Idemitsu Kosan Xarec EA 528 SPS, 30% Glass Filled

Idemitsu Kosan Xarec EA 528 SPS, 30% Glass Filled 物性表: Idemitsu Kosan Xarec EA 528 SPS, 30% Glass Filled物性表及特性介绍,Idemitsu Kosan Xarec EA 528 SPS, 30% Glass Filled注塑参数详情,如需Idemitsu Kosan Xarec EA 528 SPS, 30% Glass Filled下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.39
  • 吸水率 [%]: 0.09
  • 缺口冲击强度: 12.0
  • 拉伸强度 [MPa]: 120.0
  • 弯曲模量 [MPa]: 10.4
  • 热变形温度 [℃]: 255.0
 
Physical PropertiesMetricEnglishComments
Density 1.39 g/cc0.0502 lb/in³ISO 1183 B
Filler Content 30 %30 %Glass
Water Absorption 0.090 %0.090 %24 hours
Linear Mold Shrinkage 0.0015 - 0.0030 cm/cm
@Thickness 2.00 mm
0.0015 - 0.0030 in/in
@Thickness 0.0787 in
ISO 294
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm
@Thickness 2.00 mm
0.0070 - 0.0090 in/in
@Thickness 0.0787 in
ISO 294
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Yield 120 MPa17400 psiISO 527
Elongation at Break 2.0 %2.0 %ISO 527
Tensile Modulus 9.00 GPa1310 ksiISO 527
Flexural Strength 190 MPa27600 psiISO 178
Flexural Modulus 10.4 GPa1510 ksiISO 178
Izod Impact, Notched (ISO) 12.0 kJ/m²
@Temperature 23.0 °C
5.71 ft-lb/in²
@Temperature 73.4 °F
ISO 180/1A
Izod Impact, Unnotched (ISO) 50.0 kJ/m²23.8 ft-lb/in²ISO 180/1U
Charpy Impact Unnotched 3.90 J/cm²
@Temperature 23.0 °C
18.6 ft-lb/in²
@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 0.900 J/cm²
@Temperature 23.0 °C
4.28 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.30e+18 ohm-cm1.30e+18 ohm-cmASTM D257
Dielectric Constant 3.2
@Frequency 1e+6 Hz
3.2
@Frequency 1e+6 Hz
ASTM D150
Dielectric Strength 31.0 kV/mm
@Thickness 0.800 mm
787 kV/in
@Thickness 0.0315 in
ASTM D149
Dissipation Factor 0.0020
@Frequency 1e+6 Hz
0.0020
@Frequency 1e+6 Hz
ASTM D150
Comparative Tracking Index 425 V425 VSolution A; IEC 112
 
Thermal PropertiesMetricEnglishComments
CTE, linear 18.0 µm/m-°C
@Temperature 100 °C
10.0 µin/in-°F
@Temperature 212 °F
Deflection Temperature at 0.46 MPa (66 psi) 255 °C491 °FISO 75B
Deflection Temperature at 1.8 MPa (264 psi) 210 °C410 °FISO 75-2
Vicat Softening Point 255 °C491 °FA/10N; ISO 306
Flammability, UL94 V-0
@Thickness 1.60 mm
V-0
@Thickness 0.0630 in
Oxygen Index 28 %28 %ISO 4589-1984
Glow Wire Test  960 °C
@Thickness 1.00 mm
1760 °F
@Thickness 0.0394 in
IEC 695-2-1
 960 °C
@Thickness 2.00 mm
1760 °F
@Thickness 0.0787 in
IEC 695-2-1
 960 °C
@Thickness 3.00 mm
1760 °F
@Thickness 0.118 in
IEC 695-2-1
 
Processing PropertiesMetricEnglishComments
Melt Temperature 285 - 310 °C545 - 590 °Fpre-drying not required
Mold Temperature 40.0 - 80.0 °C104 - 176 °F
 140 - 155 °C284 - 311 °Ffor optimal gloss and heat resistance

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31998.html

免责声明: 本文 Idemitsu Kosan Xarec EA 528 SPS, 30% Glass Filled 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4