- 密度 [g/cm3]: 1.6
- 缺口冲击强度: 0.9
- 弯曲强度 [MPa]: 130.0
- 弯曲模量 [MPa]: 14.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | LATI | ||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | LATI | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527 | ||
| Flexural Modulus | 14.0 GPa | 2030 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.900 J/cm @Temperature 23.0 °C | 1.69 ft-lb/in @Temperature 73.4 °F | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 38.0 kV/mm @Thickness 2.00 mm | 965 kV/in @Thickness 0.0787 in | IEC 243-1 | ||
| Comparative Tracking Index | 185 V | 185 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | ASTM D648 | ||
| Flammability, UL94 | V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 320 - 360 °C | 608 - 680 °F | |||
| Mold Temperature | 65.0 - 95.0 °C | 149 - 203 °F | |||
| Drying Temperature | 150 °C | 302 °F | Use a desiccant-type hopper dryer. For tray drying, pellets should be dried in 2.5-5 mm deep layer for 8 hours. | ||
| Dry Time | 6 - 8 hour | 6 - 8 hour | |||
| Descriptive Properties | |||||
| Injection Speed | high | ||||