IEC 60250
 4.5
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		4.5
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		4.0mm; ASTM D 2520 B
 4.6
@Frequency 1000 Hz,
Temperature 200 °C		4.6
@Frequency 1000 Hz,
Temperature 392 °F		IEC 60250
 4.6
@Frequency 1000 Hz,
Temperature 150 °C		4.6
@Frequency 1000 Hz,
Temperature 302 °F		IEC 60250
 4.6
@Frequency 1.00e+10 Hz,
Temperature 23.0 °C		4.6
@Frequency 1.00e+10 Hz,
Temperature 73.4 °F		4.0mm; ASTM D 2520 B
 4.6
@Frequency 1000 Hz,
Temperature 100 °C		4.6
@Frequency 1000 Hz,
Temperature 212 °F		IEC 60250
 4.7
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		4.7
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		2.0mm; ASTM D 2520 B
 4.8
@Frequency 1.00e+10 Hz,
Temperature 23.0 °C		4.8
@Frequency 1.00e+10 Hz,
Temperature 73.4 °F		2.0mm; ASTM D 2520 B
Dielectric Strength  29.0 kV/mm
@Thickness 2.00 mm		737 kV/in
@Thickness 0.0787 in		IEC 60243-1
 36.0 kV/mm
@Thickness 1.00 mm		914 kV/in
@Thickness 0.0394 in		IEC 60243-1
Dissipation Factor  0.0070
@Frequency 1.00e+6 Hz,
Temperature 200 °C		0.0070
@Frequency 1.00e+6 Hz,
Temperature 392 °F		IEC 60250
 0.0090
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		0.0090
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		2.0mm; ASTM D 2520 B
 0.0090
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		0.0090
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		4.0mm; ASTM D 2520 B
 0.010
@Frequency 1.00e+10 Hz,
Temperature 23.0 °C		0.010
@Frequency 1.00e+10 Hz,
Temperature 73.4 °F		4.0mm; ASTM D 2520 B
 0.010
@Frequency 1000 Hz,
Temperature 100 °C		0.010
@Frequency 1000 Hz,
Temperature 212 °F		IEC 60250
 0.010
@Frequency 1000 Hz,
Temperature 150 °C		0.010
@Frequency 1000 Hz,
Temperature 302 °F		IEC 60250
 0.011
@Frequency 1.00e+10 Hz,
Temperature 23.0 °C		0.011
@Frequency 1.00e+10 Hz,
Temperature 73.4 °F		2.0mm; ASTM D 2520 B
 0.013
@Frequency 1000 Hz,
Temperature 200 °C		0.013
@Frequency 1000 Hz,
Temperature 392 °F		IEC 60250
 0.015
@Frequency 100 Hz,
Temperature 23.0 °C		0.015
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.016
@Frequency 1000 Hz,
Temperature 23.0 °C		0.016
@Frequency 1000 Hz,
Temperature 73.4 °F		IEC 60250
 0.018
@Frequency 1.00e+6 Hz,
Temperature 150 °C		0.018
@Frequency 1.00e+6 Hz,
Temperature 302 °F		IEC 60250
 0.031
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.031
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 0.045
@Frequency 1.00e+6 Hz,
Temperature 100 °C		0.045
@Frequency 1.00e+6 Hz,
Temperature 212 °F		IEC 60250
Comparative Tracking Index 100 - 174 V100 - 174 VUL 746A
 175 V175 VIEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear  -5.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 160 - 260 °C		-2.78 µin/in-°F
@Thickness 0.0787 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 -2.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 160 - 260 °C		-1.11 µin/in-°F
@Thickness 0.157 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 1.00 µm/m-°C
@Thickness 2.00 mm,
Temperature -40.0 - 260 °C		0.556 µin/in-°F
@Thickness 0.0787 in,
Temperature -40.0 - 500 °F		ISO 11359-1/-2
 2.00 µm/m-°C
@Thickness 4.00 mm,
Temperature -40.0 - 260 °C		1.11 µin/in-°F
@Thickness 0.157 in,
Temperature -40.0 - 500 °F		ISO 11359-1/-2
 2.00 µm/m-°C
@Thickness 2.00 mm,
Temperature -40.0 - 23.0 °C		1.11 µin/in-°F
@Thickness 0.0787 in,
Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 2.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 55.0 - 160 °C		1.11 µin/in-°F
@Thickness 0.0787 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C		1.67 µin/in-°F
@Thickness 0.157 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		1.67 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 55.0 - 160 °C		1.67 µin/in-°F
@Thickness 0.157 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 4.00 mm,
Temperature -40.0 - 23.0 °C		1.67 µin/in-°F
@Thickness 0.157 in,
Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  60.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		33.3 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2; 2mm
 61.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		33.9 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2; 4mm
 85.0 µm/m-°C
@Temperature -40.0 - 260 °C		47.2 µin/in-°F
@Temperature -40.0 - 500 °F		ISO 11359-1/-2; 2mm
 88.0 µm/m-°C
@Temperature -40.0 - 260 °C		48.9 µin/in-°F
@Temperature -40.0 - 500 °F		ISO 11359-1/-2; 4mm
 68.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		37.8 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 70.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C		38.9 µin/in-°F
@Thickness 0.157 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 88.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 55.0 - 160 °C		48.9 µin/in-°F
@Thickness 0.0787 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 92.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 55.0 - 160 °C		51.1 µin/in-°F
@Thickness 0.157 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 101 µm/m-°C
@Thickness 2.00 mm,
Temperature 160 - 260 °C		56.1 µin/in-°F
@Thickness 0.0787 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 107 µm/m-°C
@Thickness 4.00 mm,
Temperature 160 - 260 °C		59.4 µin/in-°F
@Thickness 0.157 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
Melting Point 335 °C635 °F10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 300 °C572 °FISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 268 °C514 °FISO 75-1/-2
Glass Transition Temp, Tg 120 °C248 °F10°C/min; ISO 11357-1/-2
UL RTI, Electrical  240 °C
@Thickness 1.50 mm		464 °F
@Thickness 0.0591 in		UL 746B
 240 °C
@Thickness 0.750 mm		464 °F
@Thickness 0.0295 in		UL 746B
 240 °C
@Thickness 3.00 mm		464 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical with Impact  220 °C
@Thickness 1.50 mm		428 °F
@Thickness 0.0591 in		UL 746B
 220 °C
@Thickness 0.750 mm		428 °F
@Thickness 0.0295 in		UL 746B
 220 °C
@Thickness 3.00 mm		428 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical without Impact  240 °C
@Thickness 1.50 mm		464 °F
@Thickness 0.0591 in		UL 746B
 240 °C
@Thickness 0.750 mm		464 °F
@Thickness 0.0295 in		UL 746B
 240 °C
@Thickness 3.00 mm		464 °F
@Thickness 0.118 in		UL 746B
Flammability, UL94  V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		IEC 60695-11-10
 V-0
@Thickness 0.380 mm		V-0
@Thickness 0.0150 in		IEC 60695-11-10
 V-0
@Thickness 0.750 mm		V-0
@Thickness 0.0295 in		IEC 60695-11-10
 V-0
@Thickness 0.750 mm		V-0
@Thickness 0.0295 in		UL94
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		UL94
 V-0
@Thickness 0.380 mm		V-0
@Thickness 0.0150 in		UL94
 V-0
@Thickness 0.190 mm		V-0
@Thickness 0.00748 in		IEC 60695-11-10
 V-0
@Thickness 0.190 mm		V-0
@Thickness 0.00748 in		UL94
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		IEC 60695-11-10
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		UL94
Oxygen Index 41 %41 %ISO 4589-1/-2
Glow Wire Test  800 °C
@Thickness 0.700 mm		1470 °F
@Thickness 0.0276 in		Glow Wire Ignition Temperature; IEC 60695-2-13
 800 °C
@Thickness 1.00 mm		1470 °F
@Thickness 0.0394 in		Glow Wire Ignition Temperature; IEC 60695-2-13
 825 °C
@Thickness 2.00 mm		1520 °F
@Thickness 0.0787 in		Glow Wire Ignition Temperature; IEC 60695-2-13
 875 °C
@Thickness 3.00 mm		1610 °F
@Thickness 0.118 in		Glow Wire Ignition Temperature; IEC 60695-2-13
 960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		Glow Wire Flammability Index; IEC 60695-2-12
 960 °C
@Thickness 2.00 mm		1760 °F
@Thickness 0.0787 in		Glow Wire Flammability Index; IEC 60695-2-12
 960 °C
@Thickness 1.00 mm		1760 °F
@Thickness 0.0394 in		Glow Wire Flammability Index; IEC 60695-2-12
 960 °C
@Thickness 0.700 mm		1760 °F
@Thickness 0.0276 in		Glow Wire Flammability Index; IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 355 °C671 °FOptimum
 350 - 360 °C662 - 680 °F
Mold Temperature 80.0 °C176 °FOptimum
 40.0 - 150 °C104 - 302 °F
Drying Temperature 150 °C302 °F
Dry Time 3 hour3 hourDehumidified Dryer
Moisture Content <= 0.010 %<= 0.010 %
 
Descriptive Properties
ColorBlack
Drying RecommendedYes
FeaturesAppearance, Pleasing Surface
 Arc Resistant
 Aromatic
 Chemical Resistance, Good
 Dimensional Stability, Good
 Flow, Good
 Heat Aging Resistance, Good
 Moisture Absorption, Low
 Platable
FillerGlass fiber reinforcement
Flame Retardant - Halogen/Red Phosphorus FreeYes
FormsPellets
GenericLCP
Part Marking Code>LCP-GF30<ISO 11469
Polymer FamilyLCP
Polymer TypeLCP
ProcessingInjection Moldable
Processing MethodInjection Molding
Product CategoryElectrical Resins
 Flame Retardant Resins
 Glass Reinforced Resins
Region AvailableAmericas
 Asia/Pacific
 Europe
Resin IdentificationLCP-GF30ISO 1043
UsesAutomotive Applications
 Automotive Electronics
 Automotive, Under the Hood
 Communication Applications
 Computer Components
 Connectors
 Electrical/Electronic Applications
 Parts, Engineering
 Parts, Thin-walled
 Printer Parts

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31765.html

免责声明: 本文 Celanese Zenite® 6130 BK010 LCP 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4