| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.66 g/cc | 1.66 g/cc | |||
| Viscosity | 11000 cP | 11000 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Shear Strength | 8.27 MPa | 1200 psi | Strength can be increased 40-50% by heat curing; ASTM D1002-94 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 100000 ohm-cm | 100000 ohm-cm | |||
| Dielectric Strength | 1.97 kV/mm | 50.0 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C | 25.0 µin/in-°F @Temperature 68.0 °F | |||
| Thermal Conductivity | 1.80 W/m-K | 12.5 BTU-in/hr-ft²-°F | |||
| Maximum Service Temperature, Air | 300 °C | 572 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 240 min | 4.00 hour | 2 hrs at 100°F; 2 hrs at 200°F (Recommended Cure) | ||
| 1440 - 2880 min | 24.0 - 48.0 hour | Room Temperature (Alternate Cure) | |||
| Pot Life | <= 60 min | <= 60 min | 100 gm mass @ 25°C | ||
| Descriptive Properties | |||||
| Chemical Resistance | Good | ||||
| Mix Ratio by Weight | 100:12 | resin:hardener | |||