- 密度 [g/cm3]: 1.4
- 缺口冲击强度: 95.0
- 弯曲模量 [MPa]: 9.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.020 % | 0.020 % | at 50% RH; ISO 62 |
| Moisture Vapor Transmission | 0.00606 cc-mm/m²-24hr-atm | 0.0154 cc-mil/100 in²-24hr-atm | at 38°C; DIN 53122-2 |
| Oxygen Transmission | 0.0154 cc-mm/m²-24hr-atm | 0.0390 cc-mil/100 in²-24hr-atm | 73°F, 100%RH; DIN 53380 part 3 |
| 0.0165 cc-mm/m²-24hr-atm | 0.0420 cc-mil/100 in²-24hr-atm | 73°F, 0% RH; DIN 53380 part 3 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 182 MPa | 26400 psi | 5 mm/min; ISO 527-2/1A |
| Elongation at Break | 3.4 % | 3.4 % | 5 mm/min; ISO 527-2/1A |
| Tensile Modulus | 10.6 GPa | 1540 ksi | 1 mm/min; ISO 527-2/1A |
| Flexural Strength | 158 MPa | 22900 psi | ISO 178 |
| Flexural Modulus | 9.10 GPa | 1320 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 95.0 kJ/m² | 45.2 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 252 kJ/m² | 120 ft-lb/in² | ISO 180/1U |
| Charpy Impact Unnotched | 26.7 J/cm² | 127 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 9.50 J/cm² | 45.2 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 280 °C | 536 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 187 °C | 369 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 94.0 °C | 201 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 245 - 255 °C | 473 - 491 °F | |
| Middle Barrel Temperature | 265 - 275 °C | 509 - 527 °F | |
| Front Barrel Temperature | 285 - 295 °C | 545 - 563 °F | |
| Die Temperature | 285 - 295 °C | 545 - 563 °F | |
| Melt Temperature | 285 - 295 °C | 545 - 563 °F | |