- 熔体流动速率 [g/10min]: 6.0
- 缺口冲击强度: 0.686
- 拉伸强度 [MPa]: 118.0
- 断裂伸长率 [%]: 177
- 弯曲模量 [MPa]: 0.177
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0020 - 0.0080 in/in @Thickness 0.126 in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 290 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 554 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 118 MPa @Thickness 3.20 mm | 17100 psi @Thickness 0.126 in | 5mm/min; ASTM D638 |
| Flexural Yield Strength | 177 MPa @Thickness 6.40 mm | 25600 psi @Thickness 0.252 in | 1.3mm/min; ASTM D790 |
| Flexural Modulus | 0.177 GPa @Thickness 6.40 mm | 25.6 ksi @Thickness 0.252 in | 1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.686 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 1.29 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C @Thickness 6.40 mm | 500 °F @Thickness 0.252 in | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C @Thickness 6.40 mm | 428 °F @Thickness 0.252 in | ASTM D648 |
| UL RTI, Electrical | 125 °C @Thickness >=1.60 mm | 257 °F @Thickness >=0.0630 in | |
| 130 °C @Thickness >=3.00 mm | 266 °F @Thickness >=0.118 in | ||
| UL RTI, Mechanical with Impact | 115 °C @Thickness >=1.60 mm | 239 °F @Thickness >=0.0630 in | |
| 120 °C @Thickness >=3.00 mm | 248 °F @Thickness >=0.118 in | ||
| UL RTI, Mechanical without Impact | 125 °C @Thickness >=1.60 mm | 257 °F @Thickness >=0.0630 in | |
| 130 °C @Thickness >=3.00 mm | 266 °F @Thickness >=0.118 in | ||
| Flammability, UL94 | V-0 @Thickness >=1.60 mm | V-0 @Thickness >=0.0630 in | |
| V-0 @Thickness >=3.00 mm | V-0 @Thickness >=0.118 in | ||
| 5VA @Thickness >=1.60 mm | 5VA @Thickness >=0.0630 in | ||
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 260 - 300 °C | 500 - 572 °F | Injection Molding |
| Middle Barrel Temperature | 270 - 320 °C | 518 - 608 °F | Injection Molding |
| Front Barrel Temperature | 275 - 320 °C | 527 - 608 °F | Injection Molding |
| Nozzle Temperature | 315 °C | 599 °F | Injection Molding |
| Melt Temperature | 315 °C | 599 °F | Resin, Injection Molding |
| Mold Temperature | 80.0 - 130 °C | 176 - 266 °F | Injection Molding |
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | Injection Molding |
| Dry Time | 3.00 - 5.00 hour | 3.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm | Injection Molding |