SABIC Innovative Plastics LNP STAT-KON 9X06519 Cyclic Olefinic Copolymer

SABIC Innovative Plastics LNP STAT-KON 9X06519 Cyclic Olefinic Copolymer 物性表: SABIC Innovative Plastics LNP STAT-KON 9X06519 Cyclic Olefinic Copolymer物性表及特性介绍,SABIC Innovative Plastics LNP STAT-KON 9X06519 Cyclic Olefinic Copolymer注塑参数详情,如需SABIC Innovative Plastics LNP STAT-KON 9X06519 Cyclic Olefinic Copolymer下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.17
  • 缺口冲击强度: 0.32
  • 弯曲模量 [MPa]: 16.68
 
Physical PropertiesMetricEnglishComments
Density 1.17 g/cc0.0423 lb/in³ASTM D792
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 74.0 MPa10700 psiASTM D638
Elongation at Break 0.50 %0.50 %ASTM D638
Tensile Modulus 16.04 GPa2326 ksi50 mm/min; ASTM D638
Flexural Strength 158 MPa22900 psiASTM D790
Flexural Modulus 16.68 GPa2419 ksiASTM D790
Izod Impact, Notched 0.320 J/cm0.599 ft-lb/inASTM D256
Izod Impact, Unnotched 1.22 J/cm2.29 ft-lb/inASTM D4812
 
Electrical PropertiesMetricEnglishComments
Surface Resistance 10 - 100000 ohm10 - 100000 ohmASTM D257
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 2.80 µm/m-°C
@Temperature -40.0 - 40.0 °C
1.56 µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 12.6 µm/m-°C
@Temperature -40.0 - 40.0 °C
7.00 µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 150 °C
@Thickness 3.20 mm
302 °F
@Thickness 0.126 in
unannealed; ASTM D648

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-32144.html

免责声明: 本文 SABIC Innovative Plastics LNP STAT-KON 9X06519 Cyclic Olefinic Copolymer 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4