- 缺口冲击强度: 3.74
- 拉伸强度 [MPa]: 61.23
- 弯曲模量 [MPa]: 3.34
- 热变形温度 [℃]: 63.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 100 cP | 100 cP | Hardener | ||
| 1500 cP | 1500 cP | Resin | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 70 | 70 | ASTM D2240 | ||
| Tensile Strength, Yield | 61.23 MPa | 8881 psi | ASTM D638 | ||
| Elongation at Break | 28 % | 28 % | ASTM D638 | ||
| Flexural Strength | 87.370 MPa | 12672 psi | ASTM D790 | ||
| Flexural Modulus | 3.34 GPa | 485 ksi | ASTM D638 | ||
| Adhesive Bond Strength | 1.72 MPa | 250 psi | Wood (no primer), Delamination; ASTM D4541 Elcometer | ||
| >= 2.07 MPa | >= 300 psi | Concrete (no primer), Concrete Failure; ASTM D4541 Elcometer | |||
| >= 10.3 MPa | >= 1500 psi | Steel (no primer), Substrate Failure; ASTM D4541 Elcometer | |||
| Izod Impact, Notched | 3.74 J/cm | 7.00 ft-lb/in | ASTM D628 | ||
| Taber Abrasion, mg/1000 Cycles | 80 | 80 | CS17 WHEEL, 1kg per 1000 cycles; ASTM D4060 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ASTM D648 | ||
| Flash Point | >= 93.3 °C | >= 200 °F | ASTM Pensky-Martin | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | >= 150 min | >= 2.50 hour | Tack Free Time, 75°C | ||
| Gel Time | 20.0 min | 20.0 min | 75°C | ||
| Descriptive Properties | |||||
| Color | Light Gray, Dark Gray | ||||
| Resistance to Acetic Acid (100%) | Recommended | ||||
| Resistance to Acetone | Recommended | ||||
| Resistance to Ammonium Hydroxide (50%) | Recommended | ||||
| Resistance to Brake Fluid (310g/l) | Recommended | ||||
| Resistance to Brine-Saturated H2O | Recommended | Resistance to Brine-Saturated H2O (310g/l) | |||
| Resistance to Gasoline | Recommended | ||||
| Resistance to H2O | Recommended | ||||
| Resistance to Hydrochloric Acid (50%) | Recommended | ||||
| Resistance to MEK | Recommended | ||||
| Resistance to Methanol | Recommended | ||||
| Resistance to Muriatic Acid (10%) | Recommended | ||||
| Resistance to NaCl/H2O (10%) | Recommended | ||||
| Resistance to Nitric Acid (20%) | Recommended Conditional | ||||
| Resistance to Potassium Hydroxide (10%) | Recommended | ||||
| Resistance to Potassium Hydroxide (20%) | Recommended, Discoloration | ||||
| Resistance to Sodium Bicarbonate | Recommended | ||||
| Resistance to Sodium Hydroxide (50%) | Recommended, Discoloration | ||||
| Resistance to Sodium Hypochlorite (10%) | Recommended | ||||
| Resistance to Sugar/H2O | Recommended | ||||
| Resistance to Sulfuric Acid (>50%) | Recommended | ||||
| Resistance to Sulfuric Acid (10%) | Recommended | ||||
| Resistance to Toluene | Contact EPI | ||||
| Resistance to Xylene | Recommended Conditional | ||||