| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | |||
| Viscosity | 8500 cP | 8500 cP | Mixed Viscosity | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 89 | 89 | |||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 | ||
| Shear Strength | 19.3 MPa | 2800 psi | ASTM D1002-94 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 4.00e+14 ohm-cm | 4.00e+14 ohm-cm | |||
| Dielectric Constant | 3.01 @Frequency 1000 Hz | 3.01 @Frequency 1000 Hz | |||
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | |||
| Dissipation Factor | 0.010 | 0.010 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 32.4 µm/m-°C @Temperature 20.0 °C | 18.0 µin/in-°F @Temperature 68.0 °F | |||
| Maximum Service Temperature, Air | 300 °C | 572 °F | |||
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | |||
| Shrinkage | 1.0 % | 1.0 % | Cure Shrinkage | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 180 - 240 min | 3.00 - 4.00 hour | at 300°F (Alternate Cure) | ||
| 240 min | 4.00 hour | 2 hrs at 200°F; 2 hrs at 325°F (Recommended Cure) | |||
| Pot Life | 150 min | 150 min | 100 gm mass @ 25°C | ||
| Descriptive Properties | |||||
| Chemical Resistance | Good | ||||
| Mix Ratio by Weight | 1:1 | resin:hardener | |||