- 密度 [g/cm3]: 1.68
- 吸水率 [%]: 0.08
- 缺口冲击强度: 1.1
- 弯曲强度 [MPa]: 14.0
- 弯曲模量 [MPa]: 11.0
- 硬度: 108.0
- 热变形温度 [℃]: 275.0
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.67 g/cc | 1.67 g/cc | ASTM D 792 | ||
Density | 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 | ||
Filler Content | 30 % | 30 % | |||
Moisture Absorption | 0.00200 % @Thickness 3.17 mm | 0.00200 % @Thickness 0.125 in | 50%RH,23°C,24h; ASTM D570 | ||
Water Absorption at Saturation | 0.080 % @Thickness 3.20 mm | 0.080 % @Thickness 0.126 in | Water, tap 23°C,10000h; ASTM D570 | ||
Linear Mold Shrinkage, Flow | -0.000700 cm/cm @Thickness 0.787 mm | -0.000700 in/in @Thickness 0.0310 in | ASTM D955 | ||
-0.000700 cm/cm @Thickness 15.7 mm | -0.000700 in/in @Thickness 0.620 in | ASTM D955 | |||
-0.000700 cm/cm @Thickness 3.17 mm | -0.000700 in/in @Thickness 0.125 in | ASTM D955 | |||
Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Thickness 0.800 mm | 0.0050 in/in @Thickness 0.0315 in | ASTM D955 | ||
0.0050 cm/cm @Thickness 3.17 mm | 0.0050 in/in @Thickness 0.125 in | ASTM D955 | |||
0.0080 cm/cm @Thickness 1.60 mm | 0.0080 in/in @Thickness 0.0630 in | ASTM D955 | |||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Rockwell M | 61 | 61 | ASTM D 785 | ||
Hardness, Rockwell R | 108 | 108 | ASTM D 785 | ||
Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 | ||
Tensile Strength, Ultimate | 14.0 MPa @Thickness 3.17 mm, Temperature 250 °C | 2030 psi @Thickness 0.125 in, Temperature 482 °F | ASTM D638 | ||
21.0 MPa @Thickness 0.800 mm, Temperature 250 °C | 3050 psi @Thickness 0.0315 in, Temperature 482 °F | ASTM D638 | |||
22.0 MPa @Thickness 0.800 mm, Temperature 200 °C | 3190 psi @Thickness 0.0315 in, Temperature 392 °F | ASTM D638 | |||
35.0 MPa @Thickness 3.17 mm, Temperature 200 °C | 5080 psi @Thickness 0.125 in, Temperature 392 °F | ASTM D638 | |||
50.0 MPa @Thickness 3.17 mm, Temperature 150 °C | 7250 psi @Thickness 0.125 in, Temperature 302 °F | ASTM D638 | |||
55.0 MPa @Thickness 0.800 mm, Temperature 150 °C | 7980 psi @Thickness 0.0315 in, Temperature 302 °F | ASTM D638 | |||
60.0 MPa @Thickness 3.17 mm, Temperature 120 °C | 8700 psi @Thickness 0.125 in, Temperature 248 °F | ASTM D638 | |||
82.0 MPa @Thickness 0.800 mm, Temperature 120 °C | 11900 psi @Thickness 0.0315 in, Temperature 248 °F | ASTM D638 | |||
125 MPa @Thickness 3.17 mm, Temperature 23.0 °C | 18100 psi @Thickness 0.125 in, Temperature 73.4 °F | ASTM D638 | |||
165 MPa @Thickness 0.800 mm, Temperature 23.0 °C | 23900 psi @Thickness 0.0315 in, Temperature 73.4 °F | ASTM D638 | |||
185 MPa @Thickness 3.17 mm, Temperature -40.0 °C | 26800 psi @Thickness 0.125 in, Temperature -40.0 °F | ASTM D638 | |||
250 MPa @Thickness 0.800 mm, Temperature -40.0 °C | 36300 psi @Thickness 0.0315 in, Temperature -40.0 °F | ASTM D638 | |||
Elongation at Break | 2.2 % | 2.2 % | ISO 527 | ||
2.7 % @Temperature 23.0 °C | 2.7 % @Temperature 73.4 °F | ASTM D 638 | |||
Tensile Modulus | 13.5 GPa @Temperature 23.0 °C | 1960 ksi @Temperature 73.4 °F | ISO 527 | ||
3.40 GPa @Thickness 1.60 mm, Temperature 250 °C | 493 ksi @Thickness 0.0630 in, Temperature 482 °F | ASTM D638 | |||
4.00 GPa @Thickness 3.17 mm, Temperature 250 °C | 580 ksi @Thickness 0.125 in, Temperature 482 °F | ASTM D638 | |||
4.80 GPa @Thickness 1.60 mm, Temperature 200 °C | 696 ksi @Thickness 0.0630 in, Temperature 392 °F | ASTM D638 | |||
6.70 GPa @Thickness 1.60 mm, Temperature 150 °C | 972 ksi @Thickness 0.0630 in, Temperature 302 °F | ASTM D638 | |||
8.30 GPa @Thickness 1.60 mm, Temperature 120 °C | 1200 ksi @Thickness 0.0630 in, Temperature 248 °F | ASTM D638 | |||
10.0 GPa @Thickness 3.17 mm, Temperature 200 °C | 1450 ksi @Thickness 0.125 in, Temperature 392 °F | ASTM D638 | |||
12.0 GPa @Thickness 3.17 mm, Temperature 120 °C | 1740 ksi @Thickness 0.125 in, Temperature 248 °F | ASTM D638 | |||
12.0 GPa @Thickness 3.17 mm, Temperature 150 °C | 1740 ksi @Thickness 0.125 in, Temperature 302 °F | ASTM D638 | |||
14.0 GPa @Thickness 3.17 mm, Temperature 23.0 °C | 2030 ksi @Thickness 0.125 in, Temperature 73.4 °F | ASTM D638 | |||
15.0 GPa @Thickness 1.60 mm, Temperature 23.0 °C | 2180 ksi @Thickness 0.0630 in, Temperature 73.4 °F | ASTM D638 | |||
20.0 GPa @Thickness 1.60 mm, Temperature -40.0 °C | 2900 ksi @Thickness 0.0630 in, Temperature -40.0 °F | ASTM D638 | |||
29.0 GPa @Thickness 3.17 mm, Temperature -40.0 °C | 4210 ksi @Thickness 0.125 in, Temperature -40.0 °F | ASTM D638 | |||
Flexural Strength | 190 MPa @Temperature 23.0 °C | 27600 psi @Temperature 73.4 °F | ISO 178 | ||
17.0 MPa @Thickness 3.17 mm, Temperature 250 °C | 2470 psi @Thickness 0.125 in, Temperature 482 °F | ASTM D790 | |||
22.0 MPa @Thickness 1.60 mm, Temperature 250 °C | 3190 psi @Thickness 0.0630 in, Temperature 482 °F | ASTM D790 | |||
23.0 MPa @Thickness 0.800 mm, Temperature 250 °C | 3340 psi @Thickness 0.0315 in, Temperature 482 °F | ASTM D790 | |||
33.0 MPa @Thickness 3.17 mm, Temperature 200 °C | 4790 psi @Thickness 0.125 in, Temperature 392 °F | ASTM D790 | |||
45.0 MPa @Thickness 1.60 mm, Temperature 200 °C | 6530 psi @Thickness 0.0630 in, Temperature 392 °F | ASTM D790 | |||
50.0 MPa @Thickness 0.800 mm, Temperature 200 °C | 7250 psi @Thickness 0.0315 in, Temperature 392 °F | ASTM D790 | |||
50.0 MPa @Thickness 3.17 mm, Temperature 150 °C | 7250 psi @Thickness 0.125 in, Temperature 302 °F | ASTM D790 | |||
62.0 MPa @Thickness 3.17 mm, Temperature 120 °C | 8990 psi @Thickness 0.125 in, Temperature 248 °F | ASTM D790 | |||
64.0 MPa @Thickness 1.60 mm, Temperature 150 °C | 9280 psi @Thickness 0.0630 in, Temperature 302 °F | ASTM D790 | |||
70.0 MPa @Thickness 0.800 mm, Temperature 150 °C | 10200 psi @Thickness 0.0315 in, Temperature 302 °F | ASTM D790 | |||
80.0 MPa @Thickness 1.60 mm, Temperature 120 °C | 11600 psi @Thickness 0.0630 in, Temperature 248 °F | ASTM D790 | |||
90.0 MPa @Thickness 0.800 mm, Temperature 120 °C | 13100 psi @Thickness 0.0315 in, Temperature 248 °F | ASTM D790 | |||
170 MPa @Thickness 3.17 mm, Temperature 23.0 °C | 24700 psi @Thickness 0.125 in, Temperature 73.4 °F | ASTM D790 | |||
195 MPa @Thickness 1.60 mm, Temperature 23.0 °C | 28300 psi @Thickness 0.0630 in, Temperature 73.4 °F | ASTM D790 | |||
195 MPa @Thickness 0.800 mm, Temperature 23.0 °C | 28300 psi @Thickness 0.0315 in, Temperature 73.4 °F | ASTM D790 | |||
245 MPa @Thickness 3.17 mm, Temperature -40.0 °C | 35500 psi @Thickness 0.125 in, Temperature -40.0 °F | ASTM D790 | |||
295 MPa @Thickness 1.60 mm, Temperature -40.0 °C | 42800 psi @Thickness 0.0630 in, Temperature -40.0 °F | ASTM D790 | |||
340 MPa @Thickness 0.800 mm, Temperature -40.0 °C | 49300 psi @Thickness 0.0315 in, Temperature -40.0 °F | ASTM D790 | |||
Flexural Modulus | 11.0 GPa @Temperature 23.0 °C | 1600 ksi @Temperature 73.4 °F | ISO 178 | ||
2.80 GPa @Thickness 3.17 mm, Temperature 250 °C | 406 ksi @Thickness 0.125 in, Temperature 482 °F | ASTM D790 | |||
3.40 GPa @Thickness 1.60 mm, Temperature 250 °C | 493 ksi @Thickness 0.0630 in, Temperature 482 °F | ASTM D790 | |||
4.10 GPa @Thickness 0.800 mm, Temperature 250 °C | 595 ksi @Thickness 0.0315 in, Temperature 482 °F | ASTM D790 | |||
4.80 GPa @Thickness 3.17 mm, Temperature 200 °C | 696 ksi @Thickness 0.125 in, Temperature 392 °F | ASTM D790 | |||
5.50 GPa @Thickness 3.17 mm, Temperature 150 °C | 798 ksi @Thickness 0.125 in, Temperature 302 °F | ASTM D790 | |||
6.20 GPa @Thickness 3.17 mm, Temperature 120 °C | 899 ksi @Thickness 0.125 in, Temperature 248 °F | ASTM D790 | |||
6.20 GPa @Thickness 1.60 mm, Temperature 200 °C | 899 ksi @Thickness 0.0630 in, Temperature 392 °F | ASTM D790 | |||
6.90 GPa @Thickness 0.800 mm, Temperature 200 °C | 1000 ksi @Thickness 0.0315 in, Temperature 392 °F | ASTM D790 | |||
6.90 GPa @Thickness 1.60 mm, Temperature 150 °C | 1000 ksi @Thickness 0.0630 in, Temperature 302 °F | ASTM D790 | |||
8.30 GPa @Thickness 1.60 mm, Temperature 120 °C | 1200 ksi @Thickness 0.0630 in, Temperature 248 °F | ASTM D790 | |||
9.00 GPa @Thickness 0.800 mm, Temperature 150 °C | 1310 ksi @Thickness 0.0315 in, Temperature 302 °F | ASTM D790 | |||
10.0 GPa @Thickness 0.800 mm, Temperature 120 °C | 1450 ksi @Thickness 0.0315 in, Temperature 248 °F | ASTM D790 | |||
12.0 GPa @Thickness 3.17 mm, Temperature 23.0 °C | 1740 ksi @Thickness 0.125 in, Temperature 73.4 °F | ASTM D790 | |||
15.0 GPa @Thickness 3.17 mm, Temperature -40.0 °C | 2180 ksi @Thickness 0.125 in, Temperature -40.0 °F | ASTM D790 | |||
15.0 GPa @Thickness 1.60 mm, Temperature 23.0 °C | 2180 ksi @Thickness 0.0630 in, Temperature 73.4 °F | ASTM D790 | |||
19.0 GPa @Thickness 0.800 mm, Temperature 23.0 °C | 2760 ksi @Thickness 0.0315 in, Temperature 73.4 °F | ASTM D790 | |||
19.0 GPa @Thickness 1.60 mm, Temperature -40.0 °C | 2760 ksi @Thickness 0.0630 in, Temperature -40.0 °F | ASTM D790 | |||
25.0 GPa @Thickness 0.800 mm, Temperature -40.0 °C | 3630 ksi @Thickness 0.0315 in, Temperature -40.0 °F | ASTM D790 | |||
Compressive Strength | 105 MPa | 15200 psi | ASTM D 695 | ||
Shear Strength | 51.0 MPa @Thickness 3.17 mm | 7400 psi @Thickness 0.125 in | ASTM D732 | ||
68.0 MPa @Thickness 0.800 mm | 9860 psi @Thickness 0.0315 in | ASTM D732 | |||
Izod Impact, Notched | 1.10 J/cm @Thickness 3.17 mm, Temperature -40.0 °C | 2.06 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F | ASTM D256 | ||
1.25 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 2.34 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 | |||
2.00 J/cm @Thickness 1.60 mm, Temperature 23.0 °C | 3.75 ft-lb/in @Thickness 0.0630 in, Temperature 73.4 °F | ASTM D256 | |||
2.15 J/cm @Thickness 0.800 mm, Temperature 23.0 °C | 4.03 ft-lb/in @Thickness 0.0315 in, Temperature 73.4 °F | 40%NB; ASTM D256 | |||
3.00 J/cm @Thickness 0.800 mm, Temperature -40.0 °C | 5.62 ft-lb/in @Thickness 0.0315 in, Temperature -40.0 °F | ASTM D256 | |||
Izod Impact, Unnotched | 6.55 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 12.3 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D4812 | ||
6.85 J/cm @Thickness 1.60 mm, Temperature 23.0 °C | 12.8 ft-lb/in @Thickness 0.0630 in, Temperature 73.4 °F | ASTM D4812 | |||
7.35 J/cm @Thickness 0.800 mm, Temperature -40.0 °C | 13.8 ft-lb/in @Thickness 0.0315 in, Temperature -40.0 °F | ASTM D4812 | |||
440 J/cm @Thickness 3.17 mm, Temperature -40.0 °C | 824 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F | ASTM D4812 | |||
NB @Thickness 0.800 mm, Temperature 23.0 °C | NB @Thickness 0.0315 in, Temperature 73.4 °F | ASTM D4812 | |||
Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature -40.0 °C | 9.52 ft-lb/in² @Temperature -40.0 °F | ISO 180/1A | ||
25.0 kJ/m² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
Izod Impact, Unnotched (ISO) | 30.0 kJ/m² @Temperature -30.0 °C | 14.3 ft-lb/in² @Temperature -22.0 °F | ISO 180/1U | ||
35.0 kJ/m² @Temperature 23.0 °C | 16.7 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U | |||
Charpy Impact Unnotched | 2.50 J/cm² @Temperature -30.0 °C | 11.9 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
3.50 J/cm² @Temperature 23.0 °C | 16.7 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
Charpy Impact, Notched | 2.50 J/cm² @Temperature -30.0 °C | 11.9 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
3.50 J/cm² @Temperature 23.0 °C | 16.7 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D 257 | ||
Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D 257 | ||
Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.6 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 0.8mm (0.031in); ASTM D 150 | ||
3.9 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.9 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 3.2mm (0.125in); ASTM D 150 | |||
4.0 @Frequency 1000 Hz, Temperature 23.0 °C | 4.0 @Frequency 1000 Hz, Temperature 73.4 °F | 0.8mm (0.031in); ASTM D 150 | |||
4.3 @Frequency 1.00e+6 Hz, Temperature 120 °C | 4.3 @Frequency 1.00e+6 Hz, Temperature 248 °F | 0.8mm (0.031in); ASTM D 150 | |||
4.3 @Frequency 1.00e+9 Hz, Temperature 23.0 °C | 4.3 @Frequency 1.00e+9 Hz, Temperature 73.4 °F | 1.6mm (0.062in); ASTM D 2520 B | |||
4.3 @Frequency 1.00e+9 Hz, Temperature 23.0 °C | 4.3 @Frequency 1.00e+9 Hz, Temperature 73.4 °F | 3.2mm (0.125in); ASTM D 2520 B | |||
4.4 @Frequency 1.00e+9 Hz, Temperature 150 °C | 4.4 @Frequency 1.00e+9 Hz, Temperature 302 °F | 0.8mm (0.031in); ASTM D 2520 B | |||
4.4 @Frequency 1.00e+9 Hz, Temperature 150 °C | 4.4 @Frequency 1.00e+9 Hz, Temperature 302 °F | 1.6mm (0.062in); ASTM D 2520 B | |||
4.4 @Frequency 1.00e+9 Hz, Temperature 150 °C | 4.4 @Frequency 1.00e+9 Hz, Temperature 302 °F | 3.2mm (0.125in); ASTM D 2520 B | |||
4.4 @Frequency 1.00e+9 Hz, Temperature 120 °C | 4.4 @Frequency 1.00e+9 Hz, Temperature 248 °F | 0.8mm (0.031in); ASTM D 2520 B | |||
4.4 @Frequency 1.00e+9 Hz, Temperature 120 °C | 4.4 @Frequency 1.00e+9 Hz, Temperature 248 °F | 1.6mm (0.062in); ASTM D 2520 B | |||
4.4 @Frequency 1.00e+9 Hz, Temperature 120 °C | 4.4 @Frequency 1.00e+9 Hz, Temperature 248 °F | 3.2mm (0.125in); ASTM D 2520 B | |||
4.4 @Frequency 1000 Hz, Temperature 23.0 °C | 4.4 @Frequency 1000 Hz, Temperature 73.4 °F | 3.2mm (0.125in); ASTM D 150 | |||
4.4 @Frequency 1.00e+9 Hz, Temperature 23.0 °C | 4.4 @Frequency 1.00e+9 Hz, Temperature 73.4 °F | 0.8mm (0.031in); ASTM D 2520 B | |||
4.4 @Frequency 1.00e+6 Hz, Temperature 200 °C | 4.4 @Frequency 1.00e+6 Hz, Temperature 392 °F | 0.8mm (0.031in); ASTM D 150 | |||
4.4 @Frequency 1.00e+6 Hz, Temperature 150 °C | 4.4 @Frequency 1.00e+6 Hz, Temperature 302 °F | 0.8mm (0.031in); ASTM D 150 | |||
4.5 @Frequency 1.00e+9 Hz, Temperature 200 °C | 4.5 @Frequency 1.00e+9 Hz, Temperature 392 °F | 3.2mm (0.125in); ASTM D 2520 B | |||
4.5 @Frequency 1.00e+9 Hz, Temperature 200 °C | 4.5 @Frequency 1.00e+9 Hz, Temperature 392 °F | 1.6mm (0.062in); ASTM D 2520 B | |||
4.5 @Frequency 1.00e+9 Hz, Temperature 200 °C | 4.5 @Frequency 1.00e+9 Hz, Temperature 392 °F | 0.8mm (0.031in); ASTM D 2520 B | |||
4.5 @Frequency 1000 Hz, Temperature 200 °C | 4.5 @Frequency 1000 Hz, Temperature 392 °F | 0.8mm (0.031in); ASTM D 150 | |||
4.5 @Frequency 1000 Hz, Temperature 120 °C | 4.5 @Frequency 1000 Hz, Temperature 248 °F | 0.8mm (0.031in); ASTM D 150 | |||
4.5 @Frequency 1000 Hz, Temperature 150 °C | 4.5 @Frequency 1000 Hz, Temperature 302 °F | 0.8mm (0.031in); ASTM D 150 | |||
4.8 @Frequency 1.00e+6 Hz, Temperature 150 °C | 4.8 @Frequency 1.00e+6 Hz, Temperature 302 °F | 3.2mm (0.125in); ASTM D 150 | |||
4.8 @Frequency 1.00e+9 Hz, Temperature 250 °C | 4.8 @Frequency 1.00e+9 Hz, Temperature 482 °F | 3.2mm (0.125in); ASTM D 2520 B | |||
4.8 @Frequency 1.00e+6 Hz, Temperature 120 °C | 4.8 @Frequency 1.00e+6 Hz, Temperature 248 °F | 3.2mm (0.125in); ASTM D 150 | |||
4.8 @Frequency 1.00e+9 Hz, Temperature 250 °C | 4.8 @Frequency 1.00e+9 Hz, Temperature 482 °F | 3.2mm (0.125in); ASTM D 2520 B | |||
4.8 @Frequency 1.00e+9 Hz, Temperature 250 °C | 4.8 @Frequency 1.00e+9 Hz, Temperature 482 °F | 3.2mm (0.125in); ASTM D 2520 B | |||
4.9 @Frequency 1.00e+6 Hz, Temperature 200 °C | 4.9 @Frequency 1.00e+6 Hz, Temperature 392 °F | 3.2mm (0.125in); ASTM D 150 | |||
5.0 @Frequency 1000 Hz, Temperature 200 °C | 5.0 @Frequency 1000 Hz, Temperature 392 °F | 3.2mm (0.125in); ASTM D 150 | |||
5.0 @Frequency 1000 Hz, Temperature 150 °C | 5.0 @Frequency 1000 Hz, Temperature 302 °F | 3.2mm (0.125in); ASTM D 150 | |||
5.0 @Frequency 1000 Hz, Temperature 120 °C | 5.0 @Frequency 1000 Hz, Temperature 248 °F | 3.2mm (0.125in); ASTM D 150 | |||
Dielectric Strength | 27.0 kV/mm @Thickness 3.20 mm, Temperature 150 °C | 686 kV/in @Thickness 0.126 in, Temperature 302 °F | Short time; ASTM D149 | ||
28.0 kV/mm @Thickness 3.20 mm, Temperature 120 °C | 711 kV/in @Thickness 0.126 in, Temperature 248 °F | Short time; ASTM D149 | |||
29.0 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 737 kV/in @Thickness 0.126 in, Temperature 73.4 °F | Short time; ASTM D149 | |||
31.0 kV/mm @Thickness 1.60 mm, Temperature 150 °C | 787 kV/in @Thickness 0.0630 in, Temperature 302 °F | Short time; ASTM D149 | |||
33.0 kV/mm @Thickness 1.60 mm, Temperature 120 °C | 838 kV/in @Thickness 0.0630 in, Temperature 248 °F | Short time; ASTM D149 | |||
33.0 kV/mm @Thickness 1.60 mm, Temperature 200 °C | 838 kV/in @Thickness 0.0630 in, Temperature 392 °F | Short time; ASTM D149 | |||
35.0 kV/mm @Thickness 1.60 mm, Temperature 23.0 °C | 889 kV/in @Thickness 0.0630 in, Temperature 73.4 °F | Short time; ASTM D149 | |||
37.0 kV/mm @Thickness 0.800 mm, Temperature 150 °C | 940 kV/in @Thickness 0.0315 in, Temperature 302 °F | Short time; ASTM D149 | |||
40.0 kV/mm @Thickness 0.800 mm, Temperature 200 °C | 1020 kV/in @Thickness 0.0315 in, Temperature 392 °F | Short time; ASTM D149 | |||
40.0 kV/mm @Thickness 0.800 mm, Temperature 23.0 °C | 1020 kV/in @Thickness 0.0315 in, Temperature 73.4 °F | Short time; ASTM D149 | |||
41.0 kV/mm @Thickness 0.800 mm, Temperature 120 °C | 1040 kV/in @Thickness 0.0315 in, Temperature 248 °F | Short time; ASTM D149 | |||
Dissipation Factor | 0.0040 @Frequency 1.00e+9 Hz, Temperature 23.0 °C | 0.0040 @Frequency 1.00e+9 Hz, Temperature 73.4 °F | 0.8mm (0.031in); ASTM D 2520 B | ||
0.0040 @Frequency 1.00e+9 Hz, Temperature 23.0 °C | 0.0040 @Frequency 1.00e+9 Hz, Temperature 73.4 °F | 1.6mm (0.062in); ASTM D 2520 B | |||
0.0040 @Frequency 1.00e+9 Hz, Temperature 23.0 °C | 0.0040 @Frequency 1.00e+9 Hz, Temperature 73.4 °F | 3.2mm (0.125in); ASTM D 2520 B | |||
0.0060 @Frequency 1000 Hz, Temperature 120 °C | 0.0060 @Frequency 1000 Hz, Temperature 248 °F | 3.2mm (0.125in); ASTM D 150 | |||
0.0070 @Frequency 1000 Hz, Temperature 150 °C | 0.0070 @Frequency 1000 Hz, Temperature 302 °F | 3.2mm (0.125in); ASTM D 150 | |||
0.0080 @Frequency 1000 Hz, Temperature 120 °C | 0.0080 @Frequency 1000 Hz, Temperature 248 °F | 0.8mm (0.031in); ASTM D 150 | |||
0.0090 @Frequency 1000 Hz, Temperature 150 °C | 0.0090 @Frequency 1000 Hz, Temperature 302 °F | 0.8mm (0.031in); ASTM D 150 | |||
0.0090 @Frequency 1.00e+6 Hz, Temperature 200 °C | 0.0090 @Frequency 1.00e+6 Hz, Temperature 392 °F | 3.2mm (0.125in); ASTM D 150 | |||
0.010 @Frequency 1.00e+6 Hz, Temperature 200 °C | 0.010 @Frequency 1.00e+6 Hz, Temperature 392 °F | 0.8mm (0.031in); ASTM D 150 | |||
0.012 @Frequency 1.00e+9 Hz, Temperature 120 °C | 0.012 @Frequency 1.00e+9 Hz, Temperature 248 °F | 0.8mm (0.031in); ASTM D 2520 B | |||
0.013 @Frequency 1000 Hz, Temperature 23.0 °C | 0.013 @Frequency 1000 Hz, Temperature 73.4 °F | 3.2mm (0.125in); ASTM D 150 | |||
0.013 @Frequency 1000 Hz, Temperature 23.0 °C | 0.013 @Frequency 1000 Hz, Temperature 73.4 °F | 0.8mm (0.031in); ASTM D 150 | |||
0.014 @Frequency 1000 Hz, Temperature 200 °C | 0.014 @Frequency 1000 Hz, Temperature 392 °F | 3.2mm (0.125in); ASTM D 150 | |||
0.014 @Frequency 1.00e+9 Hz, Temperature 120 °C | 0.014 @Frequency 1.00e+9 Hz, Temperature 248 °F | 1.6mm (0.062in); ASTM D 2520 B | |||
0.015 @Frequency 1000 Hz, Temperature 200 °C | 0.015 @Frequency 1000 Hz, Temperature 392 °F | 0.8mm (0.031in); ASTM D 150 | |||
0.016 @Frequency 1.00e+6 Hz, Temperature 150 °C | 0.016 @Frequency 1.00e+6 Hz, Temperature 302 °F | 0.8mm (0.031in); ASTM D 150 | |||
0.016 @Frequency 1.00e+9 Hz, Temperature 120 °C | 0.016 @Frequency 1.00e+9 Hz, Temperature 248 °F | 3.2mm (0.125in); ASTM D 2520 B | |||
0.018 @Frequency 1.00e+9 Hz, Temperature 150 °C | 0.018 @Frequency 1.00e+9 Hz, Temperature 302 °F | 0.8mm (0.031in); ASTM D 2520 B | |||
0.018 @Frequency 1.00e+6 Hz, Temperature 150 °C | 0.018 @Frequency 1.00e+6 Hz, Temperature 302 °F | 3.2mm (0.125in); ASTM D 150 | |||
0.020 @Frequency 1.00e+9 Hz, Temperature 150 °C | 0.020 @Frequency 1.00e+9 Hz, Temperature 302 °F | 1.6mm (0.062in); ASTM D 2520 B | |||
0.023 @Frequency 1.00e+9 Hz, Temperature 150 °C | 0.023 @Frequency 1.00e+9 Hz, Temperature 302 °F | 3.2mm (0.125in); ASTM D 2520 B | |||
0.025 @Frequency 1.00e+9 Hz, Temperature 200 °C | 0.025 @Frequency 1.00e+9 Hz, Temperature 392 °F | 0.8mm (0.031in); ASTM D 2520 B | |||
0.026 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.026 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 0.8mm (0.031in); ASTM D 150 | |||
0.027 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.027 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 3.2mm (0.125in); ASTM D 150 | |||
0.028 @Frequency 1.00e+9 Hz, Temperature 200 °C | 0.028 @Frequency 1.00e+9 Hz, Temperature 392 °F | 1.6mm (0.062in); ASTM D 2520 B | |||
0.032 @Frequency 1.00e+9 Hz, Temperature 200 °C | 0.032 @Frequency 1.00e+9 Hz, Temperature 392 °F | 3.2mm (0.125in); ASTM D 2520 B | |||
0.032 @Frequency 1.00e+6 Hz, Temperature 120 °C | 0.032 @Frequency 1.00e+6 Hz, Temperature 248 °F | 3.2mm (0.125in); ASTM D 150 | |||
0.034 @Frequency 1.00e+9 Hz, Temperature 250 °C | 0.034 @Frequency 1.00e+9 Hz, Temperature 482 °F | 3.2mm (0.125in); ASTM D 2520 B | |||
Comparative Tracking Index | 100 - 174 V | 100 - 174 V | UL 746A | ||
Thermal Properties | Metric | English | Comments | ||
CTE, linear | -5.00 µm/m-°C @Thickness 2.00 mm, Temperature 160 - 260 °C | -2.78 µin/in-°F @Thickness 0.0787 in, Temperature 320 - 500 °F | ISO 11359-1/-2 | ||
-2.00 µm/m-°C @Thickness 4.00 mm, Temperature 160 - 260 °C | -1.11 µin/in-°F @Thickness 0.157 in, Temperature 320 - 500 °F | ISO 11359-1/-2 | |||
1.00 µm/m-°C @Thickness 2.00 mm, Temperature -40.0 - 260 °C | 0.556 µin/in-°F @Thickness 0.0787 in, Temperature -40.0 - 500 °F | ISO 11359-1/-2 | |||
2.00 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 260 °C | 1.11 µin/in-°F @Thickness 0.157 in, Temperature -40.0 - 500 °F | ISO 11359-1/-2 | |||
2.00 µm/m-°C @Thickness 2.00 mm, Temperature -40.0 - 23.0 °C | 1.11 µin/in-°F @Thickness 0.0787 in, Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | |||
2.00 µm/m-°C @Thickness 2.00 mm, Temperature 55.0 - 160 °C | 1.11 µin/in-°F @Thickness 0.0787 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 4.00 mm, Temperature 55.0 - 160 °C | 1.67 µin/in-°F @Thickness 0.157 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 23.0 °C | 1.67 µin/in-°F @Thickness 0.157 in, Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 4.00 mm, Temperature 23.0 - 55.0 °C | 1.67 µin/in-°F @Thickness 0.157 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 1.67 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
5.00 µm/m-°C @Thickness 1.60 mm, Temperature 23.0 - 150 °C | 2.78 µin/in-°F @Thickness 0.0630 in, Temperature 73.4 - 302 °F | ASTM E 228 | |||
13.0 µm/m-°C @Thickness 3.17 mm, Temperature 23.0 - 150 °C | 7.22 µin/in-°F @Thickness 0.125 in, Temperature 73.4 - 302 °F | ASTM E 228 | |||
CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 33.3 µin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2; 2mm | ||
61.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 33.9 µin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2; 4mm | |||
85.0 µm/m-°C @Temperature -40.0 - 260 °C | 47.2 µin/in-°F @Temperature -40.0 - 500 °F | ISO 11359-1/-2; 2mm | |||
88.0 µm/m-°C @Temperature -40.0 - 260 °C | 48.9 µin/in-°F @Temperature -40.0 - 500 °F | ISO 11359-1/-2; 4mm | |||
37.0 µm/m-°C @Thickness 3.17 mm, Temperature 23.0 - 150 °C | 20.6 µin/in-°F @Thickness 0.125 in, Temperature 73.4 - 302 °F | ASTM E 228 | |||
49.0 µm/m-°C @Thickness 1.60 mm, Temperature 23.0 - 150 °C | 27.2 µin/in-°F @Thickness 0.0630 in, Temperature 73.4 - 302 °F | ASTM E 228 | |||
68.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 37.8 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
70.0 µm/m-°C @Thickness 4.00 mm, Temperature 23.0 - 55.0 °C | 38.9 µin/in-°F @Thickness 0.157 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
88.0 µm/m-°C @Thickness 2.00 mm, Temperature 55.0 - 160 °C | 48.9 µin/in-°F @Thickness 0.0787 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
92.0 µm/m-°C @Thickness 4.00 mm, Temperature 55.0 - 160 °C | 51.1 µin/in-°F @Thickness 0.157 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
101 µm/m-°C @Thickness 2.00 mm, Temperature 160 - 260 °C | 56.1 µin/in-°F @Thickness 0.0787 in, Temperature 320 - 500 °F | ISO 11359-1/-2 | |||
107 µm/m-°C @Thickness 4.00 mm, Temperature 160 - 260 °C | 59.4 µin/in-°F @Thickness 0.157 in, Temperature 320 - 500 °F | ISO 11359-1/-2 | |||
Melting Point | 335 °C | 635 °F | ASTM D 3418 | ||
335 °C | 635 °F | 10°C/min; ISO 11357-1/-3 | |||
Deflection Temperature at 0.46 MPa (66 psi) | 275 °C | 527 °F | ASTM D 648 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | ASTM D 648 | ||
268 °C | 514 °F | ISO 75-1/-2 | |||
Glass Transition Temp, Tg | 120 °C | 248 °F | ASTM D 3418 | ||
UL RTI, Electrical | 240 °C @Thickness 0.750 mm | 464 °F @Thickness 0.0295 in | UL 746B | ||
240 °C @Thickness 1.50 mm | 464 °F @Thickness 0.0591 in | UL 746B | |||
240 °C @Thickness 3.00 mm | 464 °F @Thickness 0.118 in | UL 746B | |||
UL RTI, Mechanical with Impact | 220 °C @Thickness 0.750 mm | 428 °F @Thickness 0.0295 in | UL 746B | ||
220 °C @Thickness 1.50 mm | 428 °F @Thickness 0.0591 in | UL 746B | |||
220 °C @Thickness 3.00 mm | 428 °F @Thickness 0.118 in | UL 746B | |||
UL RTI, Mechanical without Impact | 240 °C @Thickness 1.50 mm | 464 °F @Thickness 0.0591 in | UL 746B | ||
240 °C @Thickness 0.750 mm | 464 °F @Thickness 0.0295 in | UL 746B | |||
240 °C @Thickness 3.00 mm | 464 °F @Thickness 0.118 in | UL 746B | |||
Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | ||
V-0 @Thickness 0.380 mm | V-0 @Thickness 0.0150 in | IEC 60695-11-10 | |||
V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | IEC 60695-11-10 | |||
V-0 @Thickness 0.380 mm | V-0 @Thickness 0.0150 in | UL94 | |||
V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | UL94 | |||
V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | |||
V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | IEC 60695-11-10 | |||
V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL94 | |||
Oxygen Index | 38 % @Thickness 3.17 mm | 38 % @Thickness 0.125 in | ASTM D2863 | ||
Processing Properties | Metric | English | Comments | ||
Melt Temperature | 355 °C | 671 °F | Optimum | ||
350 - 360 °C | 662 - 680 °F | ||||
Mold Temperature | 80.0 °C | 176 °F | Optimum | ||
40.0 - 150 °C | 104 - 302 °F | ||||
Drying Temperature | 150 °C | 302 °F | |||
Dry Time | 3 hour | 3 hour | Dehumidified Dryer | ||
Moisture Content | <= 0.010 % | <= 0.010 % | |||
Descriptive Properties | |||||
Color | Cream | ||||
Drying Recommended | Yes | ||||
Features | Appearance, Pleasing Surface | ||||
Arc Resistant | |||||
Aromatic | |||||
Chemical Resistance, Good | |||||
Dimensional Stability, Good | |||||
Flow, Good | |||||
Heat Aging Resistance, Good | |||||
Moisture Absorption, Low | |||||
Platable | |||||
Platable | |||||
Filler | Glass fiber reinforcement | ||||
Flame Retardant - Halogen/Red Phosphorus Free | Yes | ||||
Forms | Pellets | ||||
Generic | LCP | ||||
Part Marking Code | >LCP-GF30< | ISO 11469 | |||
Polymer Family | LCP | ||||
Polymer Type | LCP | ||||
Processing | Injection Moldable | ||||
Processing Method | Injection Molding | ||||
Product Category | Electrical Resins | ||||
Flame Retardant Resins | |||||
Glass Reinforced Resins | |||||
Region Available | Americas | ||||
Asia/Pacific | |||||
Europe | |||||
Resin Identification | LCP-GF30 | ISO 1043 | |||
Uses | Automotive Applications | ||||
Automotive Electronics | |||||
Automotive, Under the Hood | |||||
Communication Applications | |||||
Computer Components | |||||
Connectors | |||||
Electrical/Electronic Applications | |||||
Parts, Engineering | |||||
Parts, Thin-walled | |||||
Printer Parts |