| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 84 | 84 | |||
| Flexural Strength | 81.4 MPa | 11800 psi | ASTM D790 | ||
| Shear Strength | 16.2 MPa | 2350 psi | ASTM D1002-94 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |||
| Dielectric Constant | 4.2 @Frequency 1000 Hz | 4.2 @Frequency 1000 Hz | |||
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | |||
| Dissipation Factor | 0.030 | 0.030 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 32.4 µm/m-°C @Temperature 20.0 °C | 18.0 µin/in-°F @Temperature 68.0 °F | |||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |||
| Shrinkage | 0.40 % | 0.40 % | Cure Shrinkage | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 300 min | 5.00 hour | 1 hrs at Room Temp; 4 hrs at 175°F (Alternate Cure) | ||
| 1440 min | 24.0 hour | Room Temperature (Recommended Cure) | |||
| Pot Life | 15 min | 15 min | 100 gm mass @ 25°C | ||
| Descriptive Properties | |||||
| Chemical Resistance | Good | ||||
| Mix Ratio by Weight | 100:13 | resin:hardener | |||