- 密度 [g/cm3]: 1.67
- 吸水率 [%]: 0.07
- 缺口冲击强度: 30.0
- 弯曲模量 [MPa]: 17.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.0700 % | 0.0700 % | ISO 62 | ||
| Linear Mold Shrinkage, Transverse | 0.00290 cm/cm | 0.00290 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 62.0 | 62.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 150 MPa | 21800 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 1.50 % | 1.50 % | 5mm/min; ISO 527-2/1A | ||
| 2.10 % | 2.10 % | Flexural strain; ISO 178 | |||
| Tensile Modulus | 16.0 GPa | 2320 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 225 MPa | 32600 psi | ISO 178 | ||
| Flexural Modulus | 17.0 GPa | 2470 ksi | ISO 178 | ||
| Compressive Strength | 100 MPa | 14500 psi | 1% strain; ISO 604 | ||
| Compressive Modulus | 13.5 GPa | 1960 ksi | ISO 604 | ||
| Izod Impact, Notched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | ISO 180/1U | ||
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 2.70 J/cm² | 12.8 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 4.10 @Frequency 1.00e+6 Hz | 4.10 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.37 @Frequency 2.05e+9 Hz | 4.37 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 | |||
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00300 @Frequency 1.00e+6 Hz | 0.00300 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 0.00600 @Frequency 2.05e+9 Hz | 0.00600 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 | |||
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 5.00 µm/m-°C | 2.78 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 59.0 µm/m-°C | 32.8 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 275 °C | 527 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 200 °C | 392 °F | B50 (50°C/h 50N); ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | ||
| Zone 1 | 315 - 335 °C | 599 - 635 °F | |||
| Zone 2 | 320 - 345 °C | 608 - 653 °F | |||
| Zone 3 | 325 - 355 °C | 617 - 671 °F | |||
| Zone 4 | 330 - 360 °C | 626 - 680 °F | |||
| Die Temperature | 335 - 350 °C | 635 - 662 °F | |||
| Melt Temperature | 335 - 355 °C | 635 - 671 °F | |||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Dew Point | <= -40.0 °C | <= -40.0 °F | Pre-drying | ||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Screw Speed | 80.0 rpm @Diameter 40.0 mm | 80.0 rpm @Diameter 1.57 in | |||
| 140 rpm @Diameter 25.0 mm | 140 rpm @Diameter 0.984 in | ||||
| 200 rpm @Diameter 16.0 mm | 200 rpm @Diameter 0.630 in | ||||
| Descriptive Properties | |||||
| Injection speed | very fast | ||||