- 熔体流动速率 [g/10min]: 0.92
- 密度 [g/cm3]: 1.02
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Oxygen Permeability | 1600 cm3 mil/(m2 day atm) | 103 cm3 mil/(100 in2 day atm) | |||
| Water Vapor Permeability | 7.60 g mil/ (m2 day) | 0.490 g mil/ (100 in2 day) | |||
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 | ||
| Water Vapor Transmission | 0.000190 g/m²/day @Temperature 23.0 °C | 0.0000122 g/100 in²/day @Temperature 73.4 °F | 85% RH; ISO 15106-3 | ||
| Oxygen Transmission | 0.0400 cc-mm/m²-24hr-atm @Temperature 23.0 °C | 0.102 cc-mil/100 in²-24hr-atm @Temperature 73.4 °F | 50% RH | ||
| Thickness | 100 microns | 3.94 mil | |||
| Melt Flow | 0.92 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.92 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 | ||
| 3.7 g/10 min @Load 2.16 kg, Temperature 230 °C | 3.7 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | |||
| 7.4 g/10 min @Load 2.16 kg, Temperature 260 °C | 7.4 g/10 min @Load 4.76 lb, Temperature 500 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | >= 150 % | >= 150 % | ISO 527-3 | ||
| Film Elongation at Break, TD | >= 100 % | >= 100 % | ISO 527-3 | ||
| Tensile Modulus | 1.26 GPa | 183 ksi | Bar; ISO 527-3 | ||
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 | ||
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ISO 527-3 | ||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | 33.0 °C | 91.4 °F | 10°C/min; ISO 11357 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | <= 1.0 % | <= 1.0 % | ISO 14782 | ||
| Gloss | >= 100 % | >= 100 % | 60° | ||
| Descriptive Properties | |||||
| Type of extrusion | Cast | Test Specimen | |||