- 缺口冲击强度: 0.686
- 拉伸强度 [MPa]: 113.0
- 断裂伸长率 [%]: 186
- 弯曲模量 [MPa]: 9.32
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0090 cm/cm @Thickness 3.20 mm | 0.0030 - 0.0090 in/in @Thickness 0.126 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 113 MPa @Thickness 3.20 mm | 16400 psi @Thickness 0.126 in | 5mm/min; ASTM D638 |
| Elongation at Break | 2.0 % @Thickness 3.20 mm | 2.0 % @Thickness 0.126 in | 5mm/min; ASTM D638 |
| Flexural Yield Strength | 186 MPa @Thickness 3.20 mm | 27000 psi @Thickness 0.126 in | 1.3mm/min; ASTM D790 |
| Flexural Modulus | 9.32 GPa @Thickness 3.20 mm | 1350 ksi @Thickness 0.126 in | 1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.686 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 1.29 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 31.0 kV/mm @Thickness 1.00 mm | 787 kV/in @Thickness 0.0394 in | ASTM D149 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | Solution A; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C @Thickness 6.40 mm | 500 °F @Thickness 0.252 in | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 230 °C @Thickness 6.40 mm | >= 446 °F @Thickness 0.252 in | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding |
| Middle Barrel Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Front Barrel Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
| Nozzle Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Mold Temperature | 80.0 - 150 °C | 176 - 302 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 3.00 - 5.00 hour | 3.00 - 5.00 hour | Injection Molding |
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm | Injection Molding |