  4. Celanese Zenite® 7145L BK010 LCP

Celanese Zenite® 7145L BK010 LCP

Celanese Zenite® 7145L BK010 LCP 物性表: Celanese Zenite® 7145L BK010 LCP物性表及特性介绍,Celanese Zenite® 7145L BK010 LCP注塑参数详情,如需Celanese Zenite® 7145L BK010 LCP下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.74
  • 吸水率 [%]: 0.1
  • 缺口冲击强度: 0.6
  • 弯曲强度 [MPa]: 40.0
  • 弯曲模量 [MPa]: 5.00
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.76 g/cc1.76 g/ccASTM D 792
Density 1.74 g/cc0.0629 lb/in³ISO 1183
Filler Content 45 %45 %
Water Absorption 0.10 %
@Thickness 3.20 mm		0.10 %
@Thickness 0.126 in		Water, tap 23°C,24h; ASTM D570
Linear Mold Shrinkage, Flow  0.00010 cm/cm
@Thickness 3.17 mm		0.00010 in/in
@Thickness 0.125 in		ASTM D955
 0.00050 cm/cm
@Thickness 2.00 mm		0.00050 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
 0.00070 cm/cm
@Thickness 15.7 mm		0.00070 in/in
@Thickness 0.620 in		ASTM D955
Linear Mold Shrinkage, Transverse  0.0030 cm/cm
@Thickness 3.17 mm		0.0030 in/in
@Thickness 0.125 in		ASTM D955
 0.0050 cm/cm
@Thickness 1.60 mm		0.0050 in/in
@Thickness 0.0630 in		ASTM D955
 0.0050 cm/cm
@Thickness 2.00 mm		0.0050 in/in
@Thickness 0.0787 in		ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  20.0 MPa
@Thickness 4.00 mm,
Temperature 250 °C		2900 psi
@Thickness 0.157 in,
Temperature 482 °F		ISO 527
 25.0 MPa
@Thickness 2.00 mm,
Temperature 250 °C		3630 psi
@Thickness 0.0787 in,
Temperature 482 °F		ISO 527
 30.0 MPa
@Thickness 1.00 mm,
Temperature 250 °C		4350 psi
@Thickness 0.0394 in,
Temperature 482 °F		ISO 527
 30.0 MPa
@Thickness 4.00 mm,
Temperature 200 °C		4350 psi
@Thickness 0.157 in,
Temperature 392 °F		ISO 527
 35.0 MPa
@Thickness 2.00 mm,
Temperature 200 °C		5080 psi
@Thickness 0.0787 in,
Temperature 392 °F		ISO 527
 40.0 MPa
@Thickness 4.00 mm,
Temperature 150 °C		5800 psi
@Thickness 0.157 in,
Temperature 302 °F		ISO 527
 40.0 MPa
@Thickness 1.00 mm,
Temperature 200 °C		5800 psi
@Thickness 0.0394 in,
Temperature 392 °F		ISO 527
 45.0 MPa
@Thickness 2.00 mm,
Temperature 150 °C		6530 psi
@Thickness 0.0787 in,
Temperature 302 °F		ISO 527
 45.0 MPa
@Thickness 4.00 mm,
Temperature 120 °C		6530 psi
@Thickness 0.157 in,
Temperature 248 °F		ISO 527
 50.0 MPa
@Thickness 1.00 mm,
Temperature 150 °C		7250 psi
@Thickness 0.0394 in,
Temperature 302 °F		ISO 527
 50.0 MPa
@Thickness 2.00 mm,
Temperature 120 °C		7250 psi
@Thickness 0.0787 in,
Temperature 248 °F		ISO 527
 55.0 MPa
@Thickness 1.00 mm,
Temperature 120 °C		7980 psi
@Thickness 0.0394 in,
Temperature 248 °F		ISO 527
 120 MPa
@Thickness 4.00 mm,
Temperature 23.0 °C		17400 psi
@Thickness 0.157 in,
Temperature 73.4 °F		ISO 527
 130 MPa
@Thickness 2.00 mm,
Temperature 23.0 °C		18900 psi
@Thickness 0.0787 in,
Temperature 73.4 °F		ISO 527
 140 MPa
@Thickness 1.00 mm,
Temperature 23.0 °C		20300 psi
@Thickness 0.0394 in,
Temperature 73.4 °F		ISO 527
 150 MPa
@Thickness 4.00 mm,
Temperature -30.0 °C		21800 psi
@Thickness 0.157 in,
Temperature -22.0 °F		ISO 527
 160 MPa
@Thickness 4.00 mm,
Temperature -40.0 °C		23200 psi
@Thickness 0.157 in,
Temperature -40.0 °F		ISO 527
 165 MPa
@Thickness 2.00 mm,
Temperature -30.0 °C		23900 psi
@Thickness 0.0787 in,
Temperature -22.0 °F		ISO 527
 180 MPa
@Thickness 1.00 mm,
Temperature -30.0 °C		26100 psi
@Thickness 0.0394 in,
Temperature -22.0 °F		ISO 527
 180 MPa
@Thickness 2.00 mm,
Temperature -40.0 °C		26100 psi
@Thickness 0.0787 in,
Temperature -40.0 °F		ISO 527
 190 MPa
@Thickness 1.00 mm,
Temperature -40.0 °C		27600 psi
@Thickness 0.0394 in,
Temperature -40.0 °F		ISO 527
Tensile Strength, Ultimate  40.0 MPa
@Thickness 3.17 mm,
Temperature 150 °C		5800 psi
@Thickness 0.125 in,
Temperature 302 °F		ASTM D638
 45.0 MPa
@Thickness 1.60 mm,
Temperature 150 °C		6530 psi
@Thickness 0.0630 in,
Temperature 302 °F		ASTM D638
 50.0 MPa
@Thickness 3.17 mm,
Temperature 120 °C		7250 psi
@Thickness 0.125 in,
Temperature 248 °F		ASTM D638
 57.0 MPa
@Thickness 1.60 mm,
Temperature 120 °C		8270 psi
@Thickness 0.0630 in,
Temperature 248 °F		ASTM D638
 119 MPa
@Thickness 3.17 mm,
Temperature 23.0 °C		17300 psi
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D638
 130 MPa
@Thickness 1.60 mm,
Temperature 23.0 °C		18900 psi
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D638
 171 MPa
@Thickness 3.17 mm,
Temperature -40.0 °C		24800 psi
@Thickness 0.125 in,
Temperature -40.0 °F		ASTM D638
 190 MPa
@Thickness 1.60 mm,
Temperature -40.0 °C		27600 psi
@Thickness 0.0630 in,
Temperature -40.0 °F		ASTM D638
Elongation at Break  0.30 %
@Thickness 1.00 mm,
Temperature 200 °C		0.30 %
@Thickness 0.0394 in,
Temperature 392 °F		ISO 527
 0.30 %
@Thickness 1.00 mm,
Temperature 250 °C		0.30 %
@Thickness 0.0394 in,
Temperature 482 °F		ISO 527
 0.40 %
@Thickness 1.00 mm,
Temperature 120 °C		0.40 %
@Thickness 0.0394 in,
Temperature 248 °F		ISO 527
 0.40 %
@Thickness 1.00 mm,
Temperature 150 °C		0.40 %
@Thickness 0.0394 in,
Temperature 302 °F		ISO 527
 0.60 %
@Thickness 2.00 mm,
Temperature 200 °C		0.60 %
@Thickness 0.0787 in,
Temperature 392 °F		ISO 527
 0.60 %
@Thickness 4.00 mm,
Temperature 120 °C		0.60 %
@Thickness 0.157 in,
Temperature 248 °F		ISO 527
 0.60 %
@Thickness 4.00 mm,
Temperature 150 °C		0.60 %
@Thickness 0.157 in,
Temperature 302 °F		ISO 527
 0.60 %
@Thickness 1.00 mm,
Temperature 23.0 °C		0.60 %
@Thickness 0.0394 in,
Temperature 73.4 °F		ISO 527
 0.60 %
@Thickness 1.00 mm,
Temperature -30.0 °C		0.60 %
@Thickness 0.0394 in,
Temperature -22.0 °F		ISO 527
 0.60 %
@Thickness 1.00 mm,
Temperature -40.0 °C		0.60 %
@Thickness 0.0394 in,
Temperature -40.0 °F		ISO 527
 0.60 %
@Thickness 4.00 mm,
Temperature 250 °C		0.60 %
@Thickness 0.157 in,
Temperature 482 °F		ISO 527
 0.70 %
@Thickness 2.00 mm,
Temperature 250 °C		0.70 %
@Thickness 0.0787 in,
Temperature 482 °F		ISO 527
 0.70 %
@Thickness 2.00 mm,
Temperature 120 °C		0.70 %
@Thickness 0.0787 in,
Temperature 248 °F		ISO 527
 0.70 %
@Thickness 4.00 mm,
Temperature 200 °C		0.70 %
@Thickness 0.157 in,
Temperature 392 °F		ISO 527
 0.70 %
@Thickness 2.00 mm,
Temperature 150 °C		0.70 %
@Thickness 0.0787 in,
Temperature 302 °F		ISO 527
 0.90 %
@Thickness 4.00 mm,
Temperature -40.0 °C		0.90 %
@Thickness 0.157 in,
Temperature -40.0 °F		ISO 527
 0.90 %
@Thickness 4.00 mm,
Temperature -30.0 °C		0.90 %
@Thickness 0.157 in,
Temperature -22.0 °F		ISO 527
 0.90 %
@Thickness 1.60 mm,
Temperature 23.0 °C		0.90 %
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D638
 0.90 %
@Thickness 2.00 mm,
Temperature 23.0 °C		0.90 %
@Thickness 0.0787 in,
Temperature 73.4 °F		ISO 527
 0.90 %
@Thickness 4.00 mm,
Temperature 23.0 °C		0.90 %
@Thickness 0.157 in,
Temperature 73.4 °F		ISO 527
 0.90 %
@Thickness 2.00 mm,
Temperature -30.0 °C		0.90 %
@Thickness 0.0787 in,
Temperature -22.0 °F		ISO 527
 0.90 %
@Thickness 2.00 mm,
Temperature -40.0 °C		0.90 %
@Thickness 0.0787 in,
Temperature -40.0 °F		ISO 527
 1.1 %
@Thickness 3.17 mm,
Temperature 23.0 °C		1.1 %
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D638
Tensile Modulus  6.00 GPa
@Thickness 4.00 mm,
Temperature 250 °C		870 ksi
@Thickness 0.157 in,
Temperature 482 °F		ISO 527
 7.00 GPa
@Thickness 2.00 mm,
Temperature 250 °C		1020 ksi
@Thickness 0.0787 in,
Temperature 482 °F		ISO 527
 7.50 GPa
@Thickness 1.00 mm,
Temperature 250 °C		1090 ksi
@Thickness 0.0394 in,
Temperature 482 °F		ISO 527
 9.00 GPa
@Thickness 3.17 mm,
Temperature 150 °C		1310 ksi
@Thickness 0.125 in,
Temperature 302 °F		ASTM D638
 9.00 GPa
@Thickness 4.00 mm,
Temperature 200 °C		1310 ksi
@Thickness 0.157 in,
Temperature 392 °F		ISO 527
 10.0 GPa
@Thickness 2.00 mm,
Temperature 200 °C		1450 ksi
@Thickness 0.0787 in,
Temperature 392 °F		ISO 527
 10.3 GPa
@Thickness 1.60 mm,
Temperature 150 °C		1490 ksi
@Thickness 0.0630 in,
Temperature 302 °F		ASTM D638
 11.0 GPa
@Thickness 1.00 mm,
Temperature 200 °C		1600 ksi
@Thickness 0.0394 in,
Temperature 392 °F		ISO 527
 11.0 GPa
@Thickness 4.00 mm,
Temperature 150 °C		1600 ksi
@Thickness 0.157 in,
Temperature 302 °F		ISO 527
 11.5 GPa
@Thickness 2.00 mm,
Temperature 150 °C		1670 ksi
@Thickness 0.0787 in,
Temperature 302 °F		ISO 527
 12.0 GPa
@Thickness 1.00 mm,
Temperature 150 °C		1740 ksi
@Thickness 0.0394 in,
Temperature 302 °F		ISO 527
 12.0 GPa
@Thickness 4.00 mm,
Temperature 120 °C		1740 ksi
@Thickness 0.157 in,
Temperature 248 °F		ISO 527
 12.5 GPa
@Thickness 2.00 mm,
Temperature 120 °C		1810 ksi
@Thickness 0.0787 in,
Temperature 248 °F		ISO 527
 13.0 GPa
@Thickness 1.00 mm,
Temperature 120 °C		1890 ksi
@Thickness 0.0394 in,
Temperature 248 °F		ISO 527
 15.2 GPa
@Thickness 3.17 mm,
Temperature 120 °C		2200 ksi
@Thickness 0.125 in,
Temperature 248 °F		ASTM D638
 18.0 GPa
@Thickness 4.00 mm,
Temperature 23.0 °C		2610 ksi
@Thickness 0.157 in,
Temperature 73.4 °F		ISO 527
 18.6 GPa
@Thickness 3.17 mm,
Temperature 23.0 °C		2700 ksi
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D638
 18.6 GPa
@Thickness 1.60 mm,
Temperature 120 °C		2700 ksi
@Thickness 0.0630 in,
Temperature 248 °F		ASTM D638
 20.5 GPa
@Thickness 2.00 mm,
Temperature 23.0 °C		2970 ksi
@Thickness 0.0787 in,
Temperature 73.4 °F		ISO 527
 21.0 GPa
@Thickness 1.60 mm,
Temperature 23.0 °C		3050 ksi
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D638
 22.0 GPa
@Thickness 1.00 mm,
Temperature 23.0 °C		3190 ksi
@Thickness 0.0394 in,
Temperature 73.4 °F		ISO 527
 22.8 GPa
@Thickness 3.17 mm,
Temperature -40.0 °C		3310 ksi
@Thickness 0.125 in,
Temperature -40.0 °F		ASTM D638
 23.5 GPa
@Thickness 4.00 mm,
Temperature -30.0 °C		3410 ksi
@Thickness 0.157 in,
Temperature -22.0 °F		ISO 527
 24.5 GPa
@Thickness 4.00 mm,
Temperature -40.0 °C		3550 ksi
@Thickness 0.157 in,
Temperature -40.0 °F		ISO 527
 24.5 GPa
@Thickness 2.00 mm,
Temperature -30.0 °C		3550 ksi
@Thickness 0.0787 in,
Temperature -22.0 °F		ISO 527
 25.0 GPa
@Thickness 1.00 mm,
Temperature -30.0 °C		3630 ksi
@Thickness 0.0394 in,
Temperature -22.0 °F		ISO 527
 26.0 GPa
@Thickness 1.60 mm,
Temperature -40.0 °C		3770 ksi
@Thickness 0.0630 in,
Temperature -40.0 °F		ASTM D638
 26.0 GPa
@Thickness 2.00 mm,
Temperature -40.0 °C		3770 ksi
@Thickness 0.0787 in,
Temperature -40.0 °F		ISO 527
 27.0 GPa
@Thickness 1.00 mm,
Temperature -40.0 °C		3920 ksi
@Thickness 0.0394 in,
Temperature -40.0 °F		ISO 527
Flexural Strength  10.0 MPa
@Thickness 4.00 mm,
Temperature 250 °C		1450 psi
@Thickness 0.157 in,
Temperature 482 °F		ISO 178
 20.0 MPa
@Thickness 2.00 mm,
Temperature 250 °C		2900 psi
@Thickness 0.0787 in,
Temperature 482 °F		ISO 178
 24.0 MPa
@Thickness 3.17 mm,
Temperature 250 °C		3480 psi
@Thickness 0.125 in,
Temperature 482 °F		ASTM D790
 29.0 MPa
@Thickness 0.790 mm,
Temperature 250 °C		4210 psi
@Thickness 0.0311 in,
Temperature 482 °F		ASTM D790
 30.0 MPa
@Thickness 1.00 mm,
Temperature 250 °C		4350 psi
@Thickness 0.0394 in,
Temperature 482 °F		ISO 178
 43.0 MPa
@Thickness 3.17 mm,
Temperature 200 °C		6240 psi
@Thickness 0.125 in,
Temperature 392 °F		ASTM D790
 45.0 MPa
@Thickness 4.00 mm,
Temperature 200 °C		6530 psi
@Thickness 0.157 in,
Temperature 392 °F		ISO 178
 50.0 MPa
@Thickness 2.00 mm,
Temperature 200 °C		7250 psi
@Thickness 0.0787 in,
Temperature 392 °F		ISO 178
 50.0 MPa
@Thickness 0.790 mm,
Temperature 200 °C		7250 psi
@Thickness 0.0311 in,
Temperature 392 °F		ASTM D790
 55.0 MPa
@Thickness 1.00 mm,
Temperature 200 °C		7980 psi
@Thickness 0.0394 in,
Temperature 392 °F		ISO 178
 58.0 MPa
@Thickness 3.17 mm,
Temperature 150 °C		8410 psi
@Thickness 0.125 in,
Temperature 302 °F		ASTM D790
 70.0 MPa
@Thickness 4.00 mm,
Temperature 150 °C		10200 psi
@Thickness 0.157 in,
Temperature 302 °F		ISO 178
 71.0 MPa
@Thickness 3.17 mm,
Temperature 120 °C		10300 psi
@Thickness 0.125 in,
Temperature 248 °F		ASTM D790
 71.0 MPa
@Thickness 1.60 mm,
Temperature 150 °C		10300 psi
@Thickness 0.0630 in,
Temperature 302 °F		ASTM D790
 75.0 MPa
@Thickness 0.790 mm,
Temperature 150 °C		10900 psi
@Thickness 0.0311 in,
Temperature 302 °F		ASTM D790
 80.0 MPa
@Thickness 2.00 mm,
Temperature 150 °C		11600 psi
@Thickness 0.0787 in,
Temperature 302 °F		ISO 178
 80.0 MPa
@Thickness 4.00 mm,
Temperature 120 °C		11600 psi
@Thickness 0.157 in,
Temperature 248 °F		ISO 178
 90.0 MPa
@Thickness 1.00 mm,
Temperature 150 °C		13100 psi
@Thickness 0.0394 in,
Temperature 302 °F		ISO 178
 90.0 MPa
@Thickness 2.00 mm,
Temperature 120 °C		13100 psi
@Thickness 0.0787 in,
Temperature 248 °F		ISO 178
 92.0 MPa
@Thickness 0.790 mm,
Temperature 120 °C		13300 psi
@Thickness 0.0311 in,
Temperature 248 °F		ASTM D790
 100 MPa
@Thickness 1.00 mm,
Temperature 120 °C		14500 psi
@Thickness 0.0394 in,
Temperature 248 °F		ISO 178
 158 MPa
@Thickness 3.17 mm,
Temperature 23.0 °C		22900 psi
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D790
 180 MPa
@Thickness 4.00 mm,
Temperature 23.0 °C		26100 psi
@Thickness 0.157 in,
Temperature 73.4 °F		ISO 178
 195 MPa
@Thickness 1.60 mm,
Temperature 23.0 °C		28300 psi
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D790
 205 MPa
@Thickness 0.790 mm,
Temperature 23.0 °C		29700 psi
@Thickness 0.0311 in,
Temperature 73.4 °F		ASTM D790
 210 MPa
@Thickness 2.00 mm,
Temperature 23.0 °C		30500 psi
@Thickness 0.0787 in,
Temperature 73.4 °F		ISO 178
 225 MPa
@Thickness 3.17 mm,
Temperature -40.0 °C		32600 psi
@Thickness 0.125 in,
Temperature -40.0 °F		ASTM D790
 230 MPa
@Thickness 1.00 mm,
Temperature 23.0 °C		33400 psi
@Thickness 0.0394 in,
Temperature 73.4 °F		ISO 178
 240 MPa
@Thickness 4.00 mm,
Temperature -30.0 °C		34800 psi
@Thickness 0.157 in,
Temperature -22.0 °F		ISO 178
 250 MPa
@Thickness 4.00 mm,
Temperature -40.0 °C		36300 psi
@Thickness 0.157 in,
Temperature -40.0 °F		ISO 178
 255 MPa
@Thickness 2.00 mm,
Temperature -30.0 °C		37000 psi
@Thickness 0.0787 in,
Temperature -22.0 °F		ISO 178
 270 MPa
@Thickness 2.00 mm,
Temperature -40.0 °C		39200 psi
@Thickness 0.0787 in,
Temperature -40.0 °F		ISO 178
 280 MPa
@Thickness 1.00 mm,
Temperature -30.0 °C		40600 psi
@Thickness 0.0394 in,
Temperature -22.0 °F		ISO 178
 280 MPa
@Thickness 1.60 mm,
Temperature -40.0 °C		40600 psi
@Thickness 0.0630 in,
Temperature -40.0 °F		ASTM D790
 300 MPa
@Thickness 0.790 mm,
Temperature -40.0 °C		43500 psi
@Thickness 0.0311 in,
Temperature -40.0 °F		ASTM D790
 300 MPa
@Thickness 1.00 mm,
Temperature -40.0 °C		43500 psi
@Thickness 0.0394 in,
Temperature -40.0 °F		ISO 178
Flexural Modulus  5.00 GPa
@Thickness 4.00 mm,
Temperature 250 °C		725 ksi
@Thickness 0.157 in,
Temperature 482 °F		ISO 178
 6.60 GPa
@Thickness 3.17 mm,
Temperature 250 °C		957 ksi
@Thickness 0.125 in,
Temperature 482 °F		ASTM D790
 7.60 GPa
@Thickness 1.60 mm,
Temperature 250 °C		1100 ksi
@Thickness 0.0630 in,
Temperature 482 °F		ASTM D790
 8.00 GPa
@Thickness 2.00 mm,
Temperature 250 °C		1160 ksi
@Thickness 0.0787 in,
Temperature 482 °F		ISO 178
 8.30 GPa
@Thickness 0.790 mm,
Temperature 250 °C		1200 ksi
@Thickness 0.0311 in,
Temperature 482 °F		ASTM D790
 8.30 GPa
@Thickness 3.17 mm,
Temperature 150 °C		1200 ksi
@Thickness 0.125 in,
Temperature 302 °F		ASTM D790
 8.60 GPa
@Thickness 3.17 mm,
Temperature 200 °C		1250 ksi
@Thickness 0.125 in,
Temperature 392 °F		ASTM D790
 9.00 GPa
@Thickness 4.00 mm,
Temperature 200 °C		1310 ksi
@Thickness 0.157 in,
Temperature 392 °F		ISO 178
 9.00 GPa
@Thickness 1.00 mm,
Temperature 250 °C		1310 ksi
@Thickness 0.0394 in,
Temperature 482 °F		ISO 178
 9.00 GPa
@Thickness 1.60 mm,
Temperature 200 °C		1310 ksi
@Thickness 0.0630 in,
Temperature 392 °F		ASTM D790
 9.70 GPa
@Thickness 0.790 mm,
Temperature 200 °C		1410 ksi
@Thickness 0.0311 in,
Temperature 392 °F		ASTM D790
 9.70 GPa
@Thickness 3.17 mm,
Temperature 120 °C		1410 ksi
@Thickness 0.125 in,
Temperature 248 °F		ASTM D790
 10.0 GPa
@Thickness 2.00 mm,
Temperature 200 °C		1450 ksi
@Thickness 0.0787 in,
Temperature 392 °F		ISO 178
 11.0 GPa
@Thickness 1.60 mm,
Temperature 150 °C		1600 ksi
@Thickness 0.0630 in,
Temperature 302 °F		ASTM D790
 12.0 GPa
@Thickness 1.00 mm,
Temperature 200 °C		1740 ksi
@Thickness 0.0394 in,
Temperature 392 °F		ISO 178
 12.5 GPa
@Thickness 4.00 mm,
Temperature 150 °C		1810 ksi
@Thickness 0.157 in,
Temperature 302 °F		ISO 178
 13.0 GPa
@Thickness 4.00 mm,
Temperature 120 °C		1890 ksi
@Thickness 0.157 in,
Temperature 248 °F		ISO 178
 13.8 GPa
@Thickness 3.17 mm,
Temperature 23.0 °C		2000 ksi
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D790
 14.0 GPa
@Thickness 2.00 mm,
Temperature 150 °C		2030 ksi
@Thickness 0.0787 in,
Temperature 302 °F		ISO 178
 14.5 GPa
@Thickness 0.790 mm,
Temperature 150 °C		2100 ksi
@Thickness 0.0311 in,
Temperature 302 °F		ASTM D790
 15.0 GPa
@Thickness 1.00 mm,
Temperature 150 °C		2180 ksi
@Thickness 0.0394 in,
Temperature 302 °F		ISO 178
 15.0 GPa
@Thickness 2.00 mm,
Temperature 120 °C		2180 ksi
@Thickness 0.0787 in,
Temperature 248 °F		ISO 178
 16.0 GPa
@Thickness 3.17 mm,
Temperature -40.0 °C		2320 ksi
@Thickness 0.125 in,
Temperature -40.0 °F		ASTM D790
 17.2 GPa
@Thickness 1.60 mm,
Temperature 23.0 °C		2490 ksi
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D790
 17.8 GPa
@Thickness 4.00 mm,
Temperature 23.0 °C		2580 ksi
@Thickness 0.157 in,
Temperature 73.4 °F		ISO 178
 18.0 GPa
@Thickness 1.00 mm,
Temperature 120 °C		2610 ksi
@Thickness 0.0394 in,
Temperature 248 °F		ISO 178
 18.6 GPa
@Thickness 1.60 mm,
Temperature -40.0 °C		2700 ksi
@Thickness 0.0630 in,
Temperature -40.0 °F		ASTM D790
 20.0 GPa
@Thickness 4.00 mm,
Temperature -30.0 °C		2900 ksi
@Thickness 0.157 in,
Temperature -22.0 °F		ISO 178
 20.5 GPa
@Thickness 2.00 mm,
Temperature 23.0 °C		2970 ksi
@Thickness 0.0787 in,
Temperature 73.4 °F		ISO 178
 20.7 GPa
@Thickness 0.790 mm,
Temperature 23.0 °C		3000 ksi
@Thickness 0.0311 in,
Temperature 73.4 °F		ASTM D790
 21.0 GPa
@Thickness 4.00 mm,
Temperature -40.0 °C		3050 ksi
@Thickness 0.157 in,
Temperature -40.0 °F		ISO 178
 21.5 GPa
@Thickness 2.00 mm,
Temperature -30.0 °C		3120 ksi
@Thickness 0.0787 in,
Temperature -22.0 °F		ISO 178
 22.5 GPa
@Thickness 2.00 mm,
Temperature -40.0 °C		3260 ksi
@Thickness 0.0787 in,
Temperature -40.0 °F		ISO 178
 24.0 GPa
@Thickness 1.00 mm,
Temperature 23.0 °C		3480 ksi
@Thickness 0.0394 in,
Temperature 73.4 °F		ISO 178
 24.1 GPa
@Thickness 0.790 mm,
Temperature -40.0 °C		3500 ksi
@Thickness 0.0311 in,
Temperature -40.0 °F		ASTM D790
 25.0 GPa
@Thickness 1.00 mm,
Temperature -30.0 °C		3630 ksi
@Thickness 0.0394 in,
Temperature -22.0 °F		ISO 178
 25.5 GPa
@Thickness 1.00 mm,
Temperature -40.0 °C		3700 ksi
@Thickness 0.0394 in,
Temperature -40.0 °F		ISO 178
Izod Impact, Notched  0.600 J/cm
@Thickness 3.17 mm,
Temperature 23.0 °C		1.12 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D256
 0.900 J/cm
@Thickness 1.60 mm,
Temperature 23.0 °C		1.69 ft-lb/in
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D256
 1.90 J/cm
@Thickness 0.790 mm,
Temperature 23.0 °C		3.56 ft-lb/in
@Thickness 0.0311 in,
Temperature 73.4 °F		ASTM D256
Izod Impact, Unnotched  3.16 J/cm
@Thickness 3.17 mm,
Temperature 23.0 °C		5.92 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D4812
 4.00 J/cm
@Thickness 0.790 mm,
Temperature 23.0 °C		7.49 ft-lb/in
@Thickness 0.0311 in,
Temperature 73.4 °F		ASTM D4812
 6.53 J/cm
@Thickness 1.60 mm,
Temperature 23.0 °C		12.2 ft-lb/in
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D4812
Izod Impact, Notched (ISO) 10.0 kJ/m²
@Temperature 23.0 °C		4.76 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Charpy Impact Unnotched  1.30 J/cm²
@Temperature -30.0 °C		6.19 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 1.80 J/cm²
@Temperature 23.0 °C		8.57 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  1.00 J/cm²
@Temperature -30.0 °C		4.76 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 1.00 J/cm²
@Temperature 23.0 °C		4.76 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+15 ohm-cm>= 1.00e+15 ohm-cmIEC 60093
 1.00e+16 ohm-cm1.00e+16 ohm-cmIEC 60093
Surface Resistance >= 1.00e+15 ohm>= 1.00e+15 ohmIEC 60093
 1.00e+16 ohm1.00e+16 ohmIEC 60093
Dielectric Constant  4.4
@Frequency 1.00e+6 Hz		4.4
@Frequency 1.00e+6 Hz		IEC 60250
 4.8
@Frequency 100 Hz		4.8
@Frequency 100 Hz		IEC 60250
 4.3
@Frequency 60.0 Hz,
Temperature 23.0 °C		4.3
@Frequency 60.0 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 4.3
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.3
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 4.6
@Frequency 1000 Hz,
Temperature 23.0 °C		4.6
@Frequency 1000 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 5.2
@Frequency 1.00e+6 Hz,
Temperature 120 °C		5.2
@Frequency 1.00e+6 Hz,
Temperature 248 °F		3.2mm (0.125in); ASTM D 150
 5.3
@Frequency 1.00e+6 Hz,
Temperature 200 °C		5.3
@Frequency 1.00e+6 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 150
 5.3
@Frequency 1.00e+6 Hz,
Temperature 150 °C		5.3
@Frequency 1.00e+6 Hz,
Temperature 302 °F		3.2mm (0.125in); ASTM D 150
 5.3
@Frequency 1000 Hz,
Temperature 120 °C		5.3
@Frequency 1000 Hz,
Temperature 248 °F		3.2mm (0.125in); ASTM D 150
 5.4
@Frequency 1000 Hz,
Temperature 150 °C		5.4
@Frequency 1000 Hz,
Temperature 302 °F		3.2mm (0.125in); ASTM D 150
 5.5
@Frequency 1000 Hz,
Temperature 200 °C		5.5
@Frequency 1000 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 150
 5.6
@Frequency 60.0 Hz,
Temperature 200 °C		5.6
@Frequency 60.0 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 150
Dielectric Strength  29.0 kV/mm
@Thickness 2.00 mm		737 kV/in
@Thickness 0.0787 in		IEC 60243-1
 36.0 kV/mm
@Thickness 1.00 mm		914 kV/in
@Thickness 0.0394 in		IEC 60243-1
 20.0 kV/mm
@Thickness 3.20 mm,
Temperature 200 °C		508 kV/in
@Thickness 0.126 in,
Temperature 392 °F		Short time; ASTM D149
 20.0 kV/mm
@Thickness 3.20 mm,
Temperature 120 °C		508 kV/in
@Thickness 0.126 in,
Temperature 248 °F		Short time; ASTM D149
 20.0 kV/mm
@Thickness 3.20 mm,
Temperature 150 °C		508 kV/in
@Thickness 0.126 in,
Temperature 302 °F		Short time; ASTM D149
 21.0 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		533 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		Short time; ASTM D149
 25.0 kV/mm
@Thickness 1.60 mm,
Temperature 150 °C		635 kV/in
@Thickness 0.0630 in,
Temperature 302 °F		Short time; ASTM D149
 26.0 kV/mm
@Thickness 1.60 mm,
Temperature 200 °C		660 kV/in
@Thickness 0.0630 in,
Temperature 392 °F		Short time; ASTM D149
 27.0 kV/mm
@Thickness 1.60 mm,
Temperature 23.0 °C		686 kV/in
@Thickness 0.0630 in,
Temperature 73.4 °F		Short time; ASTM D149
 32.0 kV/mm
@Thickness 0.800 mm,
Temperature 200 °C		813 kV/in
@Thickness 0.0315 in,
Temperature 392 °F		Short time; ASTM D149
 33.0 kV/mm
@Thickness 0.800 mm,
Temperature 150 °C		838 kV/in
@Thickness 0.0315 in,
Temperature 302 °F		Short time; ASTM D149
 33.0 kV/mm
@Thickness 0.800 mm,
Temperature 120 °C		838 kV/in
@Thickness 0.0315 in,
Temperature 248 °F		Short time; ASTM D149
 34.0 kV/mm
@Thickness 0.800 mm,
Temperature 23.0 °C		864 kV/in
@Thickness 0.0315 in,
Temperature 73.4 °F		Short time; ASTM D149
Dissipation Factor  0.0080
@Frequency 1000 Hz,
Temperature 120 °C		0.0080
@Frequency 1000 Hz,
Temperature 248 °F		3.2mm (0.125in); ASTM D 150
 0.0080
@Frequency 1.00e+6 Hz,
Temperature 200 °C		0.0080
@Frequency 1.00e+6 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 150
 0.0090
@Frequency 1000 Hz,
Temperature 150 °C		0.0090
@Frequency 1000 Hz,
Temperature 302 °F		3.2mm (0.125in); ASTM D 150
 0.012
@Frequency 1.00e+6 Hz,
Temperature 150 °C		0.012
@Frequency 1.00e+6 Hz,
Temperature 302 °F		3.2mm (0.125in); ASTM D 150
 0.013
@Frequency 100 Hz,
Temperature 23.0 °C		0.013
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.013
@Frequency 1000 Hz,
Temperature 23.0 °C		0.013
@Frequency 1000 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 0.014
@Frequency 60.0 Hz,
Temperature 23.0 °C		0.014
@Frequency 60.0 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 0.015
@Frequency 1000 Hz,
Temperature 200 °C		0.015
@Frequency 1000 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 150
 0.023
@Frequency 1.00e+6 Hz,
Temperature 120 °C		0.023
@Frequency 1.00e+6 Hz,
Temperature 248 °F		3.2mm (0.125in); ASTM D 150
 0.024
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.024
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 0.025
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.025
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 0.083
@Frequency 60.0 Hz,
Temperature 200 °C		0.083
@Frequency 60.0 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 150
Comparative Tracking Index 175 V175 VIEC 60112
 175 - 249 V175 - 249 VUL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear  0.000 µm/m-°C
@Thickness 2.00 mm,
Temperature 160 - 260 °C		0.000 µin/in-°F
@Thickness 0.0787 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 160 - 260 °C		1.67 µin/in-°F
@Thickness 0.157 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 2.00 mm,
Temperature -40.0 - 260 °C		1.67 µin/in-°F
@Thickness 0.0787 in,
Temperature -40.0 - 500 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 2.00 mm,
Temperature -40.0 - 23.0 °C		1.67 µin/in-°F
@Thickness 0.0787 in,
Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 55.0 - 160 °C		1.67 µin/in-°F
@Thickness 0.0787 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 4.00 µm/m-°C
@Thickness 4.00 mm,
Temperature -40.0 - 23.0 °C		2.22 µin/in-°F
@Thickness 0.157 in,
Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 4.00 µm/m-°C
@Thickness 4.00 mm,
Temperature -40.0 - 260 °C		2.22 µin/in-°F
@Thickness 0.157 in,
Temperature -40.0 - 500 °F		ISO 11359-1/-2
 4.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		2.22 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 5.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C		2.78 µin/in-°F
@Thickness 0.157 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 5.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 55.0 - 160 °C		2.78 µin/in-°F
@Thickness 0.157 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  51.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		28.3 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2; 4mm
 52.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		28.9 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2; 2mm
 72.0 µm/m-°C
@Temperature -40.0 - 260 °C		40.0 µin/in-°F
@Temperature -40.0 - 500 °F		ISO 11359-1/-2; 4mm
 72.0 µm/m-°C
@Temperature -40.0 - 260 °C		40.0 µin/in-°F
@Temperature -40.0 - 500 °F		ISO 11359-1/-2; 2mm
 60.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C		33.3 µin/in-°F
@Thickness 0.157 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 60.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		33.3 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 76.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 55.0 - 160 °C		42.2 µin/in-°F
@Thickness 0.0787 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 76.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 55.0 - 160 °C		42.2 µin/in-°F
@Thickness 0.157 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 78.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 160 - 260 °C		43.3 µin/in-°F
@Thickness 0.0787 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 85.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 160 - 260 °C		47.2 µin/in-°F
@Thickness 0.157 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
Melting Point 352 °C666 °F10°C/min; ISO 11357-1/-3
 357 °C675 °FASTM D 3418
Deflection Temperature at 1.8 MPa (264 psi) 295 °C563 °FISO 75-1/-2
 295 °C563 °FASTM D 648
Glass Transition Temp, Tg 120 °C248 °FASTM D 3418
UL RTI, Electrical  240 °C
@Thickness 1.50 mm		464 °F
@Thickness 0.0591 in		UL 746B
 240 °C
@Thickness 0.750 mm		464 °F
@Thickness 0.0295 in		UL 746B
 240 °C
@Thickness 3.00 mm		464 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical with Impact  210 °C
@Thickness 1.50 mm		410 °F
@Thickness 0.0591 in		UL 746B
 210 °C
@Thickness 0.750 mm		410 °F
@Thickness 0.0295 in		UL 746B
 210 °C
@Thickness 3.00 mm		410 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical without Impact  240 °C
@Thickness 1.50 mm		464 °F
@Thickness 0.0591 in		UL 746B
 240 °C
@Thickness 0.750 mm		464 °F
@Thickness 0.0295 in		UL 746B
 240 °C
@Thickness 3.00 mm		464 °F
@Thickness 0.118 in		UL 746B
Flammability, UL94  V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		IEC 60695-11-10
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		UL94
 V-0
@Thickness 0.750 mm		V-0
@Thickness 0.0295 in		IEC 60695-11-10
 V-0
@Thickness 0.750 mm		V-0
@Thickness 0.0295 in		UL94
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		IEC 60695-11-10
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		UL94
Oxygen Index 45 %45 %ISO 4589-1/-2
 38.5 %
@Thickness 3.17 mm		38.5 %
@Thickness 0.125 in		ASTM D2863
Glow Wire Test  825 °C
@Thickness 0.700 mm		1520 °F
@Thickness 0.0276 in		Glow Wire Ignition Temperature; IEC 60695-2-13
 850 °C
@Thickness 1.00 mm		1560 °F
@Thickness 0.0394 in		Glow Wire Ignition Temperature; IEC 60695-2-13
 850 °C
@Thickness 2.00 mm		1560 °F
@Thickness 0.0787 in		Glow Wire Ignition Temperature; IEC 60695-2-13
 900 °C
@Thickness 3.00 mm		1650 °F
@Thickness 0.118 in		Glow Wire Ignition Temperature; IEC 60695-2-13
 960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		Glow Wire Flammability Index; IEC 60695-2-12
 960 °C
@Thickness 2.00 mm		1760 °F
@Thickness 0.0787 in		Glow Wire Flammability Index; IEC 60695-2-12
 960 °C
@Thickness 0.700 mm		1760 °F
@Thickness 0.0276 in		Glow Wire Flammability Index; IEC 60695-2-12
 960 °C
@Thickness 1.00 mm		1760 °F
@Thickness 0.0394 in		Glow Wire Flammability Index; IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 365 °C689 °FOptimum
 360 - 370 °C680 - 698 °F
Mold Temperature 80.0 °C176 °FOptimum
 40.0 - 150 °C104 - 302 °F
Drying Temperature 150 °C302 °F
Dry Time 3 hour3 hourDehumidified Dryer
Moisture Content <= 0.010 %<= 0.010 %
 
Descriptive Properties
AdditiveLubricant
ColorBlack
Drying RecommendedYes
FeaturesAppearance, Pleasing Surface
 Arc Resistant
 Aromatic
 Chemical Resistance, Good
 Dimensional Stability, Good
 Flow, Good
 Heat Aging Resistance, Good
 Lubricated
 Moisture Absorption, Low
 Platable
FillerGlass fiber reinforcement
Flame Retardant - Halogen/Red Phosphorus FreeYes
FormsPellets
GenericLCP
Part Marking Code>LCP-GF45<ISO 11469
Polymer FamilyLCP
Polymer TypeLCP
ProcessingInjection Moldable
Processing MethodInjection Molding
Product CategoryElectrical Resins
 Flame Retardant Resins
 Glass Reinforced Resins
Region AvailableAmericas
 Asia/Pacific
 Europe
Resin IdentificationLCP-GF45ISO 1043
UsesAutomotive Applications
 Automotive Electronics
 Automotive, Under the Hood
 Communication Applications
 Computer Components
 Connectors
 Electrical/Electronic Applications
 Parts, Engineering
 Parts, Thin-walled
 Printer Parts

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31770.html

免责声明: 本文 Celanese Zenite® 7145L BK010 LCP 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4