- 密度 [g/cm3]: 1.72
- 弯曲模量 [MPa]: 16.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | ISO 1183 | ||
| Filler Content | 40 % | 40 % | Glass Reinforced | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 177 MPa @Temperature 23.0 °C | 25700 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 1.4 % @Temperature 23.0 °C | 1.4 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 17.0 GPa @Temperature 23.0 °C | 2470 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 250 MPa @Temperature 23.0 °C | 36300 psi @Temperature 73.4 °F | ISO 178 | ||
| Flexural Modulus | 16.0 GPa @Temperature 23.0 °C | 2320 ksi @Temperature 73.4 °F | ISO 178 | ||
| Charpy Impact, Notched | 1.50 J/cm² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | -2.00 µm/m-°C @Temperature 160 - 320 °C | -1.11 µin/in-°F @Temperature 320 - 608 °F | ISO 11359-1/-2 | ||
| 3.00 µm/m-°C @Temperature 55.0 - 160 °C | 1.67 µin/in-°F @Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
| -2.00 µm/m-°C @Thickness 4.00 mm, Temperature 160 - 320 °C | -1.11 µin/in-°F @Thickness 0.157 in, Temperature 320 - 608 °F | ISO 11359-1/-2 | |||
| 2.00 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 23.0 °C | 1.11 µin/in-°F @Thickness 0.157 in, Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | |||
| 2.00 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 320 °C | 1.11 µin/in-°F @Thickness 0.157 in, Temperature -40.0 - 608 °F | ISO 11359-1/-2 | |||
| 2.00 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 1.11 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
| 2.00 µm/m-°C @Thickness 2.00 mm, Temperature -40.0 - 23.0 °C | 1.11 µin/in-°F @Thickness 0.0787 in, Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | |||
| 2.00 µm/m-°C @Thickness 2.00 mm, Temperature -40.0 - 320 °C | 1.11 µin/in-°F @Thickness 0.0787 in, Temperature -40.0 - 608 °F | ISO 11359-1/-2 | |||
| 3.00 µm/m-°C @Thickness 4.00 mm, Temperature 23.0 - 55.0 °C | 1.67 µin/in-°F @Thickness 0.157 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
| 4.00 µm/m-°C @Thickness 4.00 mm, Temperature 55.0 - 160 °C | 2.22 µin/in-°F @Thickness 0.157 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 48.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 26.7 µin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | ||
| 55.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 30.6 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
| 71.0 µm/m-°C @Temperature 55.0 - 160 °C | 39.4 µin/in-°F @Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
| 74.0 µm/m-°C @Temperature -40.0 - 320 °C | 41.1 µin/in-°F @Temperature -40.0 - 608 °F | ISO 11359-1/-2 | |||
| 88.0 µm/m-°C @Temperature 160 - 320 °C | 48.9 µin/in-°F @Temperature 320 - 608 °F | ISO 11359-1/-2 | |||
| 48.0 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 23.0 °C | 26.7 µin/in-°F @Thickness 0.157 in, Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | |||
| 55.0 µm/m-°C @Thickness 4.00 mm, Temperature 23.0 - 55.0 °C | 30.6 µin/in-°F @Thickness 0.157 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
| 71.0 µm/m-°C @Thickness 4.00 mm, Temperature 55.0 - 160 °C | 39.4 µin/in-°F @Thickness 0.157 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
| 75.0 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 320 °C | 41.7 µin/in-°F @Thickness 0.157 in, Temperature -40.0 - 608 °F | ISO 11359-1/-2 | |||
| 92.0 µm/m-°C @Thickness 4.00 mm, Temperature 160 - 320 °C | 51.1 µin/in-°F @Thickness 0.157 in, Temperature 320 - 608 °F | ISO 11359-1/-2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 356 °C | 673 °F | ISO 75-1/-2 1993/N2 | ||
| UL RTI, Electrical | 130 °C @Thickness 0.300 mm | 266 °F @Thickness 0.0118 in | UL 746B | ||
| 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL 746B | |||
| UL RTI, Mechanical with Impact | 130 °C @Thickness 0.300 mm | 266 °F @Thickness 0.0118 in | UL 746B | ||
| 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL 746B | |||
| UL RTI, Mechanical without Impact | 130 °C @Thickness 0.300 mm | 266 °F @Thickness 0.0118 in | UL 746B | ||
| 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL 746B | |||
| Flammability, UL94 | V-0 @Thickness 0.300 mm | V-0 @Thickness 0.0118 in | IEC 60695-11-10 | ||
| V-0 @Thickness 0.300 mm | V-0 @Thickness 0.0118 in | UL94 | |||
| V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | IEC 60695-11-10 | |||
| V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 380 °C | 716 °F | Optimum | ||
| 375 - 385 °C | 707 - 725 °F | ||||
| Mold Temperature | 80.0 °C | 176 °F | Optimum | ||
| 40.0 - 150 °C | 104 - 302 °F | ||||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 3 hour | 3 hour | Dehumidified Dryer | ||
| Moisture Content | <= 0.010 % | <= 0.010 % | |||
| Descriptive Properties | |||||
| Appearance | Black | ||||
| DuPont Product Category | Electrical Resins | ||||
| Flame Retardant Resins | |||||
| Glass Reinforced Resins | |||||
| Form | Pellets | ||||
| Part Marking Code | >LCP-GF40< | ISO 11469 | |||
| Region | Americas | ||||
| Asia/Pacific | |||||
| Europe | |||||
| Resin Identification | LCP-GF40 | ISO 1043 | |||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.