- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.27
- 拉伸强度 [MPa]: 82.7
- 弯曲模量 [MPa]: 16.5
- 热变形温度 [℃]: 282.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.82 g/cc | 1.82 g/cc | ASTM D792 | ||
| Water Absorption | 0.010 % @Thickness 3.18 mm | 0.010 % @Thickness 0.125 in | @ 24 hrs; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 82.7 MPa | 12000 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 0.50 % | 0.50 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 20.7 GPa | 3000 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 103 MPa | 14900 psi | ASTM D790 | ||
| Flexural Modulus | 16.5 GPa | 2390 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.270 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 0.506 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.0 - 10 ohm-cm | 1.0 - 10 ohm-cm | ASTM D257 | ||
| Surface Resistance | 1.0 - 10 ohm | 1.0 - 10 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 19.0 W/m-K | 132 BTU-in/hr-ft²-°F | ASTM C177 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 282 °C @Thickness 6.35 mm | 540 °F @Thickness 0.250 in | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C @Thickness 6.35 mm | 531 °F @Thickness 0.250 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 316 - 341 °C | 601 - 646 °F | |||
| Mold Temperature | 93.3 - 121 °C | 200 - 250 °F | |||
| Descriptive Properties | |||||
| Features | Electrically Conductive | ||||
| Thermally Conductive | |||||
| Forms | Pellets | ||||
| Generic Material | LCP | ||||
| Generic Name | Liquid Crystal Polymer (LCP) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Uses | Automotive Applications | ||||
| Automotive Under the Hood | |||||
| Consumer Applications | |||||
| Electrical/Electronic Applications | |||||
| Housings | |||||
| Industrial Applications | |||||