  4. Celanese Zenite® 7130 WT010 LCP

Celanese Zenite® 7130 WT010 LCP

Celanese Zenite® 7130 WT010 LCP 物性表: Celanese Zenite® 7130 WT010 LCP物性表及特性介绍,Celanese Zenite® 7130 WT010 LCP注塑参数详情,如需Celanese Zenite® 7130 WT010 LCP下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.67
  • 缺口冲击强度: 1.7
  • 弯曲强度 [MPa]: 30.0
  • 弯曲模量 [MPa]: 13.0
  • 硬度: 110.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.65 g/cc1.65 g/ccASTM D 792
Density 1.67 g/cc0.0603 lb/in³ISO 1183
Filler Content 30 %30 %
Linear Mold Shrinkage, Flow  -0.00100 cm/cm
@Thickness 15.7 mm		-0.00100 in/in
@Thickness 0.620 in		ASTM D955
 0.00 cm/cm
@Thickness 3.17 mm		0.00 in/in
@Thickness 0.125 in		ASTM D955
Linear Mold Shrinkage, Transverse  0.0080 cm/cm
@Thickness 3.17 mm		0.0080 in/in
@Thickness 0.125 in		ASTM D955
 0.0090 cm/cm
@Thickness 1.60 mm		0.0090 in/in
@Thickness 0.0630 in		ASTM D955
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 6363ASTM D 785
Hardness, Rockwell R 110110ASTM D 785
Tensile Strength at Break 150 MPa21800 psiISO 527
Tensile Strength, Ultimate  30.0 MPa
@Thickness 3.17 mm,
Temperature 250 °C		4350 psi
@Thickness 0.125 in,
Temperature 482 °F		ASTM D638
 39.0 MPa
@Thickness 1.60 mm,
Temperature 250 °C		5660 psi
@Thickness 0.0630 in,
Temperature 482 °F		ASTM D638
 54.0 MPa
@Thickness 1.60 mm,
Temperature 200 °C		7830 psi
@Thickness 0.0630 in,
Temperature 392 °F		ASTM D638
 56.0 MPa
@Thickness 3.17 mm,
Temperature 200 °C		8120 psi
@Thickness 0.125 in,
Temperature 392 °F		ASTM D638
 60.0 MPa
@Thickness 3.17 mm,
Temperature 150 °C		8700 psi
@Thickness 0.125 in,
Temperature 302 °F		ASTM D638
 72.0 MPa
@Thickness 1.60 mm,
Temperature 150 °C		10400 psi
@Thickness 0.0630 in,
Temperature 302 °F		ASTM D638
 75.0 MPa
@Thickness 3.17 mm,
Temperature 120 °C		10900 psi
@Thickness 0.125 in,
Temperature 248 °F		ASTM D638
 79.0 MPa
@Thickness 1.60 mm,
Temperature 120 °C		11500 psi
@Thickness 0.0630 in,
Temperature 248 °F		ASTM D638
 145 MPa
@Thickness 3.17 mm,
Temperature 23.0 °C		21000 psi
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D638
 173 MPa
@Thickness 1.60 mm,
Temperature 23.0 °C		25100 psi
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D638
 230 MPa
@Thickness 3.17 mm,
Temperature -40.0 °C		33400 psi
@Thickness 0.125 in,
Temperature -40.0 °F		ASTM D638
 235 MPa
@Thickness 1.60 mm,
Temperature -40.0 °C		34100 psi
@Thickness 0.0630 in,
Temperature -40.0 °F		ASTM D638
Elongation at Break 1.4 %1.4 %ISO 527
 0.80 %
@Thickness 1.60 mm,
Temperature 250 °C		0.80 %
@Thickness 0.0630 in,
Temperature 482 °F		ASTM D638
 1.0 %
@Thickness 1.60 mm,
Temperature 150 °C		1.0 %
@Thickness 0.0630 in,
Temperature 302 °F		ASTM D638
 1.2 %
@Thickness 1.60 mm,
Temperature 120 °C		1.2 %
@Thickness 0.0630 in,
Temperature 248 °F		ASTM D638
 1.3 %
@Thickness 1.60 mm,
Temperature -40.0 °C		1.3 %
@Thickness 0.0630 in,
Temperature -40.0 °F		ASTM D638
 1.4 %
@Thickness 1.60 mm,
Temperature 200 °C		1.4 %
@Thickness 0.0630 in,
Temperature 392 °F		ASTM D638
 1.6 %
@Thickness 1.60 mm,
Temperature 23.0 °C		1.6 %
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D638
 2.2 %
@Thickness 3.17 mm,
Temperature 23.0 °C		2.2 %
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D638
Tensile Modulus 16.5 GPa2390 ksiISO 527
 8.963 GPa
@Thickness 1.60 mm,
Temperature 250 °C		1300 ksi
@Thickness 0.0630 in,
Temperature 482 °F		ASTM D638
 9.00 GPa
@Thickness 3.17 mm,
Temperature 250 °C		1310 ksi
@Thickness 0.125 in,
Temperature 482 °F		ASTM D638
 9.00 GPa
@Thickness 3.17 mm,
Temperature 150 °C		1310 ksi
@Thickness 0.125 in,
Temperature 302 °F		ASTM D638
 9.00 GPa
@Thickness 3.17 mm,
Temperature 200 °C		1310 ksi
@Thickness 0.125 in,
Temperature 392 °F		ASTM D638
 9.308 GPa
@Thickness 1.60 mm,
Temperature 200 °C		1350 ksi
@Thickness 0.0630 in,
Temperature 392 °F		ASTM D638
 12.066 GPa
@Thickness 1.60 mm,
Temperature 150 °C		1750.0 ksi
@Thickness 0.0630 in,
Temperature 302 °F		ASTM D638
 14.0 GPa
@Thickness 3.17 mm,
Temperature 120 °C		2030 ksi
@Thickness 0.125 in,
Temperature 248 °F		ASTM D638
 18.0 GPa
@Thickness 3.17 mm,
Temperature 23.0 °C		2610 ksi
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D638
 19.306 GPa
@Thickness 1.60 mm,
Temperature 23.0 °C		2800.1 ksi
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D638
 23.0 GPa
@Thickness 3.17 mm,
Temperature -40.0 °C		3340 ksi
@Thickness 0.125 in,
Temperature -40.0 °F		ASTM D638
 26.89 GPa
@Thickness 1.60 mm,
Temperature -40.0 °C		3900 ksi
@Thickness 0.0630 in,
Temperature -40.0 °F		ASTM D638
Flexural Strength 210 MPa
@Temperature 23.0 °C		30500 psi
@Temperature 73.4 °F		ISO 178
 29.0 MPa
@Thickness 1.60 mm,
Temperature 250 °C		4210 psi
@Thickness 0.0630 in,
Temperature 482 °F		ASTM D790
 30.0 MPa
@Thickness 0.800 mm,
Temperature 250 °C		4350 psi
@Thickness 0.0315 in,
Temperature 482 °F		ASTM D790
 30.0 MPa
@Thickness 3.17 mm,
Temperature 250 °C		4350 psi
@Thickness 0.125 in,
Temperature 482 °F		ASTM D790
 48.0 MPa
@Thickness 3.17 mm,
Temperature 200 °C		6960 psi
@Thickness 0.125 in,
Temperature 392 °F		ASTM D790
 49.0 MPa
@Thickness 1.60 mm,
Temperature 200 °C		7110 psi
@Thickness 0.0630 in,
Temperature 392 °F		ASTM D790
 53.0 MPa
@Thickness 0.800 mm,
Temperature 200 °C		7690 psi
@Thickness 0.0315 in,
Temperature 392 °F		ASTM D790
 64.0 MPa
@Thickness 3.17 mm,
Temperature 150 °C		9280 psi
@Thickness 0.125 in,
Temperature 302 °F		ASTM D790
 69.0 MPa
@Thickness 1.60 mm,
Temperature 150 °C		10000 psi
@Thickness 0.0630 in,
Temperature 302 °F		ASTM D790
 73.0 MPa
@Thickness 0.800 mm,
Temperature 150 °C		10600 psi
@Thickness 0.0315 in,
Temperature 302 °F		ASTM D790
 78.0 MPa
@Thickness 3.17 mm,
Temperature 120 °C		11300 psi
@Thickness 0.125 in,
Temperature 248 °F		ASTM D790
 174 MPa
@Thickness 3.17 mm,
Temperature 23.0 °C		25200 psi
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D790
 192 MPa
@Thickness 1.60 mm,
Temperature 23.0 °C		27800 psi
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D790
 215 MPa
@Thickness 0.800 mm,
Temperature 23.0 °C		31200 psi
@Thickness 0.0315 in,
Temperature 73.4 °F		ASTM D790
 270 MPa
@Thickness 3.17 mm,
Temperature -40.0 °C		39200 psi
@Thickness 0.125 in,
Temperature -40.0 °F		ASTM D790
 290 MPa
@Thickness 1.60 mm,
Temperature -40.0 °C		42100 psi
@Thickness 0.0630 in,
Temperature -40.0 °F		ASTM D790
 335 MPa
@Thickness 0.800 mm,
Temperature -40.0 °C		48600 psi
@Thickness 0.0315 in,
Temperature -40.0 °F		ASTM D790
Flexural Modulus 13.0 GPa
@Temperature 23.0 °C		1890 ksi
@Temperature 73.4 °F		ISO 178
 3.50 GPa
@Thickness 3.17 mm,
Temperature 250 °C		508 ksi
@Thickness 0.125 in,
Temperature 482 °F		ASTM D790
 4.00 GPa
@Thickness 1.60 mm,
Temperature 250 °C		580 ksi
@Thickness 0.0630 in,
Temperature 482 °F		ASTM D790
 5.00 GPa
@Thickness 0.800 mm,
Temperature 250 °C		725 ksi
@Thickness 0.0315 in,
Temperature 482 °F		ASTM D790
 6.00 GPa
@Thickness 1.60 mm,
Temperature 200 °C		870 ksi
@Thickness 0.0630 in,
Temperature 392 °F		ASTM D790
 6.50 GPa
@Thickness 3.17 mm,
Temperature 200 °C		943 ksi
@Thickness 0.125 in,
Temperature 392 °F		ASTM D790
 8.00 GPa
@Thickness 3.17 mm,
Temperature 120 °C		1160 ksi
@Thickness 0.125 in,
Temperature 248 °F		ASTM D790
 8.00 GPa
@Thickness 3.17 mm,
Temperature 150 °C		1160 ksi
@Thickness 0.125 in,
Temperature 302 °F		ASTM D790
 8.00 GPa
@Thickness 1.60 mm,
Temperature 150 °C		1160 ksi
@Thickness 0.0630 in,
Temperature 302 °F		ASTM D790
 8.00 GPa
@Thickness 0.800 mm,
Temperature 200 °C		1160 ksi
@Thickness 0.0315 in,
Temperature 392 °F		ASTM D790
 9.00 GPa
@Thickness 0.800 mm,
Temperature 150 °C		1310 ksi
@Thickness 0.0315 in,
Temperature 302 °F		ASTM D790
 13.0 GPa
@Thickness 3.17 mm,
Temperature 23.0 °C		1890 ksi
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D790
 14.0 GPa
@Thickness 1.60 mm,
Temperature 23.0 °C		2030 ksi
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D790
 16.0 GPa
@Thickness 3.17 mm,
Temperature -40.0 °C		2320 ksi
@Thickness 0.125 in,
Temperature -40.0 °F		ASTM D790
 16.0 GPa
@Thickness 1.60 mm,
Temperature -40.0 °C		2320 ksi
@Thickness 0.0630 in,
Temperature -40.0 °F		ASTM D790
 18.0 GPa
@Thickness 0.800 mm,
Temperature 23.0 °C		2610 ksi
@Thickness 0.0315 in,
Temperature 73.4 °F		ASTM D790
 22.0 GPa
@Thickness 0.800 mm,
Temperature -40.0 °C		3190 ksi
@Thickness 0.0315 in,
Temperature -40.0 °F		ASTM D790
Compressive Strength 89.0 MPa12900 psiASTM D 695
Shear Strength  57.0 MPa
@Thickness 0.800 mm		8270 psi
@Thickness 0.0315 in		ASTM D732
 58.0 MPa
@Thickness 3.17 mm		8410 psi
@Thickness 0.125 in		ASTM D732
Izod Impact, Notched  1.70 J/cm
@Thickness 1.60 mm,
Temperature 23.0 °C		3.18 ft-lb/in
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D256
 1.85 J/cm
@Thickness 3.17 mm,
Temperature -40.0 °C		3.47 ft-lb/in
@Thickness 0.125 in,
Temperature -40.0 °F		ASTM D256
 1.90 J/cm
@Thickness 1.60 mm,
Temperature -40.0 °C		3.56 ft-lb/in
@Thickness 0.0630 in,
Temperature -40.0 °F		ASTM D256
 2.25 J/cm
@Thickness 3.17 mm,
Temperature 23.0 °C		4.22 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D256
 4.00 J/cm
@Thickness 0.800 mm,
Temperature 23.0 °C		7.49 ft-lb/in
@Thickness 0.0315 in,
Temperature 73.4 °F		40%NB; ASTM D256
 4.90 J/cm
@Thickness 0.800 mm,
Temperature -40.0 °C		9.18 ft-lb/in
@Thickness 0.0315 in,
Temperature -40.0 °F		40%NB; ASTM D256
Izod Impact, Unnotched  5.55 J/cm
@Thickness 3.17 mm,
Temperature -40.0 °C		10.4 ft-lb/in
@Thickness 0.125 in,
Temperature -40.0 °F		ASTM D4812
 7.40 J/cm
@Thickness 3.17 mm,
Temperature 23.0 °C		13.9 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F		ASTM D4812
 8.40 J/cm
@Thickness 1.60 mm,
Temperature 23.0 °C		15.7 ft-lb/in
@Thickness 0.0630 in,
Temperature 73.4 °F		ASTM D4812
 470 J/cm
@Thickness 0.800 mm,
Temperature -40.0 °C		881 ft-lb/in
@Thickness 0.0315 in,
Temperature -40.0 °F		ASTM D4812
 475 J/cm
@Thickness 1.60 mm,
Temperature -40.0 °C		890 ft-lb/in
@Thickness 0.0630 in,
Temperature -40.0 °F		ASTM D4812
 NB
@Thickness 0.800 mm,
Temperature 23.0 °C		NB
@Thickness 0.0315 in,
Temperature 73.4 °F		ASTM D4812
Izod Impact, Notched (ISO) 18.0 kJ/m²
@Temperature 23.0 °C		8.57 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
@Temperature 23.0 °C		14.3 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched  2.20 J/cm²
@Temperature -30.0 °C		10.5 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 3.00 J/cm²
@Temperature 23.0 °C		14.3 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  2.00 J/cm²
@Temperature -30.0 °C		9.52 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 2.00 J/cm²
@Temperature 23.0 °C		9.52 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+16 ohm-cm1.00e+16 ohm-cmASTM D 257
Surface Resistance 1.00e+15 ohm1.00e+15 ohmASTM D 257
Dielectric Constant  3.5
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.5
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 150
 3.8
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.8
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 3.9
@Frequency 1000 Hz,
Temperature 23.0 °C		3.9
@Frequency 1000 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 150
 4.3
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		4.3
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		1.6mm (0.062in); ASTM D 2520 B
 4.3
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		4.3
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 2520 B
 4.3
@Frequency 1000 Hz,
Temperature 23.0 °C		4.3
@Frequency 1000 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 4.3
@Frequency 1.00e+6 Hz,
Temperature 120 °C		4.3
@Frequency 1.00e+6 Hz,
Temperature 248 °F		0.8mm (0.031in); ASTM D 150
 4.4
@Frequency 1.00e+9 Hz,
Temperature 150 °C		4.4
@Frequency 1.00e+9 Hz,
Temperature 302 °F		0.8mm (0.031in); ASTM D 2520 B
 4.4
@Frequency 1.00e+9 Hz,
Temperature 150 °C		4.4
@Frequency 1.00e+9 Hz,
Temperature 302 °F		1.6mm (0.062in); ASTM D 2520 B
 4.4
@Frequency 1.00e+9 Hz,
Temperature 150 °C		4.4
@Frequency 1.00e+9 Hz,
Temperature 302 °F		3.2mm (0.125in); ASTM D 2520 B
 4.4
@Frequency 1.00e+6 Hz,
Temperature 150 °C		4.4
@Frequency 1.00e+6 Hz,
Temperature 302 °F		0.8mm (0.031in); ASTM D 150
 4.4
@Frequency 1.00e+9 Hz,
Temperature 120 °C		4.4
@Frequency 1.00e+9 Hz,
Temperature 248 °F		0.8mm (0.031in); ASTM D 2520 B
 4.4
@Frequency 1.00e+9 Hz,
Temperature 120 °C		4.4
@Frequency 1.00e+9 Hz,
Temperature 248 °F		1.6mm (0.062in); ASTM D 2520 B
 4.4
@Frequency 1.00e+9 Hz,
Temperature 120 °C		4.4
@Frequency 1.00e+9 Hz,
Temperature 248 °F		3.2mm (0.125in); ASTM D 2520 B
 4.4
@Frequency 1.00e+6 Hz,
Temperature 200 °C		4.4
@Frequency 1.00e+6 Hz,
Temperature 392 °F		0.8mm (0.031in); ASTM D 150
 4.4
@Frequency 1000 Hz,
Temperature 120 °C		4.4
@Frequency 1000 Hz,
Temperature 248 °F		0.8mm (0.031in); ASTM D 150
 4.4
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		4.4
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 2520 B
 4.4
@Frequency 1000 Hz,
Temperature 200 °C		4.4
@Frequency 1000 Hz,
Temperature 392 °F		0.8mm (0.031in); ASTM D 150
 4.5
@Frequency 1000 Hz,
Temperature 150 °C		4.5
@Frequency 1000 Hz,
Temperature 302 °F		0.8mm (0.031in); ASTM D 150
 4.5
@Frequency 1.00e+6 Hz,
Temperature 120 °C		4.5
@Frequency 1.00e+6 Hz,
Temperature 248 °F		3.2mm (0.125in); ASTM D 150
 4.7
@Frequency 1.00e+9 Hz,
Temperature 200 °C		4.7
@Frequency 1.00e+9 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 2520 B
 4.7
@Frequency 1.00e+9 Hz,
Temperature 200 °C		4.7
@Frequency 1.00e+9 Hz,
Temperature 392 °F		1.6mm (0.062in); ASTM D 2520 B
 4.8
@Frequency 1.00e+9 Hz,
Temperature 200 °C		4.8
@Frequency 1.00e+9 Hz,
Temperature 392 °F		0.8mm (0.031in); ASTM D 2520 B
 4.8
@Frequency 1.00e+6 Hz,
Temperature 150 °C		4.8
@Frequency 1.00e+6 Hz,
Temperature 302 °F		3.2mm (0.125in); ASTM D 150
 4.9
@Frequency 1000 Hz,
Temperature 120 °C		4.9
@Frequency 1000 Hz,
Temperature 248 °F		3.2mm (0.125in); ASTM D 150
 4.9
@Frequency 1.00e+6 Hz,
Temperature 200 °C		4.9
@Frequency 1.00e+6 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 150
 5.0
@Frequency 1000 Hz,
Temperature 200 °C		5.0
@Frequency 1000 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 150
 5.0
@Frequency 1000 Hz,
Temperature 150 °C		5.0
@Frequency 1000 Hz,
Temperature 302 °F		3.2mm (0.125in); ASTM D 150
Dielectric Strength  >= 26.0 kV/mm
@Thickness 3.20 mm,
Temperature 150 °C		>= 660 kV/in
@Thickness 0.126 in,
Temperature 302 °F		Short time; ASTM D149
 >= 27.0 kV/mm
@Thickness 3.20 mm,
Temperature 200 °C		>= 686 kV/in
@Thickness 0.126 in,
Temperature 392 °F		Short time; ASTM D149
 >= 28.0 kV/mm
@Thickness 3.20 mm,
Temperature 120 °C		>= 711 kV/in
@Thickness 0.126 in,
Temperature 248 °F		Short time; ASTM D149
 >= 28.0 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		>= 711 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		Short time; ASTM D149
 34.0 kV/mm
@Thickness 1.60 mm,
Temperature 120 °C		864 kV/in
@Thickness 0.0630 in,
Temperature 248 °F		Short time; ASTM D149
 35.0 kV/mm
@Thickness 1.60 mm,
Temperature 23.0 °C		889 kV/in
@Thickness 0.0630 in,
Temperature 73.4 °F		Short time; ASTM D149
 35.0 kV/mm
@Thickness 1.60 mm,
Temperature 200 °C		889 kV/in
@Thickness 0.0630 in,
Temperature 392 °F		Short time; ASTM D149
 36.0 kV/mm
@Thickness 1.60 mm,
Temperature 150 °C		914 kV/in
@Thickness 0.0630 in,
Temperature 302 °F		Short time; ASTM D149
Dissipation Factor  0.0040
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		0.0040
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 2520 B
 0.0040
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		0.0040
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		1.6mm (0.062in); ASTM D 2520 B
 0.0040
@Frequency 1.00e+9 Hz,
Temperature 23.0 °C		0.0040
@Frequency 1.00e+9 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 2520 B
 0.0060
@Frequency 1000 Hz,
Temperature 150 °C		0.0060
@Frequency 1000 Hz,
Temperature 302 °F		3.2mm (0.125in); ASTM D 150
 0.0060
@Frequency 1000 Hz,
Temperature 120 °C		0.0060
@Frequency 1000 Hz,
Temperature 248 °F		3.2mm (0.125in); ASTM D 150
 0.0070
@Frequency 1000 Hz,
Temperature 120 °C		0.0070
@Frequency 1000 Hz,
Temperature 248 °F		0.8mm (0.031in); ASTM D 150
 0.0070
@Frequency 1000 Hz,
Temperature 150 °C		0.0070
@Frequency 1000 Hz,
Temperature 302 °F		0.8mm (0.031in); ASTM D 150
 0.0090
@Frequency 1.00e+6 Hz,
Temperature 200 °C		0.0090
@Frequency 1.00e+6 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 150
 0.0090
@Frequency 1.00e+6 Hz,
Temperature 200 °C		0.0090
@Frequency 1.00e+6 Hz,
Temperature 392 °F		0.8mm (0.031in); ASTM D 150
 0.012
@Frequency 1000 Hz,
Temperature 200 °C		0.012
@Frequency 1000 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 150
 0.012
@Frequency 1000 Hz,
Temperature 200 °C		0.012
@Frequency 1000 Hz,
Temperature 392 °F		0.8mm (0.031in); ASTM D 150
 0.013
@Frequency 1000 Hz,
Temperature 23.0 °C		0.013
@Frequency 1000 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 0.013
@Frequency 1000 Hz,
Temperature 23.0 °C		0.013
@Frequency 1000 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 150
 0.013
@Frequency 1.00e+9 Hz,
Temperature 120 °C		0.013
@Frequency 1.00e+9 Hz,
Temperature 248 °F		0.8mm (0.031in); ASTM D 2520 B
 0.014
@Frequency 1.00e+9 Hz,
Temperature 120 °C		0.014
@Frequency 1.00e+9 Hz,
Temperature 248 °F		1.6mm (0.062in); ASTM D 2520 B
 0.014
@Frequency 1.00e+6 Hz,
Temperature 150 °C		0.014
@Frequency 1.00e+6 Hz,
Temperature 302 °F		3.2mm (0.125in); ASTM D 150
 0.015
@Frequency 1.00e+6 Hz,
Temperature 150 °C		0.015
@Frequency 1.00e+6 Hz,
Temperature 302 °F		0.8mm (0.031in); ASTM D 150
 0.016
@Frequency 1.00e+9 Hz,
Temperature 120 °C		0.016
@Frequency 1.00e+9 Hz,
Temperature 248 °F		3.2mm (0.125in); ASTM D 2520 B
 0.019
@Frequency 1.00e+9 Hz,
Temperature 150 °C		0.019
@Frequency 1.00e+9 Hz,
Temperature 302 °F		0.8mm (0.031in); ASTM D 2520 B
 0.020
@Frequency 1.00e+9 Hz,
Temperature 150 °C		0.020
@Frequency 1.00e+9 Hz,
Temperature 302 °F		1.6mm (0.062in); ASTM D 2520 B
 0.022
@Frequency 1.00e+9 Hz,
Temperature 150 °C		0.022
@Frequency 1.00e+9 Hz,
Temperature 302 °F		3.2mm (0.125in); ASTM D 2520 B
 0.026
@Frequency 1.00e+9 Hz,
Temperature 200 °C		0.026
@Frequency 1.00e+9 Hz,
Temperature 392 °F		0.8mm (0.031in); ASTM D 2520 B
 0.028
@Frequency 1.00e+9 Hz,
Temperature 200 °C		0.028
@Frequency 1.00e+9 Hz,
Temperature 392 °F		1.6mm (0.062in); ASTM D 2520 B
 0.029
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.029
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		3.2mm (0.125in); ASTM D 150
 0.029
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.029
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		0.8mm (0.031in); ASTM D 150
 0.030
@Frequency 1.00e+6 Hz,
Temperature 120 °C		0.030
@Frequency 1.00e+6 Hz,
Temperature 248 °F		0.8mm (0.031in); ASTM D 150
 0.030
@Frequency 1.00e+9 Hz,
Temperature 200 °C		0.030
@Frequency 1.00e+9 Hz,
Temperature 392 °F		3.2mm (0.125in); ASTM D 2520 B
 0.034
@Frequency 1.00e+6 Hz,
Temperature 120 °C		0.034
@Frequency 1.00e+6 Hz,
Temperature 248 °F		3.2mm (0.125in); ASTM D 150
Comparative Tracking Index 100 - 174 V100 - 174 VUL 746A
 200 V200 VIEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear  -1.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 160 - 260 °C		-0.556 µin/in-°F
@Thickness 0.0787 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 0.000 µm/m-°C
@Thickness 4.00 mm,
Temperature 160 - 260 °C		0.000 µin/in-°F
@Thickness 0.157 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 1.00 µm/m-°C
@Thickness 2.00 mm,
Temperature -40.0 - 260 °C		0.556 µin/in-°F
@Thickness 0.0787 in,
Temperature -40.0 - 500 °F		ISO 11359-1/-2
 2.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		1.11 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 2.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 55.0 - 160 °C		1.11 µin/in-°F
@Thickness 0.0787 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 2.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 55.0 - 160 °C		1.11 µin/in-°F
@Thickness 0.157 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 2.00 µm/m-°C
@Thickness 2.00 mm,
Temperature -40.0 - 23.0 °C		1.11 µin/in-°F
@Thickness 0.0787 in,
Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 2.00 µm/m-°C
@Thickness 4.00 mm,
Temperature -40.0 - 23.0 °C		1.11 µin/in-°F
@Thickness 0.157 in,
Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 2.00 µm/m-°C
@Thickness 4.00 mm,
Temperature -40.0 - 260 °C		1.11 µin/in-°F
@Thickness 0.157 in,
Temperature -40.0 - 500 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C		1.67 µin/in-°F
@Thickness 0.157 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 4.00 µm/m-°C
@Thickness 1.60 mm,
Temperature 23.0 - 150 °C		2.22 µin/in-°F
@Thickness 0.0630 in,
Temperature 73.4 - 302 °F		ASTM E 228
 14.0 µm/m-°C
@Thickness 3.17 mm,
Temperature 23.0 - 150 °C		7.78 µin/in-°F
@Thickness 0.125 in,
Temperature 73.4 - 302 °F		ASTM E 228
CTE, linear, Transverse to Flow  54.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		30.0 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2; 4mm
 58.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		32.2 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2; 2mm
 79.0 µm/m-°C
@Temperature -40.0 - 260 °C		43.9 µin/in-°F
@Temperature -40.0 - 500 °F		ISO 11359-1/-2; 4mm
 82.0 µm/m-°C
@Temperature -40.0 - 260 °C		45.6 µin/in-°F
@Temperature -40.0 - 500 °F		ISO 11359-1/-2; 2mm
 36.0 µm/m-°C
@Thickness 3.17 mm,
Temperature 23.0 - 150 °C		20.0 µin/in-°F
@Thickness 0.125 in,
Temperature 73.4 - 302 °F		ASTM E 228
 43.0 µm/m-°C
@Thickness 1.60 mm,
Temperature 23.0 - 150 °C		23.9 µin/in-°F
@Thickness 0.0630 in,
Temperature 73.4 - 302 °F		ASTM E 228
 62.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C		34.4 µin/in-°F
@Thickness 0.157 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 66.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		36.7 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 80.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 55.0 - 160 °C		44.4 µin/in-°F
@Thickness 0.157 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 85.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 55.0 - 160 °C		47.2 µin/in-°F
@Thickness 0.0787 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 94.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 160 - 260 °C		52.2 µin/in-°F
@Thickness 0.157 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 99.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 160 - 260 °C		55.0 µin/in-°F
@Thickness 0.0787 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
Melting Point 352 °C666 °FASTM D 3418
 352 °C666 °F10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 295 °C563 °FASTM D 648
 310 °C590 °FISO 75-1/-2 1993/N2
Glass Transition Temp, Tg 120 °C248 °FASTM D 3418
UL RTI, Electrical  240 °C
@Thickness 1.50 mm		464 °F
@Thickness 0.0591 in		UL 746B
 240 °C
@Thickness 0.750 mm		464 °F
@Thickness 0.0295 in		UL 746B
 240 °C
@Thickness 3.00 mm		464 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical with Impact  210 °C
@Thickness 1.50 mm		410 °F
@Thickness 0.0591 in		UL 746B
 210 °C
@Thickness 0.750 mm		410 °F
@Thickness 0.0295 in		UL 746B
 210 °C
@Thickness 3.00 mm		410 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical without Impact  240 °C
@Thickness 1.50 mm		464 °F
@Thickness 0.0591 in		UL 746B
 240 °C
@Thickness 0.750 mm		464 °F
@Thickness 0.0295 in		UL 746B
 240 °C
@Thickness 3.00 mm		464 °F
@Thickness 0.118 in		UL 746B
Flammability, UL94  V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		IEC 60695-11-10
 V-0
@Thickness 0.750 mm		V-0
@Thickness 0.0295 in		IEC 60695-11-10
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		UL94
 V-0
@Thickness 0.750 mm		V-0
@Thickness 0.0295 in		UL94
 V-0
@Thickness 0.400 mm		V-0
@Thickness 0.0157 in		IEC 60695-11-10
 V-0
@Thickness 0.400 mm		V-0
@Thickness 0.0157 in		UL94
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		IEC 60695-11-10
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		UL94
Oxygen Index 39 %
@Thickness 3.17 mm		39 %
@Thickness 0.125 in		ASTM D2863
 
Processing PropertiesMetricEnglishComments
Melt Temperature 365 °C689 °FOptimum
 360 - 370 °C680 - 698 °F
Mold Temperature 80.0 °C176 °FOptimum
 40.0 - 150 °C104 - 302 °F
Drying Temperature 150 °C302 °F
Dry Time 3 hour3 hourDehumidified Dryer
Moisture Content <= 0.010 %<= 0.010 %
 
Descriptive Properties
ColorCream
Drying RecommendedYes
FeaturesAppearance, Pleasing Surface
 Arc Resistant
 Aromatic
 Chemical Resistance, Good
 Dimensional Stability, Good
 Flow, Good
 Heat Aging Resistance, Good
 Moisture Absorption, Low
 Platable
 Platable
FillerGlass fiber reinforcement
Flame Retardant - Halogen/Red Phosphorus FreeYes
FormsPellets
GenericLCP
Part Marking Code>LCP-GF30<ISO 11469
Polymer FamilyLCP
Polymer TypeLCP
ProcessingInjection Moldable
Processing MethodInjection Molding
Product CategoryElectrical Resins
 Flame Retardant Resins
 Glass Reinforced Resins
Region AvailableAmericas
 Asia/Pacific
 Europe
Resin IdentificationLCP-GF30ISO 1043
UsesAutomotive Applications
 Automotive Electronics
 Automotive, Under the Hood
 Communication Applications
 Computer Components
 Connectors
 Electrical/Electronic Applications
 Parts, Engineering
 Parts, Thin-walled
 Printer Parts

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31783.html

免责声明: 本文 Celanese Zenite® 7130 WT010 LCP 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4