- 密度 [g/cm3]: 1.33
- 缺口冲击强度: 12.0
- 拉伸强度 [MPa]: 175.0
- 弯曲模量 [MPa]: 8.90
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 B |
| Filler Content | 30 % | 30 % | Glass |
| Moisture Absorption | 0.190 % | 0.190 % | 24 hours, 50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.0015 - 0.0030 cm/cm @Thickness 2.00 mm | 0.0015 - 0.0030 in/in @Thickness 0.0787 in | ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 2.00 mm | 0.0050 - 0.0070 in/in @Thickness 0.0787 in | ISO 294 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 175 MPa | 25400 psi | ISO 527 |
| Elongation at Break | 2.7 % | 2.7 % | ISO 527 |
| Tensile Modulus | 9.90 GPa | 1440 ksi | ISO 527 |
| Flexural Strength | 260 MPa | 37700 psi | ISO 178 |
| Flexural Modulus | 8.90 GPa | 1290 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | ISO 180 |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 6.10 J/cm² @Temperature 23.0 °C | 29.0 ft-lb/in² @Temperature 73.4 °F | ISO 179 |
| Charpy Impact, Notched | 0.970 J/cm² @Temperature 23.0 °C | 4.62 ft-lb/in² @Temperature 73.4 °F | ISO 179 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.60e+15 ohm-cm | 2.60e+15 ohm-cm | ISO IEC 60093 |
| Dielectric Constant | 3.2 | 3.2 | ISO IEC 60250 |
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | ISO IEC 60243 |
| Dissipation Factor | 0.069 | 0.069 | ISO IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; ISO IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 25.0 µm/m-°C @Temperature 100 °C | 13.9 µin/in-°F @Temperature 212 °F | ISO 11359 |
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature 20.0 °C | 34.4 µin/in-°F @Temperature 68.0 °F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75A |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 290 - 320 °C | 554 - 608 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |