- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 0.009
- 缺口冲击强度: 1.12
- 拉伸强度 [MPa]: 121.0
- 断裂伸长率 [%]: 224
- 弯曲模量 [MPa]: 11.9
- 硬度: 120.0
- 热变形温度 [℃]: 243.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| Water Absorption | 0.0090 % @Time 86400 sec | 0.0090 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm | 0.0030 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 121 MPa | 17500 psi | ASTM D638 |
| Elongation at Break | 1.1 % | 1.1 % | ASTM D638 |
| Flexural Yield Strength | 224 MPa | 32500 psi | ASTM D790 |
| Flexural Modulus | 11.9 GPa | 1720 ksi | ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm @Thickness 3.17 mm | 2.10 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 13.3 J/cm @Thickness 3.17 mm | 25.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 23.6 kV/mm | 600 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 16.2 µm/m-°C | 9.00 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 470 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 263 °C | 505 °F | Unannealed; ASTM D648 |