| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| 1.21 g/cc | 0.0437 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.080 % | 0.080 % | 23°C / 50% RH; ISO 62 |
| 0.060 % @Time 86400 sec | 0.060 % @Time 24.0 hour | 50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec | 0.0010 - 0.0030 in/in @Time 24.0 hour | ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec | 0.0030 - 0.0050 in/in @Time 24.0 hour | ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D 638 |
| 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.0 % | 1.0 % | Type I, 5 mm/min; ASTM D 638 |
| 1.1 % | 1.1 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 7.97 GPa | 1160 ksi | 1 mm/min; ISO 527 |
| 8.57 GPa | 1240 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 117 MPa | 17000 psi | brk, 1.3 mm/min, 50 mm span; ASTM D 790 |
| 127 MPa | 18400 psi | ISO 178 | |
| Flexural Modulus | 7.45 GPa | 1080 ksi | 2 mm/min; ISO 178 |
| 7.69 GPa | 1120 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.460 J/cm @Temperature 23.0 °C | 0.862 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 3.13 J/cm @Temperature 23.0 °C | 5.86 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m² @Temperature 23.0 °C | 8.09 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 3.00 J @Temperature 23.0 °C | 2.21 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 39.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 21.7 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| CTE, linear, Transverse to Flow | 48.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 26.7 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 247 °C @Thickness 3.20 mm | 477 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 129 °C @Thickness 3.20 mm | 264 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |