- 密度 [g/cm3]: 1.26
- 缺口冲击强度: 7.0
- 拉伸强度 [MPa]: 145.0
- 弯曲模量 [MPa]: 7.30
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 B |
| Filler Content | 20 % | 20 % | Glass |
| Moisture Absorption | 0.220 % | 0.220 % | 24 hours, 50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.0025 - 0.0050 cm/cm @Thickness 2.00 mm | 0.0025 - 0.0050 in/in @Thickness 0.0787 in | ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Thickness 2.00 mm | 0.0050 - 0.0080 in/in @Thickness 0.0787 in | ISO 294 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 145 MPa | 21000 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 7.10 GPa | 1030 ksi | ISO 527 |
| Flexural Strength | 215 MPa | 31200 psi | ISO 178 |
| Flexural Modulus | 7.30 GPa | 1060 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 180 |
| Izod Impact, Unnotched (ISO) | 43.0 kJ/m² | 20.5 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 4.90 J/cm² @Temperature 23.0 °C | 23.3 ft-lb/in² @Temperature 73.4 °F | ISO 179 |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 179 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.20e+15 ohm-cm | 1.20e+15 ohm-cm | ISO IEC 60093 |
| Dielectric Constant | 3.1 | 3.1 | ISO IEC 60250 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ISO IEC 60243 |
| Dissipation Factor | 0.034 | 0.034 | ISO IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; ISO IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 36.0 µm/m-°C @Temperature 100 °C | 20.0 µin/in-°F @Temperature 212 °F | ISO 11359 |
| CTE, linear, Transverse to Flow | 69.0 µm/m-°C @Temperature 20.0 °C | 38.3 µin/in-°F @Temperature 68.0 °F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75A |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 290 - 320 °C | 554 - 608 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |