Celanese Zenite® 6330 BK010 LCP

Celanese Zenite® 6330 BK010 LCP 物性表: Celanese Zenite® 6330 BK010 LCP物性表及特性介绍,Celanese Zenite® 6330 BK010 LCP注塑参数详情,如需Celanese Zenite® 6330 BK010 LCP下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.64
  • 缺口冲击强度: 1.6
  • 弯曲强度 [MPa]: 17.0
  • 弯曲模量 [MPa]: 8.00
  • 热变形温度 [℃]: 275.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.64 g/cc1.64 g/ccASTM D 792
Density 1.64 g/cc0.0592 lb/in³ISO 1183
Filler Content 30 %30 %
Linear Mold Shrinkage, Flow  0.00 cm/cm
@Thickness 3.17 mm		0.00 in/in
@Thickness 0.125 in		ASTM D955
 0.00 cm/cm
@Thickness 2.00 mm		0.00 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse  0.0040 cm/cm
@Thickness 2.00 mm		0.0040 in/in
@Thickness 0.0787 in		ISO 294-4
 0.0050 cm/cm
@Thickness 3.17 mm		0.0050 in/in
@Thickness 0.125 in		ASTM D955
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 125 MPa18100 psiISO 527
Tensile Strength, Ultimate  17.0 MPa
@Thickness 1.60 mm,
Temperature 250 °C		2470 psi
@Thickness 0.0630 in,
Temperature 482 °F		ASTM D638
 26.0 MPa
@Thickness 1.60 mm,
Temperature 200 °C		3770 psi
@Thickness 0.0630 in,
Temperature 392 °F		ASTM D638
 48.0 MPa
@Thickness 3.17 mm,
Temperature 150 °C		6960 psi
@Thickness 0.125 in,
Temperature 302 °F		ASTM D638
 49.0 MPa
@Thickness 1.60 mm,
Temperature 150 °C		7110 psi
@Thickness 0.0630 in,
Temperature 302 °F		ASTM D638
 56.0 MPa
@Thickness 3.17 mm,
Temperature 120 °C		8120 psi
@Thickness 0.125 in,
Temperature 248 °F		ASTM D638
 59.0 MPa
@Thickness 1.60 mm,
Temperature 120 °C		8560 psi
@Thickness 0.0630 in,
Temperature 248 °F		ASTM D638
 125 MPa
@Thickness 3.17 mm,
Temperature 23.0 °C		18100 psi
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D638
 141 MPa
@Thickness 1.60 mm,
Temperature 23.0 °C		20500 psi
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D638
 200 MPa
@Thickness 3.17 mm,
Temperature -40.0 °C		29000 psi
@Thickness 0.125 in,
Temperature -40.0 °F		ASTM D638
 216 MPa
@Thickness 1.60 mm,
Temperature -40.0 °C		31300 psi
@Thickness 0.0630 in,
Temperature -40.0 °F		ASTM D638
Elongation at Break 4.2 %4.2 %ISO 527
 0.70 %
@Thickness 1.60 mm,
Temperature 250 °C		0.70 %
@Thickness 0.0630 in,
Temperature 482 °F		ASTM D638
 0.90 %
@Thickness 1.60 mm,
Temperature 200 °C		0.90 %
@Thickness 0.0630 in,
Temperature 392 °F		ASTM D638
 1.5 %
@Thickness 1.60 mm,
Temperature 150 °C		1.5 %
@Thickness 0.0630 in,
Temperature 302 °F		ASTM D638
 2.0 %
@Thickness 1.60 mm,
Temperature 120 °C		2.0 %
@Thickness 0.0630 in,
Temperature 248 °F		ASTM D638
 2.5 %
@Thickness 3.17 mm,
Temperature 150 °C		2.5 %
@Thickness 0.125 in,
Temperature 302 °F		ASTM D638
 2.8 %
@Thickness 1.60 mm,
Temperature -40.0 °C		2.8 %
@Thickness 0.0630 in,
Temperature -40.0 °F		ASTM D638
 3.2 %
@Thickness 3.17 mm,
Temperature 120 °C		3.2 %
@Thickness 0.125 in,
Temperature 248 °F		ASTM D638
 3.3 %
@Thickness 1.60 mm,
Temperature 23.0 °C		3.3 %
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D638
 4.0 %
@Thickness 3.17 mm,
Temperature 23.0 °C		4.0 %
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D638
Tensile Modulus 9.20 GPa
@Temperature 23.0 °C		1330 ksi
@Temperature 73.4 °F		ISO 527
 2.77 GPa
@Thickness 1.60 mm,
Temperature 250 °C		402 ksi
@Thickness 0.0630 in,
Temperature 482 °F		ASTM D638
 3.75 GPa
@Thickness 1.60 mm,
Temperature 200 °C		544 ksi
@Thickness 0.0630 in,
Temperature 392 °F		ASTM D638
 4.80 GPa
@Thickness 3.17 mm,
Temperature 150 °C		696 ksi
@Thickness 0.125 in,
Temperature 302 °F		ASTM D638
 5.80 GPa
@Thickness 1.60 mm,
Temperature 150 °C		841 ksi
@Thickness 0.0630 in,
Temperature 302 °F		ASTM D638
 6.15 GPa
@Thickness 1.60 mm,
Temperature 120 °C		892 ksi
@Thickness 0.0630 in,
Temperature 248 °F		ASTM D638
 10.5 GPa
@Thickness 3.17 mm,
Temperature 23.0 °C		1520 ksi
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D638
 11.6 GPa
@Thickness 3.17 mm,
Temperature -40.0 °C		1680 ksi
@Thickness 0.125 in,
Temperature -40.0 °F		ASTM D638
 11.6 GPa
@Thickness 1.60 mm,
Temperature 23.0 °C		1680 ksi
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D638
 16.5 GPa
@Thickness 1.60 mm,
Temperature -40.0 °C		2390 ksi
@Thickness 0.0630 in,
Temperature -40.0 °F		ASTM D638
Flexural Strength 145 MPa
@Temperature 23.0 °C		21000 psi
@Temperature 73.4 °F		ISO 178
 42.0 MPa
@Thickness 3.17 mm,
Temperature 150 °C		6090 psi
@Thickness 0.125 in,
Temperature 302 °F		ASTM D790
 50.0 MPa
@Thickness 0.800 mm,
Temperature 150 °C		7250 psi
@Thickness 0.0315 in,
Temperature 302 °F		ASTM D790
 51.0 MPa
@Thickness 3.17 mm,
Temperature 120 °C		7400 psi
@Thickness 0.125 in,
Temperature 248 °F		ASTM D790
 60.0 MPa
@Thickness 0.800 mm,
Temperature 120 °C		8700 psi
@Thickness 0.0315 in,
Temperature 248 °F		ASTM D790
 125 MPa
@Thickness 3.17 mm,
Temperature 23.0 °C		18100 psi
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D790
 158 MPa
@Thickness 0.800 mm,
Temperature 23.0 °C		22900 psi
@Thickness 0.0315 in,
Temperature 73.4 °F		ASTM D790
 192 MPa
@Thickness 3.17 mm,
Temperature -40.0 °C		27800 psi
@Thickness 0.125 in,
Temperature -40.0 °F		ASTM D790
 260 MPa
@Thickness 0.800 mm,
Temperature -40.0 °C		37700 psi
@Thickness 0.0315 in,
Temperature -40.0 °F		ASTM D790
Flexural Modulus 8.00 GPa
@Temperature 23.0 °C		1160 ksi
@Temperature 73.4 °F		ISO 178
 3.30 GPa
@Thickness 3.17 mm,
Temperature 150 °C		479 ksi
@Thickness 0.125 in,
Temperature 302 °F		ASTM D790
 3.40 GPa
@Thickness 3.17 mm,
Temperature 120 °C		493 ksi
@Thickness 0.125 in,
Temperature 248 °F		ASTM D790
 5.00 GPa
@Thickness 0.800 mm,
Temperature 150 °C		725 ksi
@Thickness 0.0315 in,
Temperature 302 °F		ASTM D790
 5.16 GPa
@Thickness 0.800 mm,
Temperature 120 °C		748 ksi
@Thickness 0.0315 in,
Temperature 248 °F		ASTM D790
 9.60 GPa
@Thickness 3.17 mm,
Temperature 23.0 °C		1390 ksi
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D790
 10.7 GPa
@Thickness 3.17 mm,
Temperature -40.0 °C		1550 ksi
@Thickness 0.125 in,
Temperature -40.0 °F		ASTM D790
 13.9 GPa
@Thickness 0.800 mm,
Temperature 23.0 °C		2020 ksi
@Thickness 0.0315 in,
Temperature 73.4 °F		ASTM D790
 16.7 GPa
@Thickness 0.800 mm,
Temperature -40.0 °C		2420 ksi
@Thickness 0.0315 in,
Temperature -40.0 °F		ASTM D790
Izod Impact, Notched 1.60 J/cm
@Temperature 23.0 °C		3.00 ft-lb/in
@Temperature 73.4 °F		ASTM D 256
Charpy Impact Unnotched  4.00 J/cm²
@Temperature -30.0 °C		19.0 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 6.00 J/cm²
@Temperature 23.0 °C		28.6 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  0.700 J/cm²
@Temperature -30.0 °C		3.33 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 0.900 J/cm²
@Temperature 23.0 °C		4.28 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+15 ohm-cm>= 1.00e+15 ohm-cmIEC 60093
 1.00e+16 ohm-cm1.00e+16 ohm-cmIEC 60093
 >= 1.00e+16 ohm-cm>= 1.00e+16 ohm-cmASTM D 257
Surface Resistance >= 1.00e+15 ohm>= 1.00e+15 ohmIEC 60093
 1.00e+16 ohm1.00e+16 ohmIEC 60093
 >= 1.00e+16 ohm>= 1.00e+16 ohmASTM D 257
Dielectric Constant 3.8
@Frequency 100 Hz		3.8
@Frequency 100 Hz		IEC 60250
 2.9
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		2.9
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 150
 3.2
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.2
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 3.3
@Frequency 1000 Hz,
Temperature 23.0 °C		3.3
@Frequency 1000 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 150
 3.3
@Frequency 100 Hz,
Temperature 23.0 °C		3.3
@Frequency 100 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 150
 3.4
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.4
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 3.6
@Frequency 100 Hz,
Temperature 23.0 °C		3.6
@Frequency 100 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 3.6
@Frequency 1000 Hz,
Temperature 23.0 °C		3.6
@Frequency 1000 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 3.9
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		3.9
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		1.6mm (0.062in); ASTM D 2520 B
 3.9
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		3.9
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 2520 B
 3.9
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		3.9
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 2520 B
 4.0
@Frequency 1.00e+10 Hz,
Temperature 23.0 °C		4.0
@Frequency 1.00e+10 Hz,
Temperature 73.4 °F		1.6mm (0.062in); ASTM D 2520 B
 4.0
@Frequency 1.00e+10 Hz,
Temperature 150 °C		4.0
@Frequency 1.00e+10 Hz,
Temperature 302 °F		1.6mm (0.062in); ASTM D 2520 B
 4.0
@Frequency 1.00e+10 Hz,
Temperature 120 °C		4.0
@Frequency 1.00e+10 Hz,
Temperature 248 °F		1.6mm (0.062in); ASTM D 2520 B
 4.0
@Frequency 1.00e+9 Hz,
Temperature 120 °C		4.0
@Frequency 1.00e+9 Hz,
Temperature 248 °F		1.6mm (0.062in); ASTM D 2520 B
 4.0
@Frequency 1.00e+9 Hz,
Temperature 120 °C		4.0
@Frequency 1.00e+9 Hz,
Temperature 248 °F		0.8mm (0.031in); ASTM D 2520 B
 4.0
@Frequency 1.00e+9 Hz,
Temperature 120 °C		4.0
@Frequency 1.00e+9 Hz,
Temperature 248 °F		3.2mm (0.125in); ASTM D 2520 B
 4.0
@Frequency 1.00e+9 Hz,
Temperature 150 °C		4.0
@Frequency 1.00e+9 Hz,
Temperature 302 °F		0.8mm (0.031in); ASTM D 2520 B
 4.0
@Frequency 1.00e+9 Hz,
Temperature 150 °C		4.0
@Frequency 1.00e+9 Hz,
Temperature 302 °F		1.6mm (0.062in); ASTM D 2520 B
 4.0
@Frequency 1.00e+9 Hz,
Temperature 150 °C		4.0
@Frequency 1.00e+9 Hz,
Temperature 302 °F		3.2mm (0.125in); ASTM D 2520 B
 4.0
@Frequency 1.00e+10 Hz,
Temperature 200 °C		4.0
@Frequency 1.00e+10 Hz,
Temperature 392 °F		1.6mm (0.062in); ASTM D 2520 B
 4.1
@Frequency 1.00e+10 Hz,
Temperature 200 °C		4.1
@Frequency 1.00e+10 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 2520 B
 4.1
@Frequency 1.00e+10 Hz,
Temperature 120 °C		4.1
@Frequency 1.00e+10 Hz,
Temperature 248 °F		3.2mm (0.125in); ASTM D 2520 B
 4.1
@Frequency 1.00e+9 Hz,
Temperature 200 °C		4.1
@Frequency 1.00e+9 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 2520 B
 4.1
@Frequency 1.00e+10 Hz,
Temperature 150 °C		4.1
@Frequency 1.00e+10 Hz,
Temperature 302 °F		0.8mm (0.031in); ASTM D 2520 B
 4.1
@Frequency 1.00e+9 Hz,
Temperature 200 °C		4.1
@Frequency 1.00e+9 Hz,
Temperature 392 °F		1.6mm (0.062in); ASTM D 2520 B
 4.1
@Frequency 1.00e+10 Hz,
Temperature 150 °C		4.1
@Frequency 1.00e+10 Hz,
Temperature 302 °F		3.2mm (0.125in); ASTM D 2520 B
 4.1
@Frequency 1.00e+10 Hz,
Temperature 120 °C		4.1
@Frequency 1.00e+10 Hz,
Temperature 248 °F		0.8mm (0.031in); ASTM D 2520 B
 4.1
@Frequency 1.00e+10 Hz,
Temperature 23.0 °C		4.1
@Frequency 1.00e+10 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 2520 B
 4.1
@Frequency 1.00e+10 Hz,
Temperature 23.0 °C		4.1
@Frequency 1.00e+10 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 2520 B
 4.1
@Frequency 1.00e+10 Hz,
Temperature 200 °C		4.1
@Frequency 1.00e+10 Hz,
Temperature 392 °F		0.8mm (0.031in); ASTM D 2520 B
 4.2
@Frequency 1.00e+9 Hz,
Temperature 250 °C		4.2
@Frequency 1.00e+9 Hz,
Temperature 482 °F		3.2mm (0.125in); ASTM D 2520 B
 4.2
@Frequency 1.00e+9 Hz,
Temperature 200 °C		4.2
@Frequency 1.00e+9 Hz,
Temperature 392 °F		0.8mm (0.031in); ASTM D 2520 B
Dielectric Strength  26.0 kV/mm
@Thickness 2.00 mm		660 kV/in
@Thickness 0.0787 in		IEC 60243-1
 35.0 kV/mm
@Thickness 1.00 mm		889 kV/in
@Thickness 0.0394 in		IEC 60243-1
 26.0 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		660 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		Short time; ASTM D149
 41.0 kV/mm
@Thickness 1.60 mm,
Temperature 23.0 °C		1040 kV/in
@Thickness 0.0630 in,
Temperature 73.4 °F		Short time; ASTM D149
 49.0 kV/mm
@Thickness 0.800 mm,
Temperature 23.0 °C		1240 kV/in
@Thickness 0.0315 in,
Temperature 73.4 °F		Short time; ASTM D149
Dissipation Factor  0.0010
@Frequency 1.00e+10 Hz,
Temperature 23.0 °C		0.0010
@Frequency 1.00e+10 Hz,
Temperature 73.4 °F		1.6mm (0.062in); ASTM D 2520 B
 0.0010
@Frequency 1.00e+10 Hz,
Temperature 23.0 °C		0.0010
@Frequency 1.00e+10 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 2520 B
 0.0010
@Frequency 1.00e+10 Hz,
Temperature 23.0 °C		0.0010
@Frequency 1.00e+10 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 2520 B
 0.0020
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		0.0020
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		1.6mm (0.062in); ASTM D 2520 B
 0.0020
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		0.0020
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 2520 B
 0.0020
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		0.0020
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 2520 B
 0.0050
@Frequency 1.00e+10 Hz,
Temperature 120 °C		0.0050
@Frequency 1.00e+10 Hz,
Temperature 248 °F		0.8mm (0.031in); ASTM D 2520 B
 0.0060
@Frequency 1.00e+10 Hz,
Temperature 120 °C		0.0060
@Frequency 1.00e+10 Hz,
Temperature 248 °F		1.6mm (0.062in); ASTM D 2520 B
 0.0060
@Frequency 1.00e+10 Hz,
Temperature 120 °C		0.0060
@Frequency 1.00e+10 Hz,
Temperature 248 °F		3.2mm (0.125in); ASTM D 2520 B
 0.0080
@Frequency 100 Hz,
Temperature 23.0 °C		0.0080
@Frequency 100 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 0.0090
@Frequency 100 Hz,
Temperature 23.0 °C		0.0090
@Frequency 100 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 150
 0.0090
@Frequency 1.00e+10 Hz,
Temperature 150 °C		0.0090
@Frequency 1.00e+10 Hz,
Temperature 302 °F		3.2mm (0.125in); ASTM D 2520 B
 0.0090
@Frequency 1.00e+10 Hz,
Temperature 150 °C		0.0090
@Frequency 1.00e+10 Hz,
Temperature 302 °F		0.8mm (0.031in); ASTM D 2520 B
 0.0090
@Frequency 1.00e+10 Hz,
Temperature 150 °C		0.0090
@Frequency 1.00e+10 Hz,
Temperature 302 °F		1.6mm (0.062in); ASTM D 2520 B
 0.012
@Frequency 1.00e+9 Hz,
Temperature 120 °C		0.012
@Frequency 1.00e+9 Hz,
Temperature 248 °F		0.8mm (0.031in); ASTM D 2520 B
 0.013
@Frequency 1000 Hz,
Temperature 23.0 °C		0.013
@Frequency 1000 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 150
 0.013
@Frequency 1000 Hz,
Temperature 23.0 °C		0.013
@Frequency 1000 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 0.014
@Frequency 100 Hz,
Temperature 23.0 °C		0.014
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.014
@Frequency 1.00e+9 Hz,
Temperature 120 °C		0.014
@Frequency 1.00e+9 Hz,
Temperature 248 °F		1.6mm (0.062in); ASTM D 2520 B
 0.014
@Frequency 1.00e+9 Hz,
Temperature 120 °C		0.014
@Frequency 1.00e+9 Hz,
Temperature 248 °F		3.2mm (0.125in); ASTM D 2520 B
 0.015
@Frequency 1.00e+10 Hz,
Temperature 200 °C		0.015
@Frequency 1.00e+10 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 2520 B
 0.017
@Frequency 1.00e+10 Hz,
Temperature 200 °C		0.017
@Frequency 1.00e+10 Hz,
Temperature 392 °F		0.8mm (0.031in); ASTM D 2520 B
 0.018
@Frequency 1.00e+10 Hz,
Temperature 200 °C		0.018
@Frequency 1.00e+10 Hz,
Temperature 392 °F		1.6mm (0.062in); ASTM D 2520 B
 0.018
@Frequency 1.00e+9 Hz,
Temperature 150 °C		0.018
@Frequency 1.00e+9 Hz,
Temperature 302 °F		0.8mm (0.031in); ASTM D 2520 B
 0.020
@Frequency 1.00e+9 Hz,
Temperature 150 °C		0.020
@Frequency 1.00e+9 Hz,
Temperature 302 °F		3.2mm (0.125in); ASTM D 2520 B
 0.026
@Frequency 1.00e+9 Hz,
Temperature 250 °C		0.026
@Frequency 1.00e+9 Hz,
Temperature 482 °F		3.2mm (0.125in); ASTM D 2520 B
 0.027
@Frequency 1.00e+9 Hz,
Temperature 200 °C		0.027
@Frequency 1.00e+9 Hz,
Temperature 392 °F		0.8mm (0.031in); ASTM D 2520 B
 0.028
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.028
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 0.029
@Frequency 1.00e+9 Hz,
Temperature 200 °C		0.029
@Frequency 1.00e+9 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 2520 B
 0.029
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.029
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 150
 0.031
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.031
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
Comparative Tracking Index 200 V200 VIEC 60112
 175 - 249 V175 - 249 VUL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear 8.00 µm/m-°C
@Temperature 23.0 - 150 °C		4.44 µin/in-°F
@Temperature 73.4 - 302 °F		ASTM E 228
 -4.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 160 - 260 °C		-2.22 µin/in-°F
@Thickness 0.0787 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 2.00 mm,
Temperature -40.0 - 260 °C		1.67 µin/in-°F
@Thickness 0.0787 in,
Temperature -40.0 - 500 °F		ISO 11359-1/-2
 4.00 µm/m-°C
@Thickness 2.00 mm,
Temperature -40.0 - 23.0 °C		2.22 µin/in-°F
@Thickness 0.0787 in,
Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 5.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		2.78 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 5.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 55.0 - 160 °C		2.78 µin/in-°F
@Thickness 0.0787 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 7.00 µm/m-°C
@Thickness 4.00 mm,
Temperature -40.0 - 23.0 °C		3.89 µin/in-°F
@Thickness 0.157 in,
Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 8.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C		4.44 µin/in-°F
@Thickness 0.157 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 10.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 55.0 - 160 °C		5.56 µin/in-°F
@Thickness 0.157 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 10.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 160 - 260 °C		5.56 µin/in-°F
@Thickness 0.157 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 10.0 µm/m-°C
@Thickness 4.00 mm,
Temperature -40.0 - 260 °C		5.56 µin/in-°F
@Thickness 0.157 in,
Temperature -40.0 - 500 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  22.0 µm/m-°C
@Temperature 23.0 - 150 °C		12.2 µin/in-°F
@Temperature 73.4 - 302 °F		ASTM E 228
 34.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		18.9 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2; 2mm
 34.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		18.9 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2; 4mm
 37.0 µm/m-°C
@Temperature -40.0 - 260 °C		20.6 µin/in-°F
@Temperature -40.0 - 500 °F		ISO 11359-1/-2; 2mm
 50.0 µm/m-°C
@Temperature -40.0 - 260 °C		27.8 µin/in-°F
@Temperature -40.0 - 500 °F		ISO 11359-1/-2; 4mm
 38.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C		21.1 µin/in-°F
@Thickness 0.157 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 40.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		22.2 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 44.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 55.0 - 160 °C		24.4 µin/in-°F
@Thickness 0.0787 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 46.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 160 - 260 °C		25.6 µin/in-°F
@Thickness 0.0787 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 51.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 55.0 - 160 °C		28.3 µin/in-°F
@Thickness 0.157 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 62.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 160 - 260 °C		34.4 µin/in-°F
@Thickness 0.157 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
Melting Point 335 °C635 °F10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 275 °C527 °FISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 239 °C462 °FASTM D 648
 245 °C473 °FISO 75-1/-2
Glass Transition Temp, Tg 120 °C248 °F10°C/min; ISO 11357-1/-2
 120 °C248 °FASTM D 3418
UL RTI, Electrical  240 °C
@Thickness 1.50 mm		464 °F
@Thickness 0.0591 in		UL 746B
 240 °C
@Thickness 3.00 mm		464 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical with Impact  220 °C
@Thickness 1.50 mm		428 °F
@Thickness 0.0591 in		UL 746B
 220 °C
@Thickness 3.00 mm		428 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical without Impact  240 °C
@Thickness 1.50 mm		464 °F
@Thickness 0.0591 in		UL 746B
 240 °C
@Thickness 3.00 mm		464 °F
@Thickness 0.118 in		UL 746B
Flammability, UL94  V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		IEC 60695-11-10
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		UL94
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		UL94
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		IEC 60695-11-10
Oxygen Index 47 %47 %ISO 4589-1/-2
Glow Wire Test  850 °C
@Thickness 2.00 mm		1560 °F
@Thickness 0.0787 in		Glow Wire Ignition Temperature; IEC 60695-2-13
 875 °C
@Thickness 3.00 mm		1610 °F
@Thickness 0.118 in		Glow Wire Ignition Temperature; IEC 60695-2-13
 960 °C
@Thickness 2.00 mm		1760 °F
@Thickness 0.0787 in		Glow Wire Flammability Index; IEC 60695-2-12
 960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		Glow Wire Flammability Index; IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 355 °C671 °FOptimum
 350 - 360 °C662 - 680 °F
Mold Temperature 80.0 °C176 °FOptimum
 40.0 - 150 °C104 - 302 °F
Drying Temperature 150 °C302 °F
Dry Time 3 hour3 hourDehumidified Dryer
Moisture Content <= 0.010 %<= 0.010 %
 
Descriptive Properties
ColorBlack
Drying RecommendedYes
FeaturesAppearance, Pleasing Surface
 Arc Resistant
 Aromatic
 Chemical Resistance, Good
 Dimensional Stability, Good
 Flow, Good
 Heat Aging Resistance, Good
 Moisture Absorption, Low
 Platable
 Warpage, Low
FillerMineral filler
Flame Retardant - Halogen/Red Phosphorus FreeYes
FormsPellets
GenericLCP
Mineral FillerYes
Part Marking Code>LCP-MD30<ISO 11469
Polymer FamilyLCP
Polymer TypeLCP
ProcessingInjection Moldable
Processing MethodInjection Molding
Product CategoryElectrical Resins
 Flame Retardant Resins
 Low Warp Resins
 Mineral Reinforced Resins
Region AvailableAmericas
 Asia/Pacific
 Europe
Resin IdentificationLCP-MD30ISO 1043
UsesAutomotive Applications
 Automotive Electronics
 Automotive, Under the Hood
 Communication Applications
 Computer Components
 Connectors
 Electrical/Electronic Applications
 Parts, Engineering
 Parts, Thin-walled
 Printer Parts

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31760.html

免责声明: 本文 Celanese Zenite® 6330 BK010 LCP 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4