- 吸水率 [%]: 0.02
- 缺口冲击强度: 1.28
- 拉伸强度 [MPa]: 159.0
- 弯曲模量 [MPa]: 13.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.61 g/cc | 1.61 g/cc | ASTM D792 | ||
| Water Absorption | 0.020 % @Thickness 3.17 mm | 0.020 % @Thickness 0.125 in | 24 hr. Immersion; ASTM D570 | ||
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 159 MPa | 23000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Tensile Modulus | 14.5 GPa | 2100 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Flexural Strength | 214 MPa | 31000 psi | ASTM D790 | ||
| Flexural Modulus | 13.1 GPa | 1900 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.28 J/cm | 2.40 ft-lb/in | Method A, Injection Molded, 0.125 in bars, 73°F; ASTM D648 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C | 470 °F | Unannealed, 0.125 in bars; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | Molding | ||
| Descriptive Properties | |||||
| Processing Method | Injection Molding | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.