Cool Polymers Coolpoly® D5506 Thermally Conductive Liquid Crystalline Polymer

Cool Polymers Coolpoly® D5506 Thermally Conductive Liquid Crystalline Polymer 物性表: Cool Polymers Coolpoly® D5506 Thermally Conductive Liquid Crystalline Polymer物性表及特性介绍,Cool Polymers Coolpoly® D5506 Thermally Conductive Liquid Crystalline Polymer注塑参数详情,如需Cool Polymers Coolpoly® D5506 Thermally Conductive Liquid Crystalline Polymer下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.8
  • 弯曲强度 [MPa]: 55.0
  • 弯曲模量 [MPa]: 12.7
  • 热变形温度 [℃]: 300.0
 
Physical PropertiesMetricEnglishComments
Density 1.80 g/cc0.0650 lb/in³ISO 1183
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm0.0010 - 0.0030 in/inASTM D551
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Ultimate 55.0 MPa7980 psiISO 527-1
Elongation at Break 0.76 %0.76 %ISO 527-1
Tensile Modulus 10.7 GPa1550 ksiISO 527-1
Flexural Strength 84.0 MPa12200 psiISO 178
Flexural Modulus 12.7 GPa1840 ksiISO 178
Charpy Impact Unnotched 0.560 J/cm²2.67 ft-lb/in²ISO 179-1
Charpy Impact, Notched 0.280 J/cm²1.33 ft-lb/in²ISO 179-1
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.60e+16 ohm-cm1.60e+16 ohm-cmASTM D257
Surface Resistivity per Square 2.00e+14 ohm2.00e+14 ohmASTM D257
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 6.40 µm/m-°C
@Temperature 20.0 °C
3.56 µin/in-°F
@Temperature 68.0 °F
ASTM E831-03
CTE, linear, Transverse to Flow 11.3 µm/m-°C
@Temperature 20.0 °C
6.28 µin/in-°F
@Temperature 68.0 °F
ASTM E831-03
Specific Heat Capacity 0.970 J/g-°C0.232 BTU/lb-°FASTM E1461
Thermal Conductivity 10.0 W/m-K69.4 BTU-in/hr-ft²-°FASTM E1461
Deflection Temperature at 0.46 MPa (66 psi) >= 300 °C>= 572 °FISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 264 °C507 °FISO 75-1/-2
 
Processing PropertiesMetricEnglishComments
Rear Barrel Temperature 330 - 360 °C626 - 680 °F
Middle Barrel Temperature 340 - 370 °C644 - 698 °F
Front Barrel Temperature 345 - 380 °C653 - 716 °F
Nozzle Temperature 350 - 382 °C662 - 720 °F
Melt Temperature 349 - 393 °C660 - 739 °F
Mold Temperature 93.0 - 177 °C199 - 351 °F
Drying Temperature 180 °C356 °F
Dry Time 2 - 4 hour2 - 4 hour
Moisture Content 0.010 %0.010 %
Dew Point -34.0 °C-29.2 °F
Injection Pressure 35.0 - 70.0 MPa5080 - 10200 psi
Hold Pressure 7.00 - 35.0 MPa1020 - 5080 psi
Back Pressure 0.000 - 0.350 MPa0.000 - 50.8 psi
Screw Speed 75 - 150 rpm75 - 150 rpm

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31758.html

免责声明: 本文 Cool Polymers Coolpoly® D5506 Thermally Conductive Liquid Crystalline Polymer 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4