- 密度 [g/cm3]: 1.47
- 缺口冲击强度: 0.8
- 弯曲强度 [MPa]: 115.0
- 弯曲模量 [MPa]: 13.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | LATI | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | LATI | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 115 MPa | 16700 psi | ISO 527 | ||
| Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.800 J/cm @Temperature 23.0 °C | 1.50 ft-lb/in @Temperature 73.4 °F | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 17.0 kV/mm @Thickness 2.00 mm | 432 kV/in @Thickness 0.0787 in | IEC 243-1 | ||
| Comparative Tracking Index | >= 400 V | >= 400 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ASTM D648 | ||
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 300 - 325 °C | 572 - 617 °F | |||
| Mold Temperature | 100 - 150 °C | 212 - 302 °F | |||
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Not essential. Moisture pickup may occur under adverse, high humidity conditions. | ||
| Dry Time | >= 2 hour | >= 2 hour | |||
| Descriptive Properties | |||||
| Injection Speed | high | ||||