- 缺口冲击强度: 0.342
- 断裂伸长率 [%]: 64.8
- 弯曲强度 [MPa]: 47.09
- 弯曲模量 [MPa]: 1.96
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity Measurement | 700 | 700 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 70 | 70 | |||
| Tensile Strength, Ultimate | 47.09 MPa | 6830 psi | |||
| Elongation at Break | 9.1 % | 9.1 % | |||
| Flexural Yield Strength | 64.8 MPa | 9400 psi | |||
| Flexural Modulus | 1.96 GPa | 284 ksi | |||
| Compressive Yield Strength | 63.36 MPa | 9190 psi | |||
| Compressive Modulus | 1.65 GPa | 239 ksi | |||
| Izod Impact, Notched | 0.342 J/cm | 0.641 ft-lb/in | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 3.43e+15 ohm-cm | 3.43e+15 ohm-cm | |||
| Surface Resistance | 4.71e+15 ohm | 4.71e+15 ohm | |||
| Dielectric Constant | 2.92 @Frequency 1e+6 Hz | 2.92 @Frequency 1e+6 Hz | |||
| 3.12 @Frequency 1000 Hz | 3.12 @Frequency 1000 Hz | ||||
| 3.17 @Frequency 60 Hz | 3.17 @Frequency 60 Hz | ||||
| Dissipation Factor | 0.0089 @Frequency 1000 Hz | 0.0089 @Frequency 1000 Hz | |||
| 0.010 @Frequency 60 Hz | 0.010 @Frequency 60 Hz | ||||
| 0.018 @Frequency 1e+6 Hz | 0.018 @Frequency 1e+6 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 58.0 °C | 136 °F | Deflection temperature; load unknown. | ||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 380 min | 380 min | 500 g | ||
| Descriptive Properties | |||||
| Exotherm | 154°C | Peak | |||