- 密度 [g/cm3]: 1.17
- 吸水率 [%]: 0.5
- 断裂伸长率 [%]: 110.3
- 弯曲强度 [MPa]: 62.05
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | |
| Water Absorption | 0.50 - 0.60 % | 0.50 - 0.60 % | (60x10X4 mm bar) after 10 days at 20°C (77°F) |
| 0.70 - 0.80 % | 0.70 - 0.80 % | (60x10X4 mm bar) after 1 hour at 100°C (212°F) | |
| Viscosity | 6500 - 8000 cP | 6500 - 8000 cP | |
| Vapor Pressure | <= 0.0000133 bar | <= 0.0100 torr | AboCure, at 20°C |
| 0.00133 bar | 1.00 torr | AboCast, at 180°C | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 62.05 MPa | 9000 psi | |
| Modulus of Elasticity | 3.102 GPa | 449.9 ksi | |
| Flexural Yield Strength | 110.3 MPa | 16000 psi | |
| Compressive Yield Strength | 103.4 MPa | 15000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.50e+16 ohm-cm | >= 1.50e+16 ohm-cm | |
| Dielectric Constant | 3.7 - 4.1 @Frequency 1e+6 Hz | 3.7 - 4.1 @Frequency 1e+6 Hz | |
| 4.5 - 4.8 @Frequency 50 Hz | 4.5 - 4.8 @Frequency 50 Hz | ||
| Dissipation Factor | 0.010 - 0.020 @Frequency 50 Hz | 0.010 - 0.020 @Frequency 50 Hz | |
| 0.030 - 0.040 @Frequency 1e+6 Hz | 0.030 - 0.040 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 - 70.0 µm/m-°C @Temperature 20.0 °C | 36.1 - 38.9 µin/in-°F @Temperature 68.0 °F | |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Deflection temperature; load unknown. |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Pot Life | 10 min | 10 min | at 60°C (140°F) |
| 20 min | 20 min | at 40°C (104°F) | |
| 45 min | 45 min | at 20°C (68°F) | |