- 密度 [g/cm3]: 0.959
- 吸水率 [%]: 0.03
- 拉伸强度 [MPa]: 6.89
- 断裂伸长率 [%]: 3.45
- 弯曲强度 [MPa]: 0.159
- 弯曲模量 [MPa]: 9.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.959 - 3.12 g/cc | 0.0346 - 0.113 lb/in³ | Average value: 1.94 g/cc Grade Count:17 |
| Water Absorption | 0.0300 - 0.450 % | 0.0300 - 0.450 % | Average value: 0.162 % Grade Count:5 |
| Porosity | 15.0 - 16.0 % | 15.0 - 16.0 % | Average value: 15.7 % Grade Count:3 |
| Viscosity | 3000 - 160000 cP | 3000 - 160000 cP | Average value: 42400 cP Grade Count:7 |
| Pore Size | 12.7 - 15.2 microns | 0.500 - 0.600 mil | Average value: 13.5 microns Grade Count:3 |
| Linear Mold Shrinkage | 0.00100 - 0.00400 cm/cm | 0.00100 - 0.00400 in/in | Average value: 0.00240 cm/cm Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 81.0 - 95.0 | 81.0 - 95.0 | Average value: 86.5 Grade Count:22 |
| Tensile Strength, Ultimate | 0.159 - 59.6 MPa | 23.0 - 8650 psi | Average value: 26.7 MPa Grade Count:20 |
| Tensile Strength, Yield | 6.89 - 20.7 MPa | 1000 - 3000 psi | Average value: 16.5 MPa Grade Count:5 |
| Elongation at Break | 0.000 - 130 % | 0.000 - 130 % | Average value: 19.6 % Grade Count:7 |
| Modulus of Elasticity | 4.14 - 8.27 GPa | 600 - 1200 ksi | Average value: 6.18 GPa Grade Count:6 |
| Flexural Yield Strength | 3.45 - 56.0 MPa | 500 - 8130 psi | Average value: 31.0 MPa Grade Count:16 |
| Flexural Modulus | 9.00 - 10.8 GPa | 1310 - 1570 ksi | Average value: 9.67 GPa Grade Count:3 |
| Compressive Yield Strength | 41.4 - 89.6 MPa | 6000 - 13000 psi | Average value: 73.1 MPa Grade Count:18 |
| Compressive Modulus | 3.45 - 5.17 GPa | 500 - 750 ksi | Average value: 4.41 GPa Grade Count:5 |
| Shear Strength | 13.8 - 31.0 MPa | 2000 - 4500 psi | Average value: 20.6 MPa Grade Count:17 |
| 1.70 - 31.0 MPa @Temperature -55.0 - 177 °C | 247 - 4500 psi @Temperature -67.0 - 351 °F | Average value: 14.2 MPa Grade Count:5 | |
| Adhesive Bond Strength | 6.89 - 42.1 MPa | 1000 - 6100 psi | Average value: 19.1 MPa Grade Count:7 |
| 19.3053 - 27.9238 MPa @Temperature -54.4 - 82.2 °C | 2800.00 - 4050.01 psi @Temperature -66.0 - 180 °F | Average value: 23.6 MPa Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | Average value: 1.00e+15 ohm-cm Grade Count:5 |
| Dielectric Constant | 4.90 - 21.4 | 4.90 - 21.4 | Average value: 7.90 Grade Count:6 |
| Dielectric Strength | 3.94 - 15.7 kV/mm | 100 - 400 kV/in | Average value: 13.1 kV/mm Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 31.0 - 53.0 µm/m-°C | 17.2 - 29.4 µin/in-°F | Average value: 41.3 µm/m-°C Grade Count:7 |
| 30.06 - 111 µm/m-°C @Temperature 25.0 - 125 °C | 16.70 - 61.7 µin/in-°F @Temperature 77.0 - 257 °F | Average value: 76.9 µm/m-°C Grade Count:8 | |
| Thermal Conductivity | 0.724 - 1.28 W/m-K | 5.02 - 8.88 BTU-in/hr-ft²-°F | Average value: 1.08 W/m-K Grade Count:6 |
| 19.0 - 20.5 W/m-K @Temperature 100 - 100 °C | 132 - 142 BTU-in/hr-ft²-°F @Temperature 212 - 212 °F | Average value: 19.5 W/m-K Grade Count:3 | |
| Maximum Service Temperature, Air | 108 - 210 °C | 226 - 410 °F | Average value: 145 °C Grade Count:10 |
| Minimum Service Temperature, Air | -60.0 - -20.0 °C | -76.0 - -4.00 °F | Average value: -46.0 °C Grade Count:5 |
| Glass Transition Temp, Tg | 55.0 - 132 °C | 131 - 270 °F | Average value: 92.8 °C Grade Count:6 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 21.1 - 260 °C | 70.0 - 500 °F | Average value: 133 °C Grade Count:7 |
| Cure Time | 480 - 1440 min | 8.00 - 24.0 hour | Average value: 880 min Grade Count:3 |
| 30.0 - 720 min @Temperature 45.0 - 150 °C | 0.500 - 12.0 hour @Temperature 113 - 302 °F | Average value: 284 min Grade Count:11 | |
| Pot Life | 30.0 - 100000 min | 30.0 - 100000 min | Average value: 5460 min Grade Count:19 |