- 吸水率 [%]: 3.9
- 弯曲强度 [MPa]: 17.94
- 弯曲模量 [MPa]: 0.0138
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 3.9 % @Time 28800 sec | 3.9 % @Time 8.00 hour | boil | ||
| Viscosity | 300 cP | 300 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 75 | 75 | |||
| Tensile Strength, Ultimate | 17.94 MPa | 2602 psi | |||
| Flexural Modulus | 0.0138 GPa | 2.00 ksi | |||
| Compressive Strength | 33.41 MPa | 4846 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 32.0 - 40.0 °C | 89.6 - 104 °F | Deflection Temp at unknown load | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 50.0 °C | 2.00 hour @Temperature 122 °F | 2nd step | ||
| 60.0 - 360 min @Temperature 80.0 °C | 1.00 - 6.00 hour @Temperature 176 °F | optional 3rd step | |||
| 1440 min @Temperature 25.0 °C | 24.0 hour @Temperature 77.0 °F | 1st step | |||
| Pot Life | 480 - 720 min | 480 - 720 min | or longer | ||
| Descriptive Properties | |||||
| Acetone Absorption (%) | 26.3 | 3 hr. boil | |||
| Color | Clear | ||||
| Parts by Weight (pbw) | 100 | AboCast | |||
| 30 | AboCure | ||||
| Ultimate Elongation (%) | > 100 | ||||