- 密度 [g/cm3]: 1.95
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.32
- 弯曲强度 [MPa]: 97.0
- 弯曲模量 [MPa]: 18.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.95 g/cc | 0.0704 lb/in³ | |
| Apparent Bulk Density | 0.780 g/cc | 0.0282 lb/in³ | |
| Water Absorption | 0.20 % | 0.20 % | 48 hrs, 50°C |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | typical. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 70 | 70 | |
| Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | |
| Flexural Strength | 131 MPa | 19000 psi | |
| Flexural Modulus | 18.0 GPa | 2610 ksi | |
| Compressive Strength | 207 MPa | 30000 psi | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | |
| Dielectric Constant | 4.7 @Frequency 1e+6 Hz | 4.7 @Frequency 1e+6 Hz | Wet |
| 5.4 @Frequency 1000 Hz | 5.4 @Frequency 1000 Hz | Wet | |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
| Dissipation Factor | 0.0080 @Frequency 1e+6 Hz | 0.0080 @Frequency 1e+6 Hz | Wet |
| 0.011 @Frequency 1000 Hz | 0.011 @Frequency 1000 Hz | Wet | |
| Arc Resistance | 186 sec | 186 sec | |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.4187 W/m-K | 2.906 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 230 °C | >= 446 °F | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 - 175 °C | 302 - 347 °F | Molding temperature |