- 密度 [g/cm3]: 1.0
- 弯曲模量 [MPa]: 1.70
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | |||
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Elongation at Break | 13 % | 13 % | |||
| Flexural Modulus | 1.70 GPa @Temperature 130 °C | 247 ksi @Temperature 266 °F | |||
| 2.40 GPa @Temperature 40.0 °C | 348 ksi @Temperature 104 °F | ||||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | 155 °C | 311 °F | |||
| Flammability, UL94 | HB @Thickness 3.20 mm | HB @Thickness 0.126 in | |||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 240 - 270 °C | 464 - 518 °F | |||
| Middle Barrel Temperature | 250 - 300 °C | 482 - 572 °F | |||
| Front Barrel Temperature | 260 - 310 °C | 500 - 590 °F | |||
| Nozzle Temperature | 250 - 310 °C | 482 - 590 °F | |||
| Mold Temperature | 90.0 - 115 °C | 194 - 239 °F | |||
| Descriptive Properties | |||||
| Color | Dark Green | ||||